Facile fabrication of tin-doped hematite photoelectrodes – effect of doping on magnetic properties and performance for light-induced water splitting

We present a new, easily scalable method for the deposition of nanocrystalline hematite photoelectrodes based on the spin-coating of a mixed solution containing tin(II) and iron(III) chlorides followed by thermal treatment. Our facile approach does not require any additional film-forming organic species and allows simple control of the photoelectrochemical performance of the electrode by adjusting the degree of tin doping. When annealed at 650 °C a strong increase in the water oxidation photocurrent is observed with increasing tin concentration. The maximum performance (0.45 mA cm−2 at 1.43 V vs. RHE) was found at the highest possible tin loading (20 : 100, Sn : Fe). The contrasting performance of electrodes annealed at 650 °C and 800 °C suggests different activation processes for dopant diffusion and activation. The doping of tin into the crystal structure of hematite thin films is directly evidenced by X-ray photoelectron spectroscopy and indirectly by changes in the intrinsic magnetic parameters (Morin temperature, Neel temperature) of the hematite films. The magnetization measurements thus represent a potential technique to quantify doping amounts in hematite.

[1]  Piers R. F. Barnes,et al.  Enhancement of Photoelectrochemical Hydrogen Production from Hematite Thin Films by the Introduction of Ti and Si , 2007 .

[2]  J. Ardisson,et al.  119Sn Mössbauer spectroscopic study of nanometric tin dioxide powders prepared by pyrolysis of organotin oxides , 2003 .

[3]  V. Sharma,et al.  A nanocrystalline hematite film prepared from iron(III) chloride precursor , 2010 .

[4]  Anke Weidenkaff,et al.  Photoelectrochemical water splitting with mesoporous hematite prepared by a solution-based colloidal approach. , 2010, Journal of the American Chemical Society.

[5]  E. Carter,et al.  Electron transport in pure and doped hematite. , 2011, Nano letters.

[6]  Nathan T. Hahn,et al.  Photoelectrochemical Performance of Nanostructured Ti- and Sn-Doped α-Fe2O3 Photoanodes , 2010 .

[7]  B. A. Balko,et al.  The Effect of Doping with Ti(IV) and Sn(IV) on Oxygen Reduction at Hematite Electrodes , 2001 .

[8]  Michael Grätzel,et al.  Translucent thin film Fe2O3 photoanodes for efficient water splitting by sunlight: nanostructure-directing effect of Si-doping. , 2006, Journal of the American Chemical Society.

[9]  Michael Grätzel,et al.  Light-induced water splitting with hematite: improved nanostructure and iridium oxide catalysis. , 2010, Angewandte Chemie.

[10]  A. Bard,et al.  Development of a Potential Fe2O3-Based Photocatalyst Thin Film for Water Oxidation by Scanning Electrochemical Microscopy: Effects of Ag−Fe2O3 Nanocomposite and Sn Doping , 2009 .

[11]  Chuen-Guang Chao,et al.  Control ability of spin coating planarization of resist filmand optimal control of developers , 2006, Microelectron. J..

[12]  Jinhua Ye,et al.  Photoanodic properties of pulsed-laser-deposited α-Fe2O3 electrode , 2010 .

[13]  Eric W. McFarland,et al.  Pt-Doped α-Fe2O3 Thin Films Active for Photoelectrochemical Water Splitting , 2008 .

[14]  Michael Grätzel,et al.  WO3-Fe2O3 Photoanodes for Water Splitting: A Host Scaffold, Guest Absorber Approach , 2009 .

[15]  Arnold J. Forman,et al.  Electrodeposition of α-Fe2O3 Doped with Mo or Cr as Photoanodes for Photocatalytic Water Splitting , 2008 .

[16]  R. Shrivastav,et al.  Characterization of Zn-doped hematite thin films for photoelectrochemical splitting of water , 2006 .

[17]  Yichuan Ling,et al.  Facile synthesis of highly photoactive α-Fe₂O₃-based films for water oxidation. , 2011, Nano letters.

[18]  Fu-Ren F. Fan,et al.  Rapid Screening of Effective Dopants for Fe2O3 Photocatalysts with Scanning Electrochemical Microscopy and Investigation of Their Photoelectrochemical Properties , 2009 .

[19]  Michael Grätzel,et al.  Influence of Feature Size, Film Thickness, and Silicon Doping on the Performance of Nanostructured Hematite Photoanodes for Solar Water Splitting , 2009 .

[20]  J. Kennedy,et al.  Photoactivity of Polycrystalline α ‐ Fe2 O 3 Electrodes Doped with Group IVA Elements , 1981 .

[21]  V. McKee,et al.  Nanostructured α-Fe2O3 Thin Films for Photoelectrochemical Hydrogen Generation , 2009 .

[22]  Michael Grätzel,et al.  Solar water splitting: progress using hematite (α-Fe(2) O(3) ) photoelectrodes. , 2011, ChemSusChem.

[23]  Nathan T. Hahn,et al.  Reactive ballistic deposition of alpha-Fe2O3 thin films for photoelectrochemical water oxidation. , 2010, ACS nano.

[24]  Michael Grätzel,et al.  New Benchmark for Water Photooxidation by Nanostructured α-Fe2O3 Films , 2006 .

[25]  Yichuan Ling,et al.  Sn-doped hematite nanostructures for photoelectrochemical water splitting. , 2011, Nano letters.

[26]  Akira Watanabe,et al.  Photoanodic properties of sol-gel-derived Fe2O3 thin films containing dispersed gold and silver particles , 2003 .

[27]  Hisashi Shoda.  Optical Recording Materials for Compact Disc , 2008 .

[28]  Yongjing Lin,et al.  Nanonet-based hematite heteronanostructures for efficient solar water splitting. , 2011, Journal of the American Chemical Society.

[29]  G. E. Shahnazaryan,et al.  Photoelectrochemistry of tin-doped iron oxide electrodes , 2007 .

[30]  H. Kozuka,et al.  Photoelectrochemical Properties of Fe2O3−SnO2Films Prepared by Sol−Gel Method , 2011 .

[31]  L. H. Bowen,et al.  Some aspects concerning the characterization of iron oxides and hydroxides in soils and clays , 1990 .

[32]  Asif Ali Tahir,et al.  Nanostructured α-Fe2O3 Electrodes for Solar Driven Water Splitting : Effect of Doping Agents on Preparation and Performance , 2009 .

[33]  Aron Walsh,et al.  Electrodeposited Aluminum-Doped α-Fe2O3 Photoelectrodes: Experiment and Theory , 2010 .