Study of dielectric function of (FeCoZr)x(CaF2)(100−x) nanocomposites produced with a beam of argon ions

Abstract The paper presents investigations of frequency and temperature dependences on capacitance, phase shift and loss tangent of nanocomposites (FeCoZr) x (CaF 2 ) (100−x) of the metallic phase content x  = 66.3 at.%. The sample was subjected to 15 min annealing at temperature 723 K. It has been established that within the range of 50 Hz–5 × 10 4  Hz the frequency dependence on capacitance and conductivity is weak. Further frequency increase brings about rapid decrease of capacitance and the conductivity growth. Those both processes can be described with the same relaxation time value of ca 5 × 10 −7  s. Based on the Arrhenius plots, activation energy values have been determined and they are of ca 0.112 eV and 0.0134 eV for the conductivity and permittivity, respectively. It is consistent with the model of hopping recharging, which shows that the permittivity activation energy should be lower than the conductivity activation energy. It has been established, that order of the permittivity activation energy is comparable to the potential energy of the interaction between elementary charges, negative and positive (dipole) ones located in adjacent potential wells.

[1]  A. Yalovets,et al.  THE LIQUID-PHASE MASS TRANSFER OF MATERIAL IN THE FILM−SUBSTRATE SYSTEM EXPOSED TO INTENSE ENERGY FLOWS , 2013 .

[2]  P. Węgierek,et al.  Formation of Noncoil-Like Inductance in Nanocomposites (Fe0.45Co0.45Zr0.10)x(Al2O3)1-xManufactured by Ion-Beam Sputtering of Complex Targets in Ar+O2Atmosphere , 2011 .

[3]  P. Malecki,et al.  Sol-gel method as a way of carbonyl iron powder surface modification for interaction improvement , 2015 .

[4]  M. Opielak,et al.  Structure and Properties of Multilayer Nanostructured Coatings TiN/MoN Depending on Deposition Conditions , 2014 .

[5]  Vitalii Bondariev,et al.  Annealing of (CoFeZr)x(CaF2)100-xNanocomposites Produced by the Ion-Beam Sputtering in the Ar and O2Ambient , 2013 .

[6]  Michael Tinkham,et al.  Introduction to mesoscopic physics , 1997 .

[7]  Fadei F. Komarov,et al.  Adhesive strength, superhardness, and the phase and elemental compositions of nanostructured coatings based on Ti-Hf-Si-N , 2012 .

[8]  P. Bury,et al.  Structure of transformer oil-based magnetic fluids studied using acoustic spectroscopy , 2013 .

[9]  Ionoluminescence of porous silicon , 1993 .

[10]  V. Beresnev,et al.  Effect of the preparation conditions on the phase composition, structure, and mechanical characteristics of vacuum-Arc Zr-Ti-Si-N coatings , 2011 .

[11]  A. Rodzik,et al.  Dielectric constant and ac conductivity of semi-insulating Cd[sub 1−x]Mn[sub x]Te semiconductors , 1997 .

[12]  Ma Tengcai,et al.  A biasing method for plasma immersion ion implantation and deposition process to enhance coating adhesion , 2007 .

[13]  A. Patryn,et al.  Influence of matrix type on negative capacitance effect in nanogranular composite films FeCoZr-insulator , 2013 .

[14]  J. E. Moyal.  XXX. Theory of ionization fluctuations , 1955 .

[15]  F. Komarov,et al.  Effects of surfactant and fabrication procedure on the electrical conductivity and electromagnetic shielding of single‐walled carbon nanotube films , 2015 .

[16]  K. Legg,et al.  Ion implantation as an industrial process , 1992 .

[17]  V. M. Beresnev,et al.  Nanocoatings Nanosystems Nanotechnologies , 2012 .

[18]  F. Komarov,et al.  Ion implantation for local change of the optical constants of polymer films , 2002 .

[19]  A. Pogrebnjak,et al.  Structure and properties of nanostructured (Ti-Hf-Zr-V-Nb)N coatings , 2013 .

[20]  E. Kostyukevich,et al.  AUSTENITIC STEEL SURFACE ALLOYED WITH ZIRCONIUM USING COMPRESSION PLASMA FLOW , 2012 .

[21]  Konrad Kierczyński,et al.  Formation of water nanodrops in cellulose impregnated with insulating oil , 2015, Cellulose.

[22]  G. Psarras,et al.  Dielectric dispersion and ac conductivity in—Iron particles loaded—polymer composites , 2003 .

[24]  S. I. Ananin,et al.  ALLOYING OF CARBON STEEL SURFACE BY TANTALUM USING COMPRESSION PLASMA FLOW , 2013 .

[25]  Miroslav Gutten,et al.  Assessment of water content in an impregnated pressboard based on DC conductivity measurements theoretical assumptions , 2014, IEEE Transactions on Dielectrics and Electrical Insulation.

[26]  A. Pogrebnjak,et al.  Application of micro- and nanoprobes to the analysis of small-sized 3D materials, nanosystems, and nanoobjects , 2012 .

[27]  V. F. Stelmakh,et al.  Study of the Dielectric Function of Silicon Irradiated with a Large Dose of Neutrons , 1991 .

[28]  Vitalii Bondariev,et al.  The effect of annealing on induction like properties of (FeCoZr)x(CaF2)(100−x) nanocomposite films produced by ion-beam sputtering in the vacuum environment , 2015 .

[29]  Marek Opielak,et al.  Mechanical Properties of Zn-Ni-SiO_2 Coating Deposited under X-ray Irradiation , 2014 .

[30]  R. Haglund.  Ion implantation as a tool in the synthesis of practical third-order nonlinear optical materials , 1998 .

[31]  S. Nemov,et al.  Hopping conduction via strongly localized impurity states of indium in PbTe and its solid solutions , 2002 .

[32]  P. Bury,et al.  Temperature Effect on the Structure of Transformer Oil Based Magnetic Fluids Using Acoustic Spectroscopy , 2012 .

[33]  Garima Singh,et al.  Sol-Gel processing of silica nanoparticles and their applications. , 2014, Advances in colloid and interface science.

[34]  A. Fedotov,et al.  Negative capacitance in (FeCoZr)–(PZT) nanocomposite films , 2013 .

[35]  A. Fedotov,et al.  AC/DC conductance in granular nanocomposite films (Fe45Co45Zr10)x(CaF2)100−x , 2014 .

[36]  Vitalii Bondariev,et al.  Enhancement of negative capacitance effect in (CoFeZr)x(CaF2)(100−x) nanocomposite films deposited by ion beam sputtering in argon and oxygen atmosphere , 2014 .