Conductivity spectroscopy on melt processed polypropylene–multiwalled carbon nanotube composites: Recovery after shear and crystallization

Abstract Frequency dependent investigations of conductivity and dielectric permittivity have been performed on composites of polypropylene (PP) containing different amounts of 2, 3.5, and 5 wt% of multiwalled carbon nanotubes (MWNTs) in the melt and during crystallization. The experiments were performed in a measurement slit die containing two dielectric sensors in plate–plate geometry, which was flanged to the outlet of a single screw laboratory extruder. AC conductivity and the related complex permittivity were measured in the frequency range from 20 Hz to 10 6  Hz after stopping the extruder (recovery after shearing) and during cooling (non-isothermal crystallization). For a sample with a MWNT content of 2 wt% the AC conductivity shows a tremendous increase with time after shearing was stopped. This conductivity recovery is explained by the reorganization of the conducting network-like filler structure, which was partially destroyed by the shear. The reformation kinetics of filler clusters is assumed to be due to a cooperative aggregation. For conductive fillers in a thermoplastic matrix the kinetics of cooperative aggregation is coupled to the electrical percolation. The reorganization of the percolation network can be related to reformation of (i) the local contact regions between the nanotubes (separated by polymer chains) and (ii) to the reorientation of nanotubes oriented in the shear flow. The conductivity recovery is less pronounced for samples with MWNT concentrations well above the percolation threshold. During cooling of the melt to temperatures below crystallization a significant decrease in the conductivity and permittivity was detected. This is consistently expressed in the conductivity and permittivity spectra and can be explained by reduction of the amorphous phase (high ion mobility) on expense of the crystalline phase and/or by crystalline regions in the contact region between tubes.

[1]  Boris I Shklovskii,et al.  Critical Behaviour of Conductivity and Dielectric Constant near the Metal-Non-Metal Transition Threshold , 1976 .

[2]  I. Kinloch,et al.  Ultra-low electrical percolation threshold in carbon-nanotube-epoxy composites , 2003 .

[3]  M. Klüppel,et al.  The Role of Disorder in Filler Reinforcement of Elastomers on Various Length Scales , 2003 .

[4]  Masaru Matsuo,et al.  Electrical and mechanical properties of polyimide–carbon nanotubes composites fabricated by in situ polymerization , 2005 .

[5]  Stanley,et al.  Random-walk approach to the two-component random-conductor mixture: Perturbing away from the perfect random resistor network and random superconducting-network limits. , 1986, Physical review. B, Condensed matter.

[6]  Petra Pötschke,et al.  Rheological and dielectrical characterization of melt mixed polycarbonate-multiwalled carbon nanotube composites , 2004 .

[7]  J. Luck,et al.  The electrical conductivity of binary disordered systems, percolation clusters, fractals and related models , 1990 .

[8]  B. Satapathy,et al.  Crack Toughness Behaviour of Multiwalled Carbon Nanotube (MWNT)/Polycarbonate Nanocomposites , 2005 .

[9]  Tsu-Wei Chou,et al.  Nanocomposites in context , 2005 .

[10]  Jonathan N. Coleman,et al.  Mechanical Reinforcement of Polymers Using Carbon Nanotubes , 2006 .

[11]  Joshua Jortner,et al.  Critical exponents for percolation conductivity in resistor networks , 1977 .

[12]  Gert Heinrich,et al.  Recent Advances in the Theory of Filler Networking in Elastomers , 2002 .

[13]  E. Grulke,et al.  Orientation of carbon nanotubes in a sheared polymer melt , 2003 .

[14]  B. Mandelbrot,et al.  Solvable Fractal Family, and Its Possible Relation to the Backbone at Percolation , 1981 .

[15]  Melvin Lax,et al.  Stochastic Transport in a Disordered Solid. I. Theory , 1973 .

[16]  J. Straley.  Critical phenomena in resistor networks , 1976 .

[17]  Werner J. Blau,et al.  High Performance Nanotube‐Reinforced Plastics: Understanding the Mechanism of Strength Increase , 2004 .

[18]  M. Shaffer,et al.  Fabrication and Characterization of Carbon Nanotube/Poly(vinyl alcohol) Composites , 1999 .

[19]  J. Straley,et al.  The ant in the labyrinth: diffusion in random networks near the percolation threshold , 1980 .

[20]  B. Dong,et al.  Enhanced wear resistance and micro-hardness of polystyrene nanocomposites by carbon nanotubes , 2005 .

[21]  A. Rinzler,et al.  ALIGNED SINGLE-WALL CARBON NANOTUBES IN COMPOSITES BY MELT PROCESSING METHODS , 2000 .

[22]  David Wilkinson,et al.  Enhancement of the dielectric constant near a percolation threshold , 1983 .

[23]  R. Gorga,et al.  Toughness enhancements in poly(methyl methacrylate) by addition of oriented multiwall carbon nanotubes , 2004 .

[24]  G. Weiss,et al.  Random Walks: Theory and Selected Applications , 2007 .

[25]  Jack F Douglas,et al.  Flow-induced properties of nanotube-filled polymer materials , 2004, Nature materials.

[26]  David J. Bergman,et al.  Critical Behavior of the Complex Dielectric Constant near the Percolation Threshold of a Heterogeneous Material , 1977 .

[27]  D. Stauffer.  Scaling Theory of Percolation Clusters , 1979, Complex Media and Percolation Theory.

[28]  Y. Gefen,et al.  Dynamic Scaling near the Percolation Threshold in Thin Au Films , 1984 .

[29]  M. Marzantowicz,et al.  Ac conductivity and dielectric permittivity of poly(ethylene glycol) during crystallization: Percolation picture , 2006 .

[30]  J. Kenny,et al.  EFFECTS OF SINGLE-WALLED CARBON NANOTUBES ON THE CRYSTALLIZATION BEHAVIOR OF POLYPROPYLENE , 2003 .

[31]  S. Kirkpatrick.  Percolation and Conduction , 1973 .

[32]  U. Sundararaj,et al.  Big returns from small fibers: A review of polymer/carbon nanotube composites , 2004 .

[33]  S. Roth,et al.  Melt Mixing as Method to Disperse Carbon Nanotubes into Thermoplastic Polymers , 2005 .

[34]  P. G. de Gennes,et al.  On a relation between percolation theory and the elasticity of gels , 1976 .

[35]  Petra Pötschke,et al.  Dielectric spectroscopy on melt processed polycarbonate—multiwalled carbon nanotube composites , 2003 .

[36]  Kathryn M. Butler,et al.  Thermal and flammability properties of polypropylene/carbon nanotube nanocomposites , 2004 .

[37]  Rodney Andrews,et al.  Fabrication of Carbon Multiwall Nanotube/Polymer Composites by Shear Mixing , 2002 .

[38]  M. J. Stephen.  Mean-field theory and critical exponents for a random resistor network , 1978 .

[39]  A. L. Cukierman,et al.  Magnetic properties of multi-walled carbon nanotube–epoxy composites , 2005 .

[40]  S. Havlin,et al.  Fractals and Disordered Systems , 1991 .

[41]  E. Wachtel,et al.  Nucleation ability of multiwall carbon nanotubes in polypropylene composites , 2003 .

[42]  Robert H. Hauge,et al.  Crystallization and orientation studies in polypropylene/single wall carbon nanotube composite , 2003 .

[43]  S. Redner,et al.  Introduction To Percolation Theory , 2018 .

[44]  M. Santare,et al.  Melt processing and mechanical property characterization of multi-walled carbon nanotube/high density polyethylene (MWNT/HDPE) composite films , 2003 .

[45]  M. Sahini,et al.  Applications of Percolation Theory , 2023, Applied Mathematical Sciences.

[46]  I. Alig,et al.  Combination of NIR, Raman, Ultrasonic and Dielectric Spectroscopy for In-Line Monitoring of the Extrusion Process , 2005 .

[47]  D. Resasco,et al.  Nucleation of Polypropylene Crystallization by Single-Walled Carbon Nanotubes , 2002 .

[48]  D. Stroud,et al.  Frequency dependence of the polarization catastrophe at a metal-insulator transition and related problems , 1982 .