Surface charge tuning of ceria particles by titanium doping: Towards significantly improved polishing performance
暂无分享，去创建一个
Shiyou Hao | Yongxiu Li | X. Zhou | L. Yanhua | Maosheng Fu | Lianghua Wei
[1] Maurice Gell,et al. Apatite formation on alkaline-treated dense TiO2 coatings deposited using the solution precursor plasma spray process. , 2008, Acta biomaterialia.
[2] T. Hyeon,et al. Large‐Scale Synthesis of Water Dispersible Ceria Nanocrystals by a Simple Sol–Gel Process and Their Use as a Chemical Mechanical Planarization Slurry , 2008 .
[3] K. N. Sood,et al. Effect of precursor sol's aging on properties of nanostructured thin films with coexistent CeO2 and CeTi2O6 phases , 2007 .
[4] Songlin Feng,et al. Ceria concentration effect on chemical mechanical polishing of optical glass , 2007 .
[5] Masato Yoshida,et al. A New Cerium-Based Ternary Oxide Slurry, CeTi2O6, for Chemical-Mechanical Polishing , 2007 .
[6] Zhong Lin Wang,et al. Converting Ceria Polyhedral Nanoparticles into Single-Crystal Nanospheres , 2006, Science.
[7] D. Lim,et al. The effect of CeO2 abrasive size on dishing and step height reduction of silicon oxide film in STI–CMP , 2005 .
[8] Y. Li,et al. Synthesis of CeO2 nanoparticles by mechanochemical processing and the inhibiting action of NaCl on particle agglomeration , 2005 .
[9] S. Babu,et al. Study of Surface Charge Effects on Oxide and Nitride Planarization Using Alumina/Ceria Mixed Abrasive Slurries , 2004 .
[10] Arun K. Sikder,et al. Chemical mechanical planarization for microelectronics applications , 2004 .