Local melting and tool slippage during friction stir spot welding of Al-alloys

Local melting and tool slippage during friction stir spot welding of different Al-alloy base materials is examined using a combination of detailed microscopy and temperature measurement. The stir zone peak temperature during welding is limited by either the solidus of the alloy in question or by spontaneous melting of intermetallic particles contained in the as-received base material. When spontaneous melting occurs this facilitates tool slippage at the contact interface. Accurate stir zone temperature and grain size measurements are essential elements when estimating the strain rate using the Zener–Hollomon relation. In Al 2024 and Al 7075 spot welds spontaneous melting of second-phase particles produces a drastic reduction in strain rate values. In Al 5754 and Al 6061 spot welds there is a strong correlation between tool rotational speed and estimated strain values. Local melted films dissolve rapidly in the high temperature stir zone and when the spot weld cools to room temperature following welding. Evidence of local melting is observed in Al 7075 friction stir spot welded joints made using a combination of rapid quenching, high plunge rates, and extremely short dwell time settings.

[1]  A. Godfrey,et al.  Comparative microstructural characterization of a friction-stir-welded aluminum alloy using TEM and SEM-based techniques , 2006 .

[2]  M. Whelan.  On the Kinetics of Precipitate Dissolution , 1969 .

[3]  Ward O. Winer,et al.  The thermal aspects of oxidational wear , 1985 .

[4]  Thomas H. North,et al.  Intermixing in Dissimilar Friction Stir Spot Welds , 2007 .

[5]  Jason E. Mitchell,et al.  Analysis of friction stir welds using thermocouple measurements , 2003 .

[6]  M. Starink.  Effect of compositional variations on characteristics of coarse intermetallic particles in overaged 7000 aluminium alloys , 2001 .

[7]  R. Braun,et al.  Mikrostrukturelle, mechanische und korrosive Eigenschaften reibrührgeschweißter Stumpfnähte in Aluminiumlegierungen , 1998 .

[8]  Paul T. Wang,et al.  Grain structure evolution in a 6061 aluminum alloy during hot torsion , 2006 .

[9]  Paul A. Colegrove,et al.  Experimental and numerical analysis of aluminium alloy 7075-T7351 friction stir welds , 2003 .

[10]  Thomas H. North,et al.  Energy utilisation and generation during friction stir spot welding , 2006 .

[11]  E. Cerri,et al.  Comparative hot workability of 7012 and 7075 alloys after different pretreatments , 1995 .

[12]  A. Gerlich,et al.  Peak temperatures and microstructures in aluminium and magnesium alloy friction stir spot welds , 2005 .

[13]  H. Mcqueen,et al.  Hot deformation mechanisms of a solution-treated Al-Li-Cu-Mg-Zr alloy , 1996 .

[14]  O. Reiso,et al.  Dissolution and melting of secondary Al2Cu phase particles in an AlCu alloy , 1990 .

[15]  P. Prangnell,et al.  Effect of welding parameters on nugget zone microstructure and properties in high strength aluminium alloy friction stir welds , 2003 .

[16]  Yutaka S. Sato,et al.  Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys , 2004 .

[17]  Thomas H. North,et al.  Tool penetration during friction stir spot welding of Al and Mg alloys , 2005 .

[18]  F. P. Bowden,et al.  The surface temperature of sliding solids , 1954, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[19]  N. Ryum,et al.  Local melting in Al-Mg-Zn-alloys , 1994 .

[20]  A. Gerlich,et al.  The Influence of Processing Parameters on Microstructure of Al 5754 Friction Stir Spot Welds , 2006 .

[21]  Motomichi Yamamoto,et al.  Effect of welding parameters on the strain rate and microstructure of friction stir spot welded 2024 aluminum alloy , 2007 .

[22]  J. Li,et al.  Properties and application of Fe–6Si–14Mn–9Cr–5Ni shape memory alloy , 2001 .

[23]  Joseph R. Davis,et al.  Special Features of Structure Formation and Properties of Special High-Alloy Alloys of the Al – Si – Cu System , 2023, Metal Science and Heat Treatment.

[24]  F. J. Humphreys.  Review Grain and subgrain characterisation by electron backscatter diffraction , 2001 .

[25]  E. Nes,et al.  Microstructure development during hot deformation of aluminum to large strains , 2003 .

[26]  F. P. Bowden,et al.  Physical properties of surfaces - III—The surface temperature of sliding metals - The temperature of lubricated surfaces , 1936 .

[27]  A. Gerlich,et al.  Stir zone microstructure and strain rate during Al 7075-T6 friction stir spot welding , 2006 .