Low temperature nanoparticle sintering with continuous wave and pulse lasers

Abstract New manufacturing methods are being sought for electronics production. Printable electronics is a promising method for producing low cost and large-scale electronics. In printable electronics nanoparticle inks printed on the surface of substrate contain additives, such as dispersing agent and carrier fluids that provide good printing properties by changing the viscosity and separating the nanoparticles of the ink. In the sintering process ink particles are heated to a certain, ink-specific temperature. During the sintering process the carrier fluid and dispersing agents are evaporated from the ink. Additional heating after evaporation causes the nanoparticles to start to agglomerate. A small particle size allows the use of a considerably lower sintering temperature than with bulk silver, for example 220 °C. The sintering process is usually utilized with a convection oven, with a long sintering time, and the thermal load on the surrounding material can become too great as components and patterns are formed from layers of different type inks. Hence, alternative sintering methods are sought. This paper describes tests done with two different types of laser; pulsed and continuous wave lasers. Laser sintering enables short sintering times and selective sintering, making it possible for printed structures to contain fragile active components produced with other technologies.

[1]  Tomi Mattila,et al.  Electrical sintering of nanoparticle structures , 2008, Nanotechnology.

[2]  M. Gedvilas,et al.  Patterning of ITO Layer on Glass with High Repetition Rate Picosecond Lasers , 2007 .

[3]  C. Grigoropoulos,et al.  All-inkjet-printed flexible electronics fabrication on a polymer substrate by low-temperature high-resolution selective laser sintering of metal nanoparticles , 2007 .

[4]  Tao Wang,et al.  Low-Temperature Sintering with Nano-Silver Paste in Die-Attached Interconnection , 2007 .

[5]  Sawyer B. Fuller,et al.  Ink-jet printed nanoparticle microelectromechanical systems , 2002 .

[6]  K. Suganuma,et al.  Novel method for room temperature sintering of Ag nanoparticle paste in air , 2007 .

[7]  Ching-Ping Wong,et al.  Thermal behavior of silver nanoparticles for low-temperature interconnect applications , 2005 .

[8]  V. Marinov,et al.  Electrical Resistance of Laser Sintered Direct-Write Deposited Materials for Microelectronic Applications , 2004 .

[9]  U. Schubert,et al.  Ink‐jet Printing and Microwave Sintering of Conductive Silver Tracks , 2006 .

[10]  Daniel Gamota,et al.  Printed Organic and Molecular Electronics , 2004 .

[11]  C. Grigoropoulos,et al.  Air stable high resolution organic transistors by selective laser sintering of ink-jet printed metal nanoparticles , 2007 .

[12]  Scott A. Mathews,et al.  Laser Direct-Write of Metallic Nanoparticle Inks , 2007 .

[13]  Seong-Gu Baek,et al.  Thermal behavior of direct-printed lines of silver nanoparticles , 2006 .

[14]  Costas P. Grigoropoulos,et al.  Conductor microstructures by laser curing of printed gold nanoparticle ink , 2004 .

[15]  Chung-Chih Wu,et al.  Ink-jet printing of doped polymers for organic light emitting devices , 1998 .

[16]  Orven F. Swenson,et al.  Laser sintering of direct write silver nano-ink conductors for microelectronic applications , 2008, SPIE LASE.

[17]  C. Koch,et al.  Nanostructured Materials: Processing Properties, and Potential Applications , 2002 .