Fission fragment damage to crystal lattices: lead iodide I. Electron microscopy

Earlier papers (Bowden & Chadderton 1962; Chadderton & Montagu-Pollock 1963 ; Chadderton 1964) described the damage caused to various types of crystal by energetic fission fragments, and interpreted the electron microscope observations of damage on the basis of current theories of energy loss of charged particles, and of image contrast in the microscope. In this paper, electron microscope observations of fission fragment irradiated single crystals of lead iodide are described. This compound is heat-sensitive, and might therefore be expected to show damage through lattice excitation following the passage of a heavily ionizing energetic particle. The nature of the damage is sensitively dependent on the thickness of the crystal specimen, with tracks visible in thin crystals and a random array of dislocation loops in thicker ones. The variation in track visibility and appearance with thickness is described, and the possible mechanisms of energy loss which might account for these variations are discussed. The proximity of the crystal surfaces to the path of a fission fragment is a critical factor in determining the visible effects. Observations of damage in cadmium iodide are also discussed. The random distribution of dislocation loops in thick crystals, where surface effects are no longer influential, indicates a high mobility of the point defects created in the wake of a fission fragment by direct collision and thermal processes. Some possible mechanisms for the motion of energetic knock-ons in the lattice are suggested. These will be investigated more fully in part II.

[1]  F. P. Bowden,et al.  The damage of crystals by collimated fission fragments , 1963 .

[2]  F. Fujita,et al.  Electron Microscopic Study of Fission Fragment Damage in Molybdenite Crystals , 1963 .

[3]  R. F. Redmond,et al.  Energy Spectrum of Fission Fragments Emitted from Thin Layers of Uranium Dioxide , 1962 .

[4]  A. J. Forty,et al.  The electrical conductivity and photo-decomposition of small crystals of lead iodide , 1962 .

[5]  L. T. Chadderton.  DISLOCATION LOOPS IN FISSION FRAGMENT BOMBARDED LEAD IODIDE , 1962 .

[6]  L. T. Chadderton.  Experimental Evidence for the Concept of the Displacement Spike , 1962, Nature.

[7]  P. Buhl,et al.  Observation of Fission Fragment Damage in Thin Films of Metals , 1962 .

[8]  S. Amelinckx,et al.  Fission Fragment Damage to Platinum , 1961 .

[9]  F. P. Bowden,et al.  Molecular Disarray in a Crystal Lattice Produced by a Fission Fragment , 1961, Nature.

[10]  A. J. Forty.  Helical dislocations in crystals of lead iodide , 1961 .

[11]  P. Price.  On dislocation loops formed in zinc crystals during low temperature pyramidal glide , 1961 .

[12]  T. Noggle,et al.  Electron Microscope Observations of Fission Fragment Tracks in Thin Films of UO2 , 1960 .

[13]  A. J. Forty.  Observations of the decomposition of crystals of lead iodide in the electron microscope , 1960 .

[14]  J. Silcox,et al.  Direct observations of the annealing of prismatic dislocation loops and of climb of dislocations in quenched aluminium , 1960 .

[15]  R. S. Barnes,et al.  Examination of fission fragment tracks with an electron microscope , 1959 .

[16]  R S Pease,et al.  REVIEW ARTICLES: The Displacement of Atoms in Solids by Radiation , 1955 .

[17]  G. Dienes,et al.  Radiation Effects in Solids , 1953 .

[18]  Raymond L. Murray,et al.  The Elements of Nuclear Reactor Theory , 1953 .

[19]  N. O. Lassen.  Hρ-Distribution of Fission Fragments , 1945 .

[20]  N. Bohr,et al.  Velocity-Range Relation for Fission Fragments , 1940 .

[21]  J. Bøggild,et al.  Cloud-Chamber Studies of Fission Fragment Tracks , 1940 .