High efficiency electrochemical reduction of CO2 beyond the two-electron transfer pathway on grain boundary rich ultra-small SnO2 nanoparticles

Well crystallized and interconnected SnO2 nanoparticles (<5 nm) were synthesized via oxidation of exfoliated SnS2 sheets. The SnO2 nanoparticles exhibit a high total faradaic efficiency (FE) of 97% towards electrochemical reduction of CO2 at −0.95 V vs. the reversible hydrogen electrode (RHE). The main product ratio of CO/HCOO− which intrinsically correlates to the surface SnOx/Sn ratio variation varies with the applied potential. Beyond CO and HCOO− products formed via the two-electron transfer pathway, hydrocarbons and oxygenates are produced. The formation of hydrocarbon (CH4) versus oxygenate (C2H5OH) depends on the choice of electrolyte (KOH vs. KHCO3), both of which can reach a maximal faradaic efficiency of 10%. The distinctive grain boundary and exposed corner/step sites in the interconnected SnO2 nanoparticles contribute to the high FE of CO2 reduction and unique selectivity.

[1]  M. Kanan,et al.  Selective increase in CO2 electroreduction activity at grain-boundary surface terminations , 2017, Science.

[2]  P. Ajayan,et al.  Cryo-mediated exfoliation and fracturing of layered materials into 2D quantum dots , 2017, Science Advances.

[3]  Yuyu Liu,et al.  Design and engineering of urchin-like nanostructured SnO2 catalysts via controlled facial hydrothermal synthesis for efficient electro-reduction of CO2 , 2017 .

[4]  A. Bond,et al.  Direct Detection of Electron Transfer Reactions Underpinning the Tin-Catalyzed Electrochemical Reduction of CO2 using Fourier-Transformed ac Voltammetry , 2017 .

[5]  Joseph H. Montoya,et al.  Electrochemical CO2 reduction on Au surfaces: mechanistic aspects regarding the formation of major and minor products. , 2017, Physical chemistry chemical physics : PCCP.

[6]  Joshua M. Spurgeon,et al.  Reduced SnO2 Porous Nanowires with a High Density of Grain Boundaries as Catalysts for Efficient Electrochemical CO2 -into-HCOOH Conversion. , 2017, Angewandte Chemie.

[7]  Jun‐Jie Zhu,et al.  Tuning Sn-Catalysis for Electrochemical Reduction of CO2 to CO via the Core/Shell Cu/SnO2 Structure. , 2017, Journal of the American Chemical Society.

[8]  D. Macfarlane,et al.  Hierarchical Mesoporous SnO2 Nanosheets on Carbon Cloth: A Robust and Flexible Electrocatalyst for CO2 Reduction with High Efficiency and Selectivity. , 2017, Angewandte Chemie.

[9]  B. Pan,et al.  Metallic tin quantum sheets confined in graphene toward high-efficiency carbon dioxide electroreduction , 2016, Nature Communications.

[10]  Andrés Parra,et al.  Low-energy formate production from CO2 electroreduction using electrodeposited tin on GDE , 2016 .

[11]  E. Stach,et al.  Highly selective plasma-activated copper catalysts for carbon dioxide reduction to ethylene , 2016, Nature Communications.

[12]  T. J. Whittles,et al.  Band Alignments, Valence Bands, and Core Levels in the Tin Sulfides SnS, SnS2, and Sn2S3: Experiment and Theory , 2016 .

[13]  W. Wang,et al.  Electrochemical reduction of CO 2 to formate catalyzed by electroplated tin coating on copper foam , 2016 .

[14]  Yun Huang,et al.  Mechanistic Insights into the Enhanced Activity and Stability of Agglomerated Cu Nanocrystals for the Electrochemical Reduction of Carbon Dioxide to n-Propanol. , 2016, The journal of physical chemistry letters.

[15]  Paul J. A. Kenis,et al.  One-step electrosynthesis of ethylene and ethanol from CO2 in an alkaline electrolyzer , 2016 .

[16]  Abhijit Dutta,et al.  Monitoring the Chemical State of Catalysts for CO2 Electroreduction: An In Operando Study , 2015 .

[17]  J. Savéant,et al.  Current Issues in Molecular Catalysis Illustrated by Iron Porphyrins as Catalysts of the CO2-to-CO Electrochemical Conversion. , 2015, Accounts of chemical research.

[18]  C. Friend,et al.  Achieving Selective and Efficient Electrocatalytic Activity for CO2 Reduction Using Immobilized Silver Nanoparticles. , 2015, Journal of the American Chemical Society.

[19]  Jing Shen,et al.  Catalysts and Reaction Pathways for the Electrochemical Reduction of Carbon Dioxide. , 2015, The journal of physical chemistry letters.

[20]  G. Mul,et al.  Electrocatalytic reduction of carbon dioxide to carbon monoxide and methane at an immobilized cobalt protoporphyrin , 2015, Nature Communications.

[21]  M. Robert,et al.  Molecular Catalysis of the Electrochemical and Photochemical Reduction of CO2 with Earth-Abundant Metal Complexes. Selective Production of CO vs HCOOH by Switching of the Metal Center. , 2015, Journal of the American Chemical Society.

[22]  Hyejin Chang,et al.  Concave Rhombic Dodecahedral Au Nanocatalyst with Multiple High-Index Facets for CO2 Reduction. , 2015, ACS nano.

[23]  D. Vlachos,et al.  Mechanistic Insights into the Electrochemical Reduction of CO2 to CO on Nanostructured Ag Surfaces , 2015 .

[24]  Andrew B. Bocarsly,et al.  Mechanistic Insights into the Reduction of CO2 on Tin Electrodes using in Situ ATR-IR Spectroscopy , 2015 .

[25]  Anders Nilsson,et al.  High selectivity for ethylene from carbon dioxide reduction over copper nanocube electrocatalysts. , 2015, Angewandte Chemie.

[26]  John L DiMeglio,et al.  Efficient Conversion of CO₂ to CO Using Tin and Other Inexpensive and Easily Prepared Post-Transition Metal Catalysts. , 2015, Journal of the American Chemical Society.

[27]  Shoushan Fan,et al.  Grain-boundary-dependent CO2 electroreduction activity. , 2015, Journal of the American Chemical Society.

[28]  X. Bao,et al.  Size-dependent electrocatalytic reduction of CO2 over Pd nanoparticles. , 2015, Journal of the American Chemical Society.

[29]  Matthew W. Kanan,et al.  Controlling H+ vs CO2 Reduction Selectivity on Pb Electrodes , 2015 .

[30]  Thomas F. Jaramillo,et al.  Electrocatalytic conversion of carbon dioxide to methane and methanol on transition metal surfaces. , 2014, Journal of the American Chemical Society.

[31]  Jingjie Wu,et al.  Electrochemical reduction of carbon dioxide: IV dependence of the Faradaic efficiency and current density on the microstructure and thickness of tin electrode , 2014 .

[32]  Etosha R. Cave,et al.  Insights into the electrocatalytic reduction of CO₂ on metallic silver surfaces. , 2014, Physical chemistry chemical physics : PCCP.

[33]  Matthew W. Kanan,et al.  Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper , 2014, Nature.

[34]  G. Somorjai,et al.  In Situ Characterizations of Nanostructured SnOx/Pt(111) Surfaces Using Ambient-Pressure XPS (APXPS) and High-Pressure Scanning Tunneling Microscopy (HPSTM) , 2014 .

[35]  T. Meyer,et al.  Nanostructured tin catalysts for selective electrochemical reduction of carbon dioxide to formate. , 2014, Journal of the American Chemical Society.

[36]  Jingjie Wu,et al.  Electrochemical reduction of carbon dioxide III. The role of oxide layer thickness on the performance of Sn electrode in a full electrochemical cell , 2014 .

[37]  Yihong Chen,et al.  Aqueous CO2 reduction at very low overpotential on oxide-derived Au nanoparticles. , 2012, Journal of the American Chemical Society.

[38]  M. Mura,et al.  Formic Acid: A Promising Bio‐Renewable Feedstock for Fine Chemicals , 2012 .

[39]  Matthew W Kanan,et al.  CO2 reduction at low overpotential on Cu electrodes resulting from the reduction of thick Cu2O films. , 2012, Journal of the American Chemical Society.

[40]  Yihong Chen,et al.  Tin oxide dependence of the CO2 reduction efficiency on tin electrodes and enhanced activity for tin/tin oxide thin-film catalysts. , 2012, Journal of the American Chemical Society.

[41]  C. H. Bhosale,et al.  Physical properties of sprayed antimony doped tin oxide thin films: The role of thickness , 2011 .

[42]  A. Shchukarev,et al.  XPS spectra and electronic structure of Group IA sulfates , 2007 .

[43]  Luca Ottaviano,et al.  XPS study of the surface chemistry of L-CVD SnO2 thin films after oxidation , 2005 .

[44]  Shinobu Fujihara,et al.  Hydrothermal routes to prepare nanocrystalline mesoporous SnO2 having high thermal stability. , 2004, Langmuir : the ACS journal of surfaces and colloids.

[45]  P. Midgley,et al.  Differentiation of tin oxides using electron energy-loss spectroscopy , 2004 .

[46]  Chunrui Wang,et al.  Raman scattering, far infrared spectrum and photoluminescence of SnS2 nanocrystallites , 2002 .

[47]  Hongyuan Chen,et al.  Rapid synthesis of nanocrystalline SnO2 powders by microwave heating method , 2002 .

[48]  Angel Diéguez,et al.  The complete Raman spectrum of nanometric SnO 2 particles , 2001 .

[49]  D. Aurbach,et al.  Sonochemical Synthesis of SnO2 Nanoparticles and Their Preliminary Study as Li Insertion Electrodes , 2000 .

[50]  P. Sherwood,et al.  X‐ray photoelectron spectroscopic studies of sulfates and bisulfates interpreted by Xα and band structure calculations , 2000 .

[51]  Joseph K. L. Lai,et al.  Grain growth in nanocrystalline SnO2 prepared by sol-gel route , 1999 .

[52]  I. Kartio,et al.  XPS study of clean metal sulfide surfaces , 1994 .

[53]  Corallo,et al.  Electron-energy-loss study of the oxidation of polycrystalline tin. , 1992, Physical review. B, Condensed matter.

[54]  Lambin,et al.  Characterization of tin oxides by x-ray-photoemission spectroscopy. , 1992, Physical review. B, Condensed matter.

[55]  Masahiro Watanabe,et al.  Design of Alloy Electrocatalysts for CO 2 Reduction III . The Selective and Reversible Reduction of on Cu Alloy Electrodes , 1991 .

[56]  Ram S. Katiyar,et al.  Dynamics of the rutile structure. III. Lattice dynamics, infrared and Raman spectra of SnO2 , 1971 .