Comprehensive study of microcrystalline silicon solar cells deposited at high rate using 13.56 MHz plasma-enhanced chemical vapor deposition

In this article we present a comprehensive study of microcrystalline silicon (μc-Si:H) p-i-n solar cells prepared by using plasma-enhanced chemical vapor deposition (PECVD) at 13.56 MHz excitation frequency. In the first step the cell development was performed in a small area PECVD reactor showing the relationship between the deposition process parameters and the resulting solar cell performance. Subsequent up-scaling to a substrate area of 30×30 cm2 confirmed the scalability of optimized deposition parameters to large area reactors. We investigated the deposition regime of high rf power Prf (0.25–0.7 W/cm2) and high deposition pressure pdep (1–11 Torr) for the μc-Si:H i layer. Furthermore, the influence of silane concentration and deposition temperature was studied. A transition between amorphous and microcrystalline growth could be achieved by a variation of either deposition pressure, plasma power, or silane concentration. The best microcrystalline silicon solar cells were prepared close to the transition to amorphous growth. A high deposition pressure was a prerequisite for obtaining high quality material at a high growth rate. The best solar cell efficiencies achieved so far are 8.1% and 6.6% at i-layer growth rates of 5 and 10 A/s, respectively, for μc-Si:H single junction cells. Applied in a-Si:H/μc-Si:H tandem cells a stabilized efficiency of 10.0% was achieved.In this article we present a comprehensive study of microcrystalline silicon (μc-Si:H) p-i-n solar cells prepared by using plasma-enhanced chemical vapor deposition (PECVD) at 13.56 MHz excitation frequency. In the first step the cell development was performed in a small area PECVD reactor showing the relationship between the deposition process parameters and the resulting solar cell performance. Subsequent up-scaling to a substrate area of 30×30 cm2 confirmed the scalability of optimized deposition parameters to large area reactors. We investigated the deposition regime of high rf power Prf (0.25–0.7 W/cm2) and high deposition pressure pdep (1–11 Torr) for the μc-Si:H i layer. Furthermore, the influence of silane concentration and deposition temperature was studied. A transition between amorphous and microcrystalline growth could be achieved by a variation of either deposition pressure, plasma power, or silane concentration. The best microcrystalline silicon solar cells were prepared close to the transit...

[1]  Hideki Matsumura,et al.  Formation of Silicon-Based Thin Films Prepared by Catalytic Chemical Vapor Deposition (Cat-CVD) Method , 1998 .

[2]  A. Matsuda,et al.  Substrate dependence of initial growth of microcrystalline silicon in plasma‐enhanced chemical vapor deposition , 1996 .

[3]  Y. Takeuchi,et al.  Radio-frequency plasma production using a ladder-shaped antenna , 1999 .

[4]  A. Matsuda,et al.  High Rate Deposition of Microcrystalline Silicon Using Conventional Plasma-Enhanced Chemical Vapor Deposition , 1998 .

[5]  W. V. Sark,et al.  Structural properties of a-Si:H related to ion energy distributions in VHF silane deposition plasmas , 1998 .

[6]  R. Collins,et al.  Evolutionary phase diagrams for the deposition of silicon films from hydrogen-diluted silane , 2000 .

[7]  O. Vetterl,et al.  Effects of Structural Properties of νc-Si:H Absorber Layers on Solar Cell Performance , 2000 .

[8]  W. Kulisch,et al.  Plasma properties at the transition from remote to direct plasma , 1998 .

[9]  Reinhard Carius,et al.  Optical and transport studies on thin microcrystalline silicon films prepared by very high frequency glow discharge for solar cell applications , 1997 .

[10]  J. Müller,et al.  Amorphous and microcrystalline silicon solar cells prepared at high deposition rates using RF (13.56 MHz) plasma excitation frequencies , 2001 .

[11]  A. Matsuda,et al.  High rate growth of microcrystalline silicon at low temperatures , 2000 .

[12]  A. Howling,et al.  Large Area Deposition of Amorphous and Microcrystalline Silicon by Very High Frequency Plasma , 1998 .

[13]  Bernd Rech,et al.  Intrinsic microcrystalline silicon: A new material for photovoltaics , 2000 .

[14]  F. Finger,et al.  High deposition rates for microcrystalline silicon with low temperature plasma enhanced chemical vapor deposition processes , 1998 .

[15]  M. Klick,et al.  Influence of excitation frequency on plasma parameters and etching characteristics of radio-frequency discharges , 1999 .

[16]  Diego Fischer,et al.  Microcrystalline silicon and micromorph tandem solar cells , 1999 .

[17]  J. Müller,et al.  Development of highly efficient thin film silicon solar cells on texture-etched zinc oxide-coated glass substrates , 2001 .

[18]  A. Shah,et al.  Fast Deposition of a-Si:H Layers and Solar Cells in a Large-Area (40 x40 cm2) VHF-GD Reactor , 1999 .

[19]  Kenji Yamamoto,et al.  Thin film Si solar cell fabricated at low temperature , 2000 .

[20]  H. Shirai,et al.  Spatial distribution of high-density microwave plasma for fast deposition of microcrystalline silicon film , 2001 .

[21]  Y. Takeuchi,et al.  Characteristics of Very High Frequency Plasma Produced Using a Ladder-Shaped Electrode , 1999 .

[22]  E. Taglauer,et al.  Surface hydrogen content and passivation of silicon deposited by plasma induced chemical vapor deposition from silane and the implications for the reaction mechanism , 1989 .

[23]  M. Heintze.  Versatile High Rate Plasma Deposition and Processing with very high Frequency Excitation , 1997 .