Effect of wheel speed on magnetic and mechanical properties of melt spun Fe-6.5 wt.% Si high silicon steel

Fe-Si electric steel is the most widely used soft magnetic material in electric machines and transformers. Increasing the silicon content from 3.2 wt.% to 6.5 wt.% brings about large improvement in the magnetic and electrical properties. However, 6.5 wt.% silicon steel is inherited with brittleness owing to the formation of B2 and D03 ordered phase. To obtain ductility in Fe-6.5wt.% silicon steel, the ordered phase has to be bypassed with methods like rapid cooling. In present paper, the effect of cooling rate on magnetic and mechanical properties of Fe-6.5wt.% silicon steel is studied by tuning the wheel speed during melt spinning process. The cooling rate significantly alters the ordering and microstructure, and thus the mechanical and magnetic properties. X-ray diffraction data shows that D03 ordering was fully suppressed at high wheel speeds but starts to nucleate at 10m/s and below, which correlates with the increase of Young’s modulus towards low wheel speeds as tested by nanoindentation. The grain sizes of the ribbons on the wheel side decrease with increasing wheel speeds, ranging from ∼100 μm at 1m/s to ∼8 μm at 30m/s, which lead to changes in coercivity.

[1]  T. Sritharan,et al.  Ordering and grain growth in nanocrystalline Fe75Si25 alloy , 2005 .

[2]  K. Arai,et al.  Ribbon-form silicon-iron alloy containing around 6.5 percent silicon , 1980 .

[3]  R. Misra,et al.  Evolution of microstructure and texture in grain-oriented 6.5%Si steel processed by strip-casting , 2017 .

[4]  M. Abe,et al.  Commercial scale production of Fe-6.5 wt. % Si sheet and its magnetic properties , 1988 .

[5]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[6]  T. Hiratani,et al.  Magnetic properties and workability of 6.5% Si steel sheet , 1996 .

[7]  J. Lin,et al.  Cold rolled Fe-6.5 wt. % Si alloy foils with high magnetic induction , 2012 .

[8]  Hyuck-Mo Lee,et al.  Ordering–disordering phenomena and micro-hardness characteristics of B2 phase in Fe–(5–6.5%)Si alloys , 2005 .

[9]  G. Chen,et al.  Effect of annealing temperature on magnetic properties of cold rolled high silicon steel thin sheet , 2010 .

[10]  Junpin Lin,et al.  Fabrication of Fe-6.5wt%Si Ribbons by Melt Spinning Method on Large Scale , 2015 .

[11]  A. L. Greer.  Grain refinement in rapidly solidified alloys , 1991 .

[12]  X. Bi,et al.  Fabrication and magnetic properties of Fe–6.5% Si alloys by magnetron sputtering method , 2010 .

[13]  P. Ramachandrarao.  Rapid solidification of steels , 1992 .

[14]  Y. Houbaert,et al.  Production of high silicon steel for electrical applications by thermomechanical processing , 2003 .

[15]  P. Swann,et al.  The B2 and DO3 Ordering Reactions in Iron–Silicon Alloys in the Vicinity of the Curie Temperature , 1975 .

[16]  Huadong Fu,et al.  Effects of precipitated phase and order degree on bending properties of an Fe-6.5 wt%Si alloy with columnar grains , 2011 .

[17]  T. Sato,et al.  Production and properties of melt-spun Fe-6.5wt.%Si ribbons , 1988 .

[18]  R. McCallum,et al.  Rapid solidification and metallic glass formation – Experimental and theoretical limits , 2007 .