Measurement of the full-field polymerization shrinkage and depth of cure of dental composites using digital image correlation.

OBJECTIVES The aim of this study was to measure the full-field polymerization shrinkage of dental composites using optical image correlation method. METHODS Bar specimens of cross-section 4mm x 2mm and length 10mm approximately were light cured with two irradiances, 450 mW/cm(2) and 180 mW/cm(2), respectively. The curing light was generated with Optilux 501 (Kerr) and the two different irradiances were achieved by adjusting the distance between the light tip and the specimen. A single-camera 2D measuring system was used to record the deformation of the composite specimen for 30 min at a frequency of 0.1 Hz. The specimen surface under observation was sprayed with paint to produce sufficient contrast to allow tracking of individual points on the surface. The curing light was applied to one end of the specimen for 40s during which the painted surface was fully covered. After curing, the cover was removed immediately so that deformation of the painted surface could be recorded by the camera. The images were then analyzed with specialist software and the volumetric shrinkage determined along the beam length. RESULTS A typical shrinkage strain field obtained on a specimen surface was highly non-uniform, even at positions of constant distance from the irradiation surface, indicating possible heterogeneity in material composition and shrinkage behavior in the composite. The maximum volumetric shrinkage strain of approximately 1.5% occurred at a subsurface distance of about 1mm, instead of at the irradiation surface. After reaching its peak value, the shrinkage strain then gradually decreased with increasing distance along the beam length, before leveling off to a value of approximately 0.2% at a distance of 4-5mm. The maximum volumetric shrinkage obtained agreed well with the value of 1.6% reported by the manufacturer for the composite examined in this work. Using irradiance of 180 mW/cm(2) resulted in only slightly less polymerization shrinkage than using irradiance of 450 mW/cm(2). SIGNIFICANCE Compared to the other measurement methods, the image correlation method is capable of producing full-field information about the polymerization shrinkage behavior of dental composites.

[1]  Sheng Lin-Gibson,et al.  X-ray microcomputed tomography for measuring polymerization shrinkage of polymeric dental composites. , 2008, Dental materials : official publication of the Academy of Dental Materials.

[2]  Gustavo F. Arenas,et al.  Polymerization shrinkage of a dental resin composite determined by a fiber optic Fizeau interferometer , 2007 .

[3]  A. Versluis,et al.  Analysis of strain gage method for measurement of post-gel shrinkage in resin composites. , 1997, Dental materials : official publication of the Academy of Dental Materials.

[4]  Andrej Meniga,et al.  Digital interferometry for measuring of the resin composite thickness variation during blue light polymerization , 2004 .

[5]  J. Embury,et al.  Digital image correlation studies for microscopic strain distribution and damage in dual phase steels , 2007 .

[6]  D. Watts.  Reaction kinetics and mechanics in photo-polymerised networks. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[7]  B. Suh,et al.  Volumetric shrinkage of composites using video-imaging. , 2003, Journal of dentistry.

[8]  K. Jandt,et al.  Knoop hardness depth profiles and compressive strength of selected dental composites polymerized with halogen and LED light curing technologies. , 2002, Journal of biomedical materials research.

[9]  V. Fano,et al.  Polymerization shrinkage of microfilled composites determined by laser beam scanning. , 1997, Biomaterials.

[10]  Douglas A Terry,et al.  Applications of nanotechnology. , 2004, Practical procedures & aesthetic dentistry : PPAD.

[11]  J. Ferracane,et al.  In vitro aging of dental composites in water--effect of degree of conversion, filler volume, and filler/matrix coupling. , 1998, Journal of biomedical materials research.

[12]  R. Sakaguchi,et al.  Critical configuration analysis of four methods for measuring polymerization shrinkage strain of composites. , 2004, Dental materials : official publication of the Academy of Dental Materials.

[13]  M. T. Kelly,et al.  Laser interferometric method for measuring linear polymerization shrinkage in light cured dental restoratives. , 2002, Dental materials : official publication of the Academy of Dental Materials.

[14]  C. Davidson,et al.  A modified dilatometer for continuous recording of volumetric polymerization shrinkage of composite restorative materials. , 1981, Journal of dentistry.

[15]  A. Feilzer,et al.  True linear polymerization shrinkage of unfilled resins and composites determined with a linometer. , 1993, Dental materials : official publication of the Academy of Dental Materials.

[16]  D. Watts,et al.  3D-marginal adaptation versus setting shrinkage in light-cured microhybrid resin composites. , 2007, Dental materials : official publication of the Academy of Dental Materials.

[17]  J. Middleton,et al.  Identification of the Constitutive Behaviour of Dental Composite Cements During Curing. , 1999, Computer methods in biomechanics and biomedical engineering.

[18]  E. Frollini,et al.  Monomer conversion at different dental composite depths using six light-curing methods , 2006 .

[19]  W H Douglas,et al.  Strain gauge method for measuring polymerization contraction of composite restoratives. , 1991, Journal of dentistry.

[20]  P Neuhaus,et al.  Correlation of intimal hyperplasia development and shear stress distribution at the distal end-side-anastomosis, in vitro study using particle image velocimetry. , 2003, European journal of vascular and endovascular surgery : the official journal of the European Society for Vascular Surgery.

[21]  Jack L Ferracane,et al.  A pilot study of a simple photon migration model for predicting depth of cure in dental composite. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[22]  William M Palin,et al.  In vitro cuspal deflection and microleakage of maxillary premolars restored with novel low-shrink dental composites. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[23]  B. Lim,et al.  The effect of consistency, specimen geometry and adhesion on the axial polymerization shrinkage measurement of light cured composites. , 2006, Dental Materials.

[24]  D C Watts,et al.  Determination of polymerization shrinkage kinetics in visible-light-cured materials: methods development. , 1991, Dental materials : official publication of the Academy of Dental Materials.