Abstract The interfacial shear (IS) force of copper ball onto aluminium-based bond pad in microelectronics packaging depends on the formation and growth of Cu–Al intermetallic. This paper reports the study on the behaviour of the IS force of the Cu–Al bonds that were subjected to pressure cooker test up to 576 h. Initially, the IS force increases with test readout point until 192 h, due to Cu–Al intermetallic growth that has strengthened the bonding. However, IS force decreases significantly from 157.4 gf at 192 h to 97.6 gf at final test readout point, 576 h. The number of shear-induced cratering shows similar reduction trend after 288 h. Result of scanning electron microscopy (SEM) on bonding morphology shows the evidence of crack at the aluminium bond periphery or outer Cu–Al interface and the cracking trend continues at higher time point. Surface analysis of ball-peeled bond pad using X-ray photoelectron spectroscopy (XPS) indicated that the cracks were due to stress corrosion cracking at aluminium that has been stimulated by copper. The concentration of CuO at the surface bonded area was found to be increased at higher readout point and reached 100% at 576 h. These results indicated that the Cu–Al bond had been weakened by stress corrosion cracking at outer bond interface and reduced the IS force.
[1]
Elliott Philofsky.
Purple Plague Revisited
,
1970
.
[2]
Elliott Philofsky,et al.
Intermetallic formation in gold-aluminum systems
,
1970
.
[3]
W. Stickle,et al.
Handbook of X-Ray Photoelectron Spectroscopy
,
1992
.
[4]
H. K. Charles,et al.
The effect of high-temperature intermetallic growth on ball shear-induced cratering
,
1989
.
[5]
K. Mizuno,et al.
Au/Al2O3/Al薄膜における金の拡散および金属間化合物生成の挙動
,
1995
.
[6]
L. Nguyen,et al.
Optimization of copper wire bonding on Al-Cu metallization
,
1995
.
[7]
W. J. Tomlinson,et al.
Effect of heat treatment on the shear strength and fracture modes of copper wire thermosonic ball bonds to Al-1% Si device metallization
,
1990
.
[8]
Tim Koch,et al.
A Bond Failure Mechanism
,
1986,
24th International Reliability Physics Symposium.
[9]
Howard M. Berg,et al.
Micro-Corrosion of Al-Cu Bonding Pads
,
1987,
23rd International Reliability Physics Symposium.
[10]
K. Toyozawa,et al.
Development of copper wire bonding application technology
,
1990
.