Initial stages of plasma electrolytic oxidation of titanium

The initial stages of oxide growth on titanium are examined in a recently developed commercial alkaline pyrophosphate/aluminate electrolyte of interest for plasma electrolytic oxidation of light metal alloys. Constant current anodizing was employed, with resultant films examined by scanning and transmission electron microscopies and Rutherford backscattering spectroscopy. The initial film is relatively uniform and composed of TiO2, with low concentrations of aluminium and phosphorus species incorporated from the electrolyte. With increase in voltage the film breaks down locally, and regions of original and modified film develop simultaneously, with the latter occupying more of the surface as the voltage rises. Porous regions due to dielectric breakdown also become increasingly evident. At � 240 V, sparking commences, and the surface reveals extensive, relatively uniform porosity, with the coating now containing much enhanced concentrations of aluminium and phosphorus species compared with the coating at lower voltages. The films develop at low efficiency due to generation of oxygen. The oxygen is produced within the original film material and at sites of dielectric breakdown. The former type of film develops a two-layered morphology, with an outer layer of amorphous TiO2 and an inner layer with numerous fine and course cavities. The cavities are due to the generation of oxygen that may be associated with the formation of anatase in the inner layer. 2003 Elsevier Ltd. All rights reserved.

[1]  J. Zahavi,et al.  Electrolytic breakdown crystallization of anodic oxide films on A1, Ta and Ti , 1970 .

[2]  A. Matthews,et al.  Deposition of layered bioceramic hydroxyapatite/TiO2 coatings on titanium alloys using a hybrid technique of micro-arc oxidation and electrophoresis , 2000 .

[3]  T. P. Yarovaya,et al.  Anodic spark deposition of P, Me(II) or Me(III) containing coatings on aluminium and titanium alloys in electrolytes with polyphosphate complexes , 2001 .

[4]  Lawrence R. Doolittle,et al.  Algorithms for the rapid simulation of Rutherford backscattering spectra , 1985 .

[5]  A. Matthews,et al.  Characterisation of oxide films produced by plasma electrolytic oxidation of a Ti–6Al–4V alloy , 2000 .

[6]  A. Aladjem Anodic oxidation of titanium and its alloys , 1973 .

[7]  J. Leach,et al.  The anodic oxidation of valve metals—I. Determination of ionic transport numbers by α-spectrometry , 1986 .

[8]  A. Matthews,et al.  Plasma electrolysis for surface engineering , 1999 .

[9]  W. Xue,et al.  Microstructure and Phase Composition of Microarc Oxidation Coatings Formed on Ti–6Al–4V Alloy in Aluminate Solution , 2001 .

[10]  K. Shimizu,et al.  Influence of tungsten species on the structure of anodic titania , 1998 .

[11]  M. Textor,et al.  Characterization of anodic spark-converted titanium surfaces for biomedical applications , 1999, Journal of materials science. Materials in medicine.

[12]  J. Pringle The anodic oxidation of superimposed metallic layers: theory , 1980 .

[13]  H. G. Schneider,et al.  Application Fields of ANOF Layers and Composites , 1986 .

[14]  S. Gnedenkov,et al.  Anticorrosion, antiscale coatings obtained on the surface of titanium alloys by microarc oxidation method and used in seawater , 2000 .

[15]  S. Brown,et al.  Anodic Spark Deposition from Aqueous Solutions of NaAlO2 and Na2SiO3 , 1971 .

[16]  S. Nagata,et al.  Ionic transport in amorphous anodic titania stabilised by incorporation of silicon species , 2002 .

[17]  T. Albrektsson,et al.  Characteristics of the surface oxides on turned and electrochemically oxidized pure titanium implants up to dielectric breakdown: the oxide thickness, micropore configurations, surface roughness, crystal structure and chemical composition. , 2002, Biomaterials.