Effects of sulfur substitution on chemical bonding nature and electrochemical performance of layered LiMn0.9Cr0.1O2-xSx

Sulfur-substituted LiMn 0.9 Cr 0.1 O 2-x S x (0≤x≤0.1) layered oxides have been prepared by solid state reaction under inert atmosphere. From powder X-ray diffraction analyses, all the present lithium manganates were found to be crystallized with monoclinic-layered structure. Electrochemical measurements clearly demonstrated that, in comparison with the pristine LiMn 0.9 Cr 0.1 O 2 , the sulfur-substituted derivatives exhibit smaller discharge capacities for the entire cycle range but the recovery of discharge capacity after the initial several cycles becomes faster upon sulfur substitution. The effect of the sulfur substitution on the chemical bonding nature of LiMn 0.9 Cr 0.1 O 2-x S x has been investigated using X-ray absorption spectroscopic (XAS) analyses at Mn and Cr K-edges. According to Mn K-edge XAS results, the trivalent oxidation state of manganese ion remains unchanged before and after the substitution whereas the local structure around manganese ions becomes more distorted with increasing the substitution rate of sulfur. On the other hand, the replacement of oxygen with sulfur has negligible influence on the local atomic arrangement around chromium ions, which is surely due to the high octahedral stabilization energy of Cr +III ions. Based on the present experimental findings, we have suggested that the decrease of discharge capacity upon sulfur substitution is ascribable to the enhanced structural distortion of MnO 6 octahedra and/or to the formation of covalent Li-S bonds, and the accompanying improvement of cyclability would be related to the depression of Mn migration and/or to the pillaring effect of larger sulfur anion.

[1]  J. Choy,et al.  Local atomic arrangement and electronic structure of nanocrystalline transition metal oxides determined by X-ray absorption spectroscopy , 2003 .

[2]  Y. S. Lee,et al.  Synthesis and electrochemical properties of sulfur doped-LixMnO2−ySy materials for lithium secondary batteries , 2003 .

[3]  M. Kakihana,et al.  Local crystal structure around manganese in new potassium-based nanocrystalline manganese oxyiodide , 2002 .

[4]  G. Park,et al.  Structural Changes (Degradation) of Oxysulfide LiAl0.24Mn1.76 O 3.98 S 0.02 Spinel on High-Temperature Cycling , 2001 .

[5]  J. Choy,et al.  Effects of Chromium Substitution on the Chemical Bonding Nature and Electrochemical Performance of Layered Lithium Manganese Oxide , 2000 .

[6]  J. Choy,et al.  Evolution of Local Structure around Manganese in Layered LiMnO2 upon Chemical and Electrochemical Delithiation/Relithiation , 2000 .

[7]  K. Nahm,et al.  Synthesis and Characterization of a New Spinel, Li1.02Al0.25Mn1.75 O 3.97 S 0.03, Operating at Potentials Between 4.3 and 2.4 V , 2000 .

[8]  Seung‐Wan Song,et al.  Relationship between Chemical Bonding Nature and Electrochemical Property of LiMn2O4 Spinel Oxides with Various Particle Sizes: “Electrochemical Grafting” Concept , 1999 .

[9]  K. West,et al.  Lithium Intercalation into Layered LiMnO2 , 1997 .

[10]  Michael M. Thackeray,et al.  Manganese oxides for lithium batteries , 1997 .

[11]  Boon K. Teo,et al.  EXAFS: Basic Principles and Data Analysis , 1986 .

[12]  R. D. Shannon Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides , 1976 .

[13]  James E. Huheey,et al.  Inorganic chemistry; principles of structure and reactivity , 1972 .