Effect of micro-inclusions on subsurface-initiated rolling contact fatigue of a railway wheel

The objectives of this paper are to investigate the size of the maximum micro-inclusion in a railway wheel using ultrasonic fatigue testing and to evaluate the effect of the micro-inclusion on subsurface-initiated rolling contact fatigue of the railway wheel. Fatigue specimens with a large risk volume were quenched, tempered and oxynitrocarburized to increase both the strength of the matrix and the resistance to surface corrosion, which ensured that all of the specimens fractured from the internal inclusion under water cooling. The test results show that the size of the micro-inclusion obtained using the fatigue method are much larger than those obtained by a traditional surface analysis method, which means that the accuracy of the fatigue method is higher than that of the traditional method. The maximum square root of the micro-inclusion area and the maximum length of the major axis of the elliptical micro-inclusion for a full-sized railway wheel are estimated using the statistics of extreme values method to be 296 µm and 736 µm, respectively. Based on the estimated maximum micro-inclusion sizes and principles of fracture mechanics, the critical loading of the railway wheel for both subsurface-initiated fatigue and fatigue initiated at a deep-lying material defect are obtained.

[1]  Elena Kabo,et al.  Wheel/rail rolling contact fatigue – Probe, predict, prevent , 2014 .

[2]  Nishijima,et al.  Stepwise S-N curve and fish-eye failure in gigacycle fatigue , 1999 .

[3]  J. M. De Monicault,et al.  Automated Piezoelectric Fatigue Machine for Severe Environments , 2002 .

[4]  Elena Kabo,et al.  An engineering model for prediction of rolling contact fatigue of railway wheels , 2002 .

[5]  Jiang Min,et al.  IN SITU OBSERVATION OF MnS INCLUSION BEHAVIOR IN RESULFURIZED FREE-CUTTING STEEL DURING HEATING , 2011 .

[6]  R. Mehrabian,et al.  Initial coarsening of manganese sulfide inclusions in rolled steel during homogenization , 1975 .

[7]  Roberto Roberti,et al.  Contact fatigue propagation of deep defects in railway wheels , 2013 .

[8]  Guojiang Wan,et al.  Enhancement of corrosion resistance of AISI 420 stainless steels by nitrogen and silicon plasma immersion ion implantation , 2007 .

[9]  Jens C. O. Nielsen,et al.  Track Condition Analyser: Identification of Rail Rolling Surface Defects, Likely to Generate Fatigue Damage in Wheels, Using Instrumented Wheelset Measurements , 2011 .

[10]  Jens C. O. Nielsen,et al.  Subsurface initiated rolling contact fatigue of railway wheels as generated by rail corrugation , 2007 .

[11]  Claude Bathias,et al.  Piezoelectric fatigue testing machines and devices , 2006 .

[12]  Yukitaka Murakami,et al.  Instructions for a New Method of Inclusion Rating and Correlations with the Fatigue Limit , 1994 .

[13]  Jens C. O. Nielsen,et al.  Influence of Short-Pitch Wheel/Rail Corrugation on Rolling Contact Fatigue of Railway Wheels , 2005 .

[14]  M. K. Kassir,et al.  Three-Dimensional Stress Distribution Around an Elliptical Crack Under Arbitrary Loadings , 1966 .

[15]  Min Jiang,et al.  Effect of Heat Treatment Conditions on Shape Control of Large-sized Elongated MnS Inclusions in Resulfurized Free-cutting Steels , 2011 .

[16]  Anders Ekberg,et al.  Anisotropy and rolling contact fatigue of railway wheels , 2001 .

[17]  A Ekberg,et al.  Influence of plastic deformations on growth of subsurface rolling contact fatigue cracks in railway wheels , 2006 .

[18]  Merton C. Flemings,et al.  Effect of homogenization on sulfide inclusions in ferrous alloys , 1974, Metallurgical and Materials Transactions B.

[19]  Anders Ekberg,et al.  Effects of imperfections on fatigue initiation in railway wheels , 2000 .

[20]  Takayuki Abe,et al.  Giga-cycle Fatigue Properties of Induction Hardened 0.40% C Carbon Steels , 2007 .

[21]  W. H. Zhang,et al.  Inclusion size evaluation and fatigue strength analysis of 35CrMo alloy railway axle steel , 2013 .

[22]  Y. Murakami,et al.  Small Defects and Inhomogeneities in Fatigue Strength: Experiments, Models and Statistical Implications , 1999 .

[23]  Elena Kabo,et al.  Fatigue initiation in railway wheels — a numerical study of the influence of defects , 2002 .

[24]  Helen V. Atkinson,et al.  Characterization of inclusions in clean steels: a review including the statistics of extremes methods , 2003 .

[25]  Yukitaka Murakami,et al.  Fatigue Crack Path and Threshold in Mode II and Mode III Loadings , 2008, CP 2013.

[26]  T Wu,et al.  An automatic ultrasonic fatigue testing system for studying low crack growth at room and high temperatures , 1994 .

[27]  Yu. M. Lakhtin.  Oxynitriding (nitrooxidizing) , 1994 .

[28]  E. Kabo,et al.  Fatigue of railway wheels and rails under rolling contact and thermal loading—an overview , 2005 .

[29]  Elena Kabo,et al.  Material defects in rolling contact fatigue — influence of overloads and defect clusters , 2002 .

[30]  Yoshiyuki Furuya,et al.  Specimen size effects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing , 2008 .