Mechanisms for Solidification Crack Initiation and Growth in Aluminum Welding

In the present work, mechanisms are proposed for solidification crack initiation and growth in aluminum alloy 6060 arc welds. Calculations for an interdendritic liquid pressure drop, made using the Rappaz–Drezet–Gremaud (RDG) model, demonstrate that cavitation as a liquid fracture mechanism is not likely to occur except at elevated levels of hydrogen content. Instead, a porosity-based crack initiation model has been developed based upon pore stability criteria, assuming that gas pores expand from pre-existing nuclei. Crack initiation is taken to occur when stable pores form within the coherent dendrite region, depending upon hydrogen content. Following initiation, crack growth is modeled using a mass balance approach, controlled by local strain rate conditions. The critical grain boundary liquid deformation rate needed for solidification crack growth has been determined for a weld made with a 16 pct 4043 filler addition, based upon the local strain rate measurement and a simplified strain rate partitioning model. Combined models show that hydrogen and strain rate control crack initiation and growth, respectively. A hypothetical hydrogen strain rate map is presented, defining conceptually the combined conditions needed for cracking and porosity.

[1]  J. C. Fisher.  The Fracture of Liquids , 1948 .

[2]  H. Heuser.  Value of Different Hot Cracking Tests for the Manufacturer of Filler Metals , 2005 .

[3]  D. R. Poirier,et al.  Permeability for flow parallel to primary dendrite arms , 1992 .

[4]  D. Eliezer,et al.  The Effects of Hydrogen on , 1991 .

[5]  A. Ohno,et al.  Solidification of Metals , 1914, Nature.

[6]  J. Beech,et al.  Origin of gas bubbles in aluminium , 1978 .

[7]  Thomas Böllinghaus,et al.  Hot Cracking Phenomena in Welds III , 2005 .

[8]  Suyitno,et al.  Hot tearing criteria evaluation for direct-chill casting of an Al-4.5 pct Cu alloy , 2005 .

[9]  J. Rutter,et al.  Experiments on the solidification structure of alloy castings , 1971 .

[10]  D. G. McCartney,et al.  Development of a New Hot-cracking Test for Aluminium Alloys , 1989 .

[11]  Christophe L. Martin,et al.  Hot tearing phenomena in Al-Cu alloys : grain refinement effect , 2000 .

[12]  Ø. Grong,et al.  Effect of scandium and titanium–boron on grain refinement and hot cracking of aluminium alloy 7108 , 1999 .

[13]  N. Coniglio,et al.  Weld Parameter and Minor Element Effects on Solidification Crack Initiation in Aluminium , 2008 .

[14]  Suyitno,et al.  Mechanical properties in the semi-solid state and hot tearing of aluminium alloys , 2004 .

[15]  D. J. Lahaie,et al.  Physical modeling of the deformation mechanisms of semisolid bodies and a mechanical criterion for hot tearing , 2001 .

[16]  A. Jacot,et al.  Last-stage solidification of alloys: Theoretical model of dendrite-arm and grain coalescence , 2003 .

[17]  L. F. Mondolfo.  Aluminum alloys: Structure and properties , 1976 .

[18]  J.C.M. Farrar,et al.  Hot Cracking Tests — The Route to International Standardization , 2005 .

[19]  D. Scott MacKenzie,et al.  Handbook of Aluminum : Vol. 1: Physical Metallurgy and Processes , 2003 .

[20]  Stan A David,et al.  Trends in Welding Research , 1986 .

[21]  C. Cross.  On the Origin of Weld Solidification Cracking , 2005 .

[22]  J. Lippold.  Recent Developments in Weldability Testing , 2005 .

[23]  N. Coniglio,et al.  Phase formation in 6060/4043 aluminum weld solidification , 2009 .

[24]  J. Drezet,et al.  A new hot-tearing criterion , 1999 .

[25]  L. Katgerman,et al.  A Quest for a New Hot Tearing Criterion , 2007 .