Fabrication of porous silicon nitride ceramics using binder jetting technology

This paper presents the results of the binder jetting technology application for the processing of the Si3N4-based ceramics. The difference of the developed technology from analogues used for additive manufacturing of silicon nitride ceramics is a method of the separate deposition of the mineral powder and binder without direct injection of suspensions/slurries. It is assumed that such approach allows reducing the technology complexity and simplifying the process of the feedstock preparation, including the simplification of the composite materials production. The binders based on methyl ester of acrylic acid with polyurethane and modified starch were studied. At this stage of the investigations, the technology of green body's fabrication is implemented using a standard HP cartridge mounted on the robotic arm. For the coordinated operation of the cartridge and robot the specially developed software was used. Obtained green bodies of silicon powder were used to produce the ceramic samples via reaction sintering. The results of study of ceramics samples microstructure and composition are presented. Sintered ceramics are characterized by fibrous α-Si3N4 structure and porosity up to 70%.

[1]  Andreas Gebhardt,et al.  Rapid prototyping , 2003 .

[2]  Fritz B. Prinz,et al.  RP of Si3N4 burner arrays via assembly mould SDM , 2004 .

[3]  Rainer Telle,et al.  Direct inkjet printing of Si3N4: Characterization of ink, green bodies and microstructure , 2008 .

[4]  Noshir A. Langrana,et al.  Microstructural Characterization and Mechanical Properties of Si3N4 Formed by Fused Deposition of Ceramics , 2008 .

[5]  V. Krstić,et al.  Silicon nitride: the engineering material of the future , 2011, Journal of Materials Science.

[6]  R. Telle,et al.  Rheological Properties of Aqueous Si3N4 and MoSi2 Suspensions Tailor-Made for Direct Inkjet Printing , 2011 .

[7]  Litong Zhang,et al.  Effect of chemical vapor infiltration of Si3N4 on the mechanical and dielectric properties of porous Si3N4 ceramic fabricated by a technique combining 3-D printing and pressureless sintering , 2012 .

[8]  Litong Zhang,et al.  Microstructure and mechanical properties of three porous Si3N4 ceramics fabricated by different techniques , 2012 .

[9]  S. Sōmiya.  Handbook of advanced ceramics : materials, applications, processing, and properties , 2013 .

[10]  Xiaowei Yin,et al.  Absorption properties of twinned SiC nanowires reinforced Si3N4 composites fabricated by 3d-prining , 2015 .

[11]  Shichao Liu,et al.  Feasibility of preparing of silicon nitride ceramics components by aqueous tape casting in combination with laminated object manufacturing , 2015 .

[12]  Jay Patel,et al.  Additive manufacturing , 2016, XRDS.