Effect of poly(ethylene glycol) molecular weight on tensile and swelling properties of oligo(poly(ethylene glycol) fumarate) hydrogels for cartilage tissue engineering.

This study was designed to determine the effect of changes in poly(ethylene glycol) (PEG) molecular weight on swelling and mechanical properties of hydrogels made from a novel polymer, oligo(poly(ethylene glycol) fumarate) (OPF), recently developed in our laboratory. Properties of hydrogels made from OPF with initial PEG molecular weights of 860, 3900, and 9300 were examined. The PEG 3900 formulation had a tensile modulus of 23.1 +/- 12.4 kPa and percent elongation at fracture of 53.2 +/- 13.7%; the PEG 9300 formulation had similar tensile properties (modulus: 16.5 +/- 4.6 kPa, elongation: 76.0 +/- 26.4%). However, the PEG 860 gels had a significantly higher modulus (89.5 +/- 50.7 kPa) and a significantly smaller percent elongation at fracture (30.1 +/- 6.4%), when compared with other formulations. Additionally, there were significant differences in percent swelling between each of the formulations. Molecular weight between crosslinks (M(c)) and mesh size were calculated for each OPF formulation. M(c) increased from 2010 +/- 116 g/mol with PEG 860 to 6250 +/- 280 g/mol with PEG 9300. Mesh size calculations showed a similar trend (76 +/- 2 A for PEG 860 to 160 +/- 6 A for PEG 9300). It was also found that these hydrogels could be laminated if a second layer was added before the first had completely crosslinked. Mechanical testing of these laminated gels revealed that the presence of an interfacial area did not significantly alter their tensile properties. These results suggest that the material properties of OPF-based hydrogels can be altered by changing the molecular weight of PEG used in synthesis and that multilayered OPF hydrogel constructs can be produced, with each layer having distinct mechanical properties.

[1]  D. J. Montgomery,et al.  The physics of rubber elasticity , 1949 .

[2]  Fred W. Billmeyer,et al.  Textbook Of Polymer Science , 1971 .

[3]  W. Oppermann,et al.  Elasticity and swelling behaviour of chemically crosslinked cellulose ethers in aqueous systems , 1990 .

[4]  D. Mooney,et al.  Degradation behavior of covalently cross-linked poly(aldehyde guluronate) hydrogels , 2000 .

[5]  Antonios G. Mikos,et al.  Synthesis and Characterization of Oligo(poly(ethylene glycol) fumarate) Macromer , 2001 .

[6]  J. Elisseeff,et al.  Photoencapsulation of chondrocytes in poly(ethylene oxide)-based semi-interpenetrating networks. , 2000, Journal of biomedical materials research.

[7]  B. D. Barr-Howell,et al.  Characterization of the Cross-Linked Structure of Hydrogels , 1986, Hydrogels in Medicine and Pharmacy.

[8]  M. Newman,et al.  Safety of Poly(ethylene glycol) and Poly(ethylene glycol) Derivatives , 1997 .

[9]  C. Bowman,et al.  Mechanical properties of hydrogels and their experimental determination. , 1996, Biomaterials.

[10]  J. M. Harris,et al.  Poly(Ethylene Glycol) Chemistry , 1992 .

[11]  S. A. Dubrovskii,et al.  Elastic and Osmotic Behavior and Network Imperfections of Nonionic and Weakly Ionized Acrylamide-Based Hydrogels , 1997 .

[12]  S J Bryant,et al.  The effects of scaffold thickness on tissue engineered cartilage in photocrosslinked poly(ethylene oxide) hydrogels. , 2001, Biomaterials.

[13]  N. Peppas,et al.  Crosslinked poly(vinyl alcohol) hydrogels as swollen elastic networks , 1977 .

[14]  D. Mooney,et al.  Rigidity of Two-Component Hydrogels Prepared from Alginate and Poly(ethylene glycol)−Diamines , 1999 .

[15]  W McIntosh,et al.  Transdermal photopolymerization for minimally invasive implantation. , 1999, Proceedings of the National Academy of Sciences of the United States of America.

[16]  A. Mikos,et al.  Review: tissue engineering for regeneration of articular cartilage. , 2000, Biomaterials.