Dependence of the Electroluminescence on the Spacer Layer Growth Temperature of Multilayer Quantum-Dot Laser Structures

Electroluminescence (EL) measurements have been performed on a set of In(Ga)As-GaAs quantum-dot (QD) structures with varying spacer layer growth temperature. At room temperature and low injection current, a superlinear dependence of the integrated EL intensity (IEL) on the injection current is observed. This superlinearity decreases as the spacer layer growth temperature increases and is attributed to a reduction in the amount of nonradiative recombination. Temperature-dependent IEL measurements show a reduction of the IEL with increasing temperature. Two thermally activated quenching processes, with activation energies of ~ 157 meV and ~ 320 meV, are deduced and these are attributed to the loss of electrons and holes from the QD ground state to the GaAs barriers. Our results demonstrate that growing the GaAs barriers at higher temperatures improves their quality, thereby increasing the radiative efficiency of the QD emission.

[1]  A. Stintz,et al.  Thermal activation of excitons in asymmetric InAs dots-in-a-well InxGa1−xAs∕GaAs structures , 2007 .

[2]  S. Sanguinetti,et al.  Carrier thermodynamics in InAs/In x Ga 1-x As quantum dots , 2006 .

[3]  M. Hopkinson,et al.  Improved performance of 1.3-/spl mu/m In(Ga)As quantum-dot lasers by modifying the temperature profile of the GaAs spacer layers , 2006, IEEE Photonics Technology Letters.

[4]  J. Chyi,et al.  Pinholelike defects in multistack 1.3μm InAs quantum dot laser , 2006 .

[5]  M. Hopkinson,et al.  Recombination mechanisms in 1.3-/spl mu/m InAs quantum-dot lasers , 2006, IEEE Photonics Technology Letters.

[6]  K. Pierz,et al.  Temperature-dependent optical properties of In As ∕ Ga As quantum dots: Independent carrier versus exciton relaxation , 2005 .

[7]  Kristian M. Groom,et al.  Improved performance of 1.3μm multilayer InAs quantum-dot lasers using a high-growth-temperature GaAs spacer layer , 2004 .

[8]  A. Forchel,et al.  The role of Auger recombination in InAs 1.3-/spl mu/m quantum-dot lasers investigated using high hydrostatic pressure , 2003 .

[9]  R. Murray,et al.  Temperature and excitation density dependence of the photoluminescence from annealed InAs/GaAs quantum dots , 2003 .

[10]  D. Bimberg,et al.  The influence of heat treatment conditions on the evaporation of defect regions in structures with InGaAs quantum dots in the GaAs matrix , 2002 .

[11]  C. Pan,et al.  Correlation between Defect Concentration and Carrier Lifetime of GaAs Grown by Molecular Beam Epitaxy at Different Temperatures , 2001 .

[12]  Hongwei Li,et al.  Mismatch and chemical composition analysis of vertical InxGa1−xAs quantum-dot arrays by transmission electron microscopy , 2001 .

[13]  Nikolai N. Ledentsov,et al.  1.3 µm luminescence and gain from defect-free InGaAs-GaAs quantum dots grown by metal-organic chemical vapour deposition , 2000 .

[14]  B. Streetman,et al.  Factors influencing the interfacial roughness of InGaAs/GaAs heterostructures: A scanning tunneling microscopy study , 1999 .

[15]  John E. Bowers,et al.  Time‐resolved optical characterization of InGaAs/GaAs quantum dots , 1994 .

[16]  J. Merz,et al.  Characterization of recombination processes in multiple narrow asymmetric coupled quantum wells based on the dependence of photoluminescence on laser intensity , 1992 .

[17]  J. David,et al.  Carrier decay in GaAs quantum wells , 1990 .

[18]  R. Olshansky,et al.  Measurement of radiative and nonradiative recombination rates in InGaAsP and AlGaAs light sources , 1984 .

[19]  H. Sakaki,et al.  Multidimensional quantum well laser and temperature dependence of its threshold current , 1982 .