Effects of early-age thermal behaviour on damage risks in massive concrete structures

At early age, temperature in massive concrete structures may reach over 70°C because hydration is an exothermic chemical reaction. Temperature evolution (increasing followed by decreasing temperature) can lead to damage risks in the short and long term. Firstly, cracking due to self-restrained strains (essentially thermal strains) can occur (which increase the transport properties and so the kinetics of degradation); and secondly, delayed ettringite formation can appear. In addition, if autogenous and thermal strains are restrained, compressive stresses and then tensile stresses increase, which can cause crossing cracks. However, this paper will not deal with these phenomena. In the first part, sensitivity to delayed ettringite formation and early age cracks by self-restrained strains are studied with regards to the environmental conditions by a numerical approach. This part shows that the external temperature has a significant impact on the maximal temperature reached, but that the temperature difference between the core and the surface is mainly impacted by the wind velocity. Then, a parametric study on the effect of the variation of thermal properties at early age has been achieved and shows that it needs to be taken into account. Finally, visco-elastic mechanical calculations show the impact of thermal property variation on the stresses generated by self restraint.

[1]  Vincent Waller,et al.  Relations entre composition des betons, exothermie en cours de prise et resistance en compression , 1999 .

[2]  Franz-Josef Ulm,et al.  Microprestress-Solidification Theory for Concrete Creep. I: Aging and Drying Effects , 1997 .

[3]  Farid Benboudjema,et al.  Interaction between drying, shrinkage, creep and cracking phenomena in concrete , 2005 .

[4]  Olivier Coussy,et al.  Couplings in early-age concrete: From material modeling to structural design , 1998 .

[5]  Farid Benboudjema,et al.  Early-age behaviour of concrete nuclear containments , 2008 .

[6]  Ahmed Loukili,et al.  A new approach to determine autogenous shrinkage of mortar at an early age considering temperature history , 2000 .

[7]  Jin-Keun Kim,et al.  Experimental study on the convective heat transfer coefficient of early-age concrete , 2009 .

[8]  A. L. Marshall,et al.  The thermal properties of concrete , 1972 .

[9]  Lars Damkilde,et al.  TRANSITIONAL THERMAL CREEP OF EARLY AGE CONCRETE , 1999 .

[10]  G. D. Schutter.  Degree of hydration based Kelvin model for the basic creep of early age concrete , 1999 .

[11]  Ahmed Loukili,et al.  Autogenous deformations of cement pastes: Part I. Temperature effects at early age and micro–macro correlations , 2006 .

[12]  Rui Faria,et al.  Modelling of concrete at early ages: Application to an externally restrained slab , 2006 .

[13]  P Laplante.  PROPRIETES MECANIQUES DES BETONS DURCISSANTS : ANALYSE COMPAREE DES BETONS CLASSIQUES ET A TRES HAUTES PERFORMANCES , 1993 .

[14]  Se-Jin Jeon,et al.  Advanced Assessment of Cracking due to Heat of Hydration and Internal Restraint , 2008 .

[15]  Rui Faria,et al.  Identification of early-age concrete temperatures and strains : monitoring and numerical simulation , 2009 .

[16]  Benoît Bissonnette,et al.  Prediction of elastic properties of cement pastes at early ages , 2010 .

[17]  Robert Otto Rasmussen,et al.  CONCRETE TEMPERATURE MODELING AND STRENGTH PREDICTION USING MATURITY CONCEPTS IN THE FHWA HIPERPAV SOFTWARE , 2001 .

[18]  Laurie Lacarrière,et al.  Prévision et évaluation de la fissuration précoce des ouvrages en béton , 2007 .

[19]  C. W. Yu,et al.  Creep of concrete under uniaxial and biaxial stresses at elevated temperatures , 1967 .

[20]  M. Collepardi,et al.  A state-of-the-art review on delayed ettringite attack on concrete , 2003 .

[21]  Sven Thelandersson,et al.  Modeling of Combined Thermal and Mechanical Action in Concrete , 1987 .