Metal complexation of poly[1‐(2‐hydroxyethyl)aziridine‐co‐2‐methyl‐2‐oxazoline] in aqueous solution

The metal complexation of water-soluble poly[1-(2-hydroxyethyl)aziridine-co-2-methyl-2-oxazoline] with Co(II), Zn(II), Ni(II), Cu(II), Cr(III), Fe(III), Cd(II), Pb(II), and Sr(II) ions was investigated in aqueous phase using Liquid-Phase Polymer-Based Retention (LPR). The study shows that all metal ions are complexed at pH 5, except Co(II) and Zn(II). In contrast to Sr(II), which showed only a slight interaction over a pH range of 3 to 7, 94% of Co(II) and 88% of Zn(II) were retained at pH 7. At pH 3, only Cu(II) and Cr(III) ions interacted with the copolymer with retention values of 76% for Cu(II) and 52% for Cr(III). Viscosimetric measurements of the copolymer were performed in the presence of metal ions at different pH values. Die Metallkomplexierung von wasserloslichem Poly[1-(2-hydroxyethyl)aziridin-co-2-methyl-2-oxazolin] mit Co(II), Zn(II), Ni(II), Cu(II), Cr(III), Fe(III), Cd(II), Pb(II) und Sr(II)-Ionen wurde in wasriger Phase mit der Methode der Liquid-Phase Polymer-Based Retention (LPR) untersucht. Die Studie zeigt, das alle Metallionen, auser Co(II) und Zn(II), bei pH 5 komplexiert wurden. Im Gegensatz zu Sr(II), das nur eine schwache Wechselwirkung in einem pH-Bereich von 3 bis 7 zeigte, wurden bei pH 7 94% Co(II) und 88% Zn(II) retentiert. Bei pH 3 zeigten nur Cu(II) und Cr(III) eine Wechselwirkung mit dem Polymeren, wobei die Retentionswerte 76% fur Cu(II) und 52% fur Cr(III) betrugen. Viskositatsmessungen des Copolymeren in Gegenwart von Metallionen wurden bei verschiedenen pH-Werten durchgefuhrt.