Acid-Alkali-Treated Natural Mordenite-Supported Platinum Nanoparticles (Pt/MORn-H-OH) for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

In this work, a series of natural mordenite-supported platinum (Pt) catalysts were prepared by a facile two-step method, namely, treatment of natural mordenite and then the loading of Pt nanoparticles. The acid-alkali-treated natural mordenite-supported Pt samples (1% Pt/MORn-H-OH) exhibited the highly enhanced catalytic oxidation activity of formaldehyde (HCHO) at room temperature. XRD results showed that the crystalline phase of the mordenite did not change significantly in 1% Pt/MORn-H-OH catalyst. However, the acid-alkali treatment endowed the Pt particles excellent dispersion with the smallest diameter of 2.8 nm in a high loading content, which contributed to the optimal catalytic activity of 1% Pt/MORn-H-OH.

[1]  Tianhu Chen,et al.  Synergetic effect of Cu and Mn oxides supported on palygorskite for the catalytic oxidation of formaldehyde: Dispersion, microstructure, and catalytic performance , 2018, Applied Clay Science.

[2]  Zheng Jiang,et al.  New insight into the enhanced activity of ordered mesoporous nickel oxide in formaldehyde catalytic oxidation reactions , 2018 .

[3]  R. Fréty,et al.  Preparation of zeolite P by desilication and recrystallization of zeolites ZSM-22 and ZSM-35 , 2018 .

[4]  D. Leung,et al.  Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature , 2018 .

[5]  F. Xiao,et al.  Complete oxidation of formaldehyde at room temperature over an Al-rich Beta zeolite supported platinum catalyst , 2017 .

[6]  F. Esenli,et al.  Acid treated mordenites as adsorbents of C2H4 and H2 gases , 2017 .

[7]  M. Jaroniec,et al.  Enhanced formaldehyde oxidation on CeO2/AlOOH-supported Pt catalyst at room temperature , 2016 .

[8]  Kebin Zhou,et al.  Support Morphology-Dependent Catalytic Activity of Pd/CeO₂ for Formaldehyde Oxidation. , 2015, Environmental science & technology.

[9]  M. Jaroniec,et al.  Highly active mesoporous ferrihydrite supported pt catalyst for formaldehyde removal at room temperature. , 2015, Environmental science & technology.

[10]  Q. Trinh,et al.  Removal of ethylene from air stream by adsorption and plasma-catalytic oxidation using silver-based bimetallic catalysts supported on zeolite. , 2015, Journal of hazardous materials.

[11]  F. Xiao,et al.  Importance of platinum particle size for complete oxidation of toluene over Pt/ZSM-5 catalysts. , 2015, Chemical communications.

[12]  M. Jaroniec,et al.  Efficient catalytic removal of formaldehyde at room temperature using AlOOH nanoflakes with deposited Pt , 2015 .

[13]  Wenxiang Zhang,et al.  Catalytic oxidation of formaldehyde over different silica supported platinum catalysts , 2013 .

[14]  M. Flytzani-Stephanopoulos,et al.  Alkali-metal-promoted Pt/TiO2 opens a more efficient pathway to formaldehyde oxidation at ambient temperatures. , 2012, Angewandte Chemie.

[15]  I. Nam,et al.  Oxidation of formaldehyde over Pd/Beta catalyst , 2012 .

[16]  D. Leung,et al.  Complete elimination of indoor formaldehyde over supported Pt catalysts with extremely low Pt content at ambient temperature , 2011 .

[17]  K. Tomishige,et al.  Steam reforming of ethanol over metal-oxide-promoted Pt/SiO2 catalysts: Effects of strong metal-oxide interaction (SMOI) , 2010 .

[18]  Shaobin Wang,et al.  Natural zeolites as effective adsorbents in water and wastewater treatment , 2010 .

[19]  Shudong Wang,et al.  Performance and characterization of supported metal catalysts for complete oxidation of formaldehyde at low temperatures , 2007 .

[20]  K. Rangsriwatananon,et al.  Synthesis of sodium zeolites from natural and modified diatomite , 2005 .

[21]  S. Ülkü,et al.  The effect of HCl treatment on water vapor adsorption characteristics of clinoptilolite rich natural zeolite , 2005 .

[22]  Himanshu Saxena,et al.  Application of natural zeolites in the purification and separation of gases , 2003 .

[23]  Sang-wook Kim,et al.  Characteristics of CO gas adsorption on modified natural zeolite , 1996 .