Subsequent yield conditions of metal under cyclic loading at elevated temperature

SummaryA method to predict the yield conditions of metal at elevated temperature subjected to cyclic loading is presented in this paper. The main assumption made herein is that the yield function can be expressed as the linear sum of the yield function at the preceding stage and the one associated with the plastic strain increment at the present stage. The proposed general theory was applied to the special case of Yoshimura's yield condition. Cyclic tension-torsion tests were conducted on thin-walled tubular specimens; and simultaneously, the cyclically induced ratcheting strain was examined. Good correlation was obtained between experimental and theoretical results.ÜbersichtEs wird die Möglichkeit untersucht, die Fließeigenschaften von Metallen unter hohen Temperaturen und bei zyklischer Belastung vorauszubestimmen. Wichtigste Voraussetzung ist dafür, daß die Fließfunktion als eine lineare Summe der Fließfunktion im vorhergehenden Zustand und der Fließfunktion durch die plastische Dehnungszunahme in diesem Zustand ausgedrückt werden kann. Die vorgeschlagene allgemeine Theorie wurde auf den Sonderfall der Yoshimuraschen Fließbedingungen angewandt. Es wurden an dünnwandigen Proben zyklische Spannungs-Torsions-Versuche durchgeführt. Gleichzeitig wurde eine zyklischinduzierte gerichtete Dehnung untersucht. Experimentelle und theoretische Ergebnisse stimmen gut überein.