Effects of ultrasonic vibration on the micro-molding processing of polylactide.

A new ultrasonic micro-molding system was used to process polylactide (PLA) and fabricate reduced dimension specimens. Plasticization and molding of PLA were achieved by applying ultrasonic waves after feeding the polymer into a plasticizing chamber. Chemical and physical characteristics of processed PLA varied depending on the processing window (i.e. changes in ultrasonic wave amplitude between 14.2 and 48.1 μm and molding pressure between 0.5 in 6 bars). In terms of chemical effects, the application of ultrasound can lead to lower molecular weights (e.g. decreases of more than 45% in the weight average molecular weight), revealing partial degradation of the material. Also, the processed materials exhibited slightly higher thermal degradability than pure PLA because ultrasonic vibrations break molecular linkages and worsen the polymer structure. Finally, the processing conditions for the preparation of PLA specimens could be optimized without causing degradation and preserving structural characteristics and mechanical properties. Specifically, the use of an amplitude of 48.1 μm and a pressure of 3 bars gave samples with the same molecular weight as the raw material (i.e. 117,500 g/mol as opposed to 117,300 g/mol for Mw).

[1]  Y. Kimura,et al.  Microstructure and Thermal Properties of Polylactides with Different L- and D-Unit Sequences: Importance of the Helical Nature of the L-Sequenced Segments , 2003 .

[2]  Muthupandian Ashokkumar,et al.  Bubbles in an acoustic field: an overview. , 2007, Ultrasonics sonochemistry.

[3]  Sang-ik Lee,et al.  Localized mold heating with the aid of selective induction for injection molding of high aspect ratio micro-features , 2010 .

[4]  Christian Hopmann,et al.  Manufacturing of polymer micro parts by ultrasonic plasticization and direct injection , 2011 .

[5]  Katrin Mackenzie,et al.  Thermal decomposition of biodegradable polyesters—II. Poly(lactic acid) , 1996 .

[6]  P. Dawson,et al.  Heating and bonding mechanisms in ultrasonic welding of thermoplastics , 1983 .

[7]  W. Michaeli,et al.  New plastification concepts for micro injection moulding , 2002 .

[8]  Shaoyun Guo,et al.  Ultrasonic improvement of weld line strength of injection-molded polystyrene and polystyrene/polyethylene blend parts , 2005 .

[9]  C. Starke,et al.  Ultrasonic investigations of the thermoplastics injection moulding process , 2005 .

[10]  Ya Cao,et al.  Effects of ultrasound on the conformation and crystallization behavior of isotactic polypropylene and β-isotactic polypropylene , 2010 .

[11]  I. C. Mcneill,et al.  Degradation studies of some polyesters and polycarbonates—1. Polylactide: General features of the degradation under programmed heating conditions , 1985 .

[12]  S. L. Peshkovskii,et al.  Acoustic cavitation and its effect on flow in polymers and filled systems , 1983 .

[13]  G. Cravotto,et al.  Forcing and controlling chemical reactions with ultrasound. , 2007, Angewandte Chemie.

[14]  K. Chrissafis.  Detail kinetic analysis of the thermal decomposition of PLA with oxidized multi-walled carbon nanotubes , 2010 .

[15]  Alfonso Maffezzoli,et al.  An Overview of Progress and Current Challenges in Ultrasonic Treatment of Polymer Melts , 2013 .

[16]  G. Strobl,et al.  Temperature dependent variations in the lamellar structure of poly(l-lactide) , 2006 .

[17]  R. Ahrens,et al.  Microstructuring of multiwell plates for three-dimensional cell culture applications by ultrasonic embossing , 2012, Biomedical microdevices.

[18]  Catia Bastioli,et al.  Effect of molecular weight and crystallinity on poly(lactic acid) mechanical properties , 1996 .

[19]  D. Yao,et al.  High‐frequency proximity heating for injection molding applications , 2006 .

[20]  Shaoyun Guo,et al.  Ultrasonic improvement of rheological behavior of polystyrene , 2002 .

[21]  Keun Park,et al.  Direct patterning of micro-features on a polymer substrate using ultrasonic vibration , 2012 .

[22]  Lawrence A. Crum,et al.  Sonochemistry and Sonoluminescence , 1999 .

[23]  S. Perren,et al.  The effect of melt-processing on the degradation of selected polyhydroxyacids: polylactides, polyhydroxybutyrate, and polyhydroxybutyrate-co-valerates , 1993 .

[24]  Shaoyun Guo,et al.  The mechanism of ultrasonic improvement of weld line strength of injection molded polystyrene and polystyrene/polyethylene blend parts , 2006 .

[25]  J. Puiggalí,et al.  Thermal degradation studies of poly(trimethylene carbonate) blends with either polylactide or polycaprolactone , 2012 .

[26]  Huilin Li,et al.  Physical and chemical effects of ultrasound vibration on polymer melt in extrusion. , 2010, Ultrasonics sonochemistry.

[27]  Michel Vert,et al.  Effects of morphology, conformation and configuration on the IR and Raman spectra of various poly(lactic acid)s , 1998 .

[28]  Clarisse Ribeiro,et al.  Tailoring the morphology and crystallinity of poly(L-lactide acid) electrospun membranes. , 2011, Science and technology of advanced materials.

[29]  J. Giboz,et al.  Microinjection molding of thermoplastic polymers: a review , 2007 .

[30]  H. Zou,et al.  Thermal degradation of poly(lactic acid) measured by thermogravimetry coupled to Fourier transform infrared spectroscopy , 2009 .

[31]  Yue Cheng,et al.  Micro ultrasonic welding: joining of chemically inert polymer microparts for single material fluidic components and systems , 2006 .

[32]  Jos-Luis Capelo-Martnez,et al.  Ultrasound in Chemistry , 2008 .

[33]  A. Isayev.  Injection Molding: Technology and Fundamentals , 2009 .

[34]  Xiaozhen Yang,et al.  A Spectroscopic Analysis of Poly(lactic acid) Structure , 2001 .