Fabrication of Metal Nanobridge Arrays using Sacrificial Silicon Nanowire

Novel fabrication method of nanobridge array of various materials was proposed using suspended silicon nanowire array as a sacrificial template structure. Nanobridges of various materials can be simply fabricated by direct deposition with thermal evaporation on the top of prefabricated suspended silicon nanobridge arrays, which are used as a sacrificial structure. Since silicon nanowire can be easily removed by selective dry etching, nanobridge arrays of an intended material are finally obtained. In this paper, metal nanobridges of Ti/Au, around 50-200 nm in thickness and width, 5-20 μm in length were fabricated to prove the advantages of the proposed nanowire or nanobridge fabrication method. The nanobridges of Ti/Au after complete removal of sacrificial silicon nanowire template were well-established and bending of nanobridge caused by the tensile stress was observed after silicon removing. Up to 50 nm and 10 μm of silicon nanowire in diameter and length respectively was also very useful for nanowire templates.