Natural hydrophobicity and reversible wettability conversion of flat anatase TiO₂ thin film.

Flat anatase TiO2 thin film deposited at room temperature shows the natural hydrophobicity, which is destroyed by 400 °C vacuum annealing. On the basis of the analysis of surface composition and structure, the origin of hydrophobicity of the flat TiO2 film can be identified as (1) approximately fully stoichiometric TiO2 and (2) hydrocarbon adsorbates on the film surface. We further validate that interfacial water molecules near the surface of the as-prepared TiO2 film are oriented in the hydrophobic hydration structure via Fourier transform infrared/attenuated total reflection. Moreover, the as-prepared TiO2 film also shows a smart surface reversibly switched between hydrophobicity and super-hydrophilicity. During the recovery process of hydrophobicity, the irradiated films show the wettability with water contact angle of 107 ± 1.7, 72 ± 2.5, 80 ± 1.1, and 17 ± 1.3° corresponding to after a week of exposure to ambient air, O2, CF4, and Ar, respectively. It can be strongly reinforced that the stoichiometry and the adsorbates both play an important role in forming the hydrophobic TiO2 films.

[1]  A. Fujishima,et al.  Studies of Surface Wettability Conversion on TiO2 Single-Crystal Surfaces , 1999 .

[2]  Eiichi Kojima,et al.  Light-induced amphiphilic surfaces , 1997, Nature.

[3]  B. Grzybowska,et al.  Effect of potassium on the surface potential of titania , 1994 .

[4]  M. Engelhard,et al.  Interactions of Liquid and Vapor Water with Stoichiometric and Defective TiO2(100) Surfaces , 1999 .

[5]  Annabella Selloni,et al.  Structure and energetics of stoichiometric TiO 2 anatase surfaces , 2001 .

[6]  R. Caminiti,et al.  Short Hydrogen Bonds at the Water/TiO2 (Anatase) Interface , 2008 .

[7]  A. Parker,et al.  Water capture by a desert beetle , 2001, Nature.

[8]  R. N. Wenzel.  RESISTANCE OF SOLID SURFACES TO WETTING BY WATER , 1936 .

[9]  J. Drelich,et al.  Origins of thermodynamically stable superhydrophobicity of boron nitride nanotubes coatings. , 2012, Langmuir : the ACS journal of surfaces and colloids.

[10]  O. Brümmer,et al.  Corundum Structure Oxides Studied by XPS , 1983 .

[11]  Lei Jiang,et al.  Reversible switching between superhydrophilicity and superhydrophobicity. , 2004, Angewandte Chemie.

[12]  De‐Yin Wu,et al.  Raman spectroscopic and quantum chemical study of hydrogen adsorption at platinum electrodes , 1999 .

[13]  H. Erbil,et al.  Transformation of a Simple Plastic into a Superhydrophobic Surface , 2003, Science.

[14]  A. Cassie,et al.  Wettability of porous surfaces , 1944 .

[15]  P. Rossky,et al.  Water reorientation, hydrogen-bond dynamics and 2D-IR spectroscopy next to an extended hydrophobic surface. , 2010, Faraday discussions.

[16]  H. Tsao,et al.  Superhydrophilicity to superhydrophobicity transition of CuO nanowire films , 2010 .

[17]  Jungmok Seo,et al.  Guided transport of water droplets on superhydrophobic-hydrophilic patterned Si nanowires. , 2011, ACS applied materials & interfaces.

[18]  G. Richmond,et al.  Water at Hydrophobic Surfaces: Weak Hydrogen Bonding and Strong Orientation Effects , 2001, Science.

[19]  K. Leung,et al.  Reversible switching between hydrophilic and hydrophobic superparamagnetic iron oxide microspheres via one-step supramolecular dynamic dendronization: exploration of dynamic wettability. , 2009, ACS applied materials & interfaces.

[20]  Y. Shen,et al.  Surface Vibrational Spectroscopic Studies of Hydrogen Bonding and Hydrophobicity , 1994, Science.

[21]  Pablo G Debenedetti,et al.  Effect of surface polarity on water contact angle and interfacial hydration structure. , 2007, The journal of physical chemistry. B.

[22]  A. Reller,et al.  Photoinduced reactivity of titanium dioxide , 2004 .

[23]  Yichun Liu,et al.  Morphologically-tunable TiO2 nanorod film with high energy facets: green synthesis, growth mechanism and photocatalytic activity. , 2012, Nanoscale.

[24]  A. Vladár,et al.  Contamination-free imaging by electron induced carbon volatilization in environmental scanning electron microscopy , 2009 .

[25]  Jin Zhai,et al.  Reversible super-hydrophobicity to super-hydrophilicity transition of aligned ZnO nanorod films. , 2004, Journal of the American Chemical Society.

[26]  Ping Chen,et al.  Reversible switching on superhydrophobic TiO2 nano-strawberry films fabricated at low temperature. , 2008, Chemical communications.

[27]  K. Moon,et al.  Reversible superhydrophobic-superhydrophilic transition of ZnO nanorod/epoxy composite films. , 2012, ACS applied materials & interfaces.

[28]  Jin Zhai,et al.  Super-hydrophobic surfaces: From natural to artificial , 2002 .

[29]  A. Fujishima,et al.  Superhydrophobic TiO2 Surfaces: Preparation, Photocatalytic Wettability Conversion, and Superhydrophobic-Superhydrophilic Patterning , 2007 .

[30]  Rajeev Dhiman,et al.  Hydrophobicity of rare-earth oxide ceramics. , 2013, Nature materials.