Optical, electrical and structural properties of sol gel ZnO:Al coatings

Abstract Single and multilayer transparent conducting aluminium doped zinc oxide films have been prepared on DESAG AF45 substrates by the sol gel dip coating process. Zinc acetate solutions of 0.1–0.5 M in isopropanol stabilised by diethanolamine and doped with a concentrated solution of aluminium nitrate in ethanol were used. Each layer was fired at 600°C in a conventional furnace for 15 min. The final coatings were then tempered under a flux of forming gas (N2/H2) at 400°C for 2 h. The coatings have been characterised by surface stylus profiling, optical spectroscopy (UV-NIR), X-ray diffraction (XRD), transmission electron microscopy (TEM) and combined Hall and van der Pauw techniques. Single layers with thickness, d, ranging from 25 to 186 nm are polycrystalline with the zincite structure and exhibit a small preferential orientation with the (002) direction perpendicular to the surface (texture coefficient, TC, ranging from 1.8 to 2.8). They consist of almost spherical particles with size ranging from 15 to 25 nm (thin sample) to 40 nm (thick sample) with crystallite sizes ranging from 23 to 40 nm (002), respectively. The film resistivity decreases from 5×10−1 Ω cm (d=25 nm) to 4×10−2 Ω cm (d=186 nm). Multilayer coatings built with about 20 nm thick layers are also slightly textured along the (002) direction (TC ranging from 1.9 to 2.8). A structural evolution in morphology from spherical to columnar growth was observed. The crystallite size calculated from the (002) reflex increases with the number of layers from 23 nm for a single layer to over 100 nm for ten layers. The resistivity decreases from 5×10−1 Ω cm for a single layer to 5×10−3 Ω cm for ten layers (d=174 nm). A model for the growth of the crystallites in sol gel multilayer coatings is presented.

[1]  Yasutaka Takahashi,et al.  Preparation of transparent, electrically conducting ZnO film from zinc acetate and alkoxide , 1994, Journal of Materials Science.

[2]  M. Leskelä,et al.  Ale Growth of Transparent Conductors , 1996 .

[3]  Thomas Krajewski,et al.  Comparative study of SnO2:Sb transparent conducting films produced by various coating and heat treatment techniques , 1997 .

[4]  Y. Ohya,et al.  Microstructure of TiO2 and ZnO Films Fabricated by the Sol‐Gel Method , 1996 .

[5]  K. Nakano,et al.  Dip-coating of ITO films , 1997 .

[6]  Toshinobu Yoko,et al.  Preparation of ZnO Films with Preferential Orientation by Sol-Gel Method , 1996 .

[7]  J. Müller,et al.  Conductivity model for sputtered ZnO-thin film gas sensors , 1997 .

[8]  David R. Clarke,et al.  On the optical band gap of zinc oxide , 1998 .

[9]  Richard H. Bube,et al.  Optical and electrical properties of ZnO films prepared by spray pyrolysis for solar cell applications , 1979 .

[10]  Arvind Shah,et al.  The growth of surface textured aluminum doped ZnO films for a-Si solar cells by RF magnetron sputtering at low temperature , 1996 .

[11]  G. Scherer Sintering of sol-gel films , 1997 .

[12]  D. Campi,et al.  Prediction of optical properties of amorphous tetrahedrally bonded materials , 1988 .

[13]  Hidekazu Tanaka,et al.  Preparation of crystallized zinc oxide films on amorphous glass substrates by pulsed laser deposition , 1996 .

[14]  Y. Takahashi,et al.  Photoconductivity of Ultrathin Zinc Oxide Films , 1994 .

[15]  Jonathan C. Knowles,et al.  Speciation and the nature of ZnO thin films from chemical bath deposition , 1996 .

[16]  H. Nanto,et al.  Electrical and optical properties of zinc oxide thin films prepared by rf magnetron sputtering for transparent electrode applications , 1984 .

[17]  T. Nakada,et al.  Comparison Between Al- and B-Doped Zno Window Layers For CuInSe 2 Thin Film Solar Cells , 1996 .

[18]  Vinay Gupta,et al.  Influence of postdeposition annealing on the structural and optical properties of sputtered zinc oxide film , 1996 .

[19]  D. Cameron,et al.  Aluminum-doped zinc oxide transparent conductors deposited by the sol-gel process , 1994 .

[20]  M. Bertolotti,et al.  OPTICAL PROPAGATION LOSS REDUCTION IN ZNO THIN-FILMS UNDER CO2-LASER TREATMENT , 1990 .

[21]  Toshinobu Yoko,et al.  Sol-gel preparation of ZnO films with extremely preferred orientation along (002) plane from zinc acetate solution , 1997 .

[22]  M. Rahaman Ceramic Processing and Sintering , 1995 .

[23]  B. Szyszka,et al.  Optical and electrical properties of doped zinc oxide films prepared by ac reactive magnetron sputtering , 1997 .

[24]  J. Chun,et al.  X-ray studies of SnO2 prepared by chemical vapour deposition , 1986 .