Accelarated Publication: Evaluation of Cu-bumps with lead-free solders for flip-chip package applications
暂无分享,去创建一个
Low cost electroplated Cu-bump with environmental friendly Sn solder was developed for flip-chip applications. The seed layer used was Ti/WN"x/Ti/Cu where WN"x was used as the Cu diffusion barrier and Ti was used to enhance the adhesion between bump and the chip pad. Thick negative photoresist (THB JSR-151N) with a high aspect ratio of 2.4 was used for electroplating of copper bump and Sn solder. The Sn solder cap was reflowed at 225^o for 6min at N"2 atmosphere. No wetting phenomenon was observed for the Sn solder as evaluated by energy-dispersed spectroscopy (EDS). The Cu-bump with Ti/WN"x/Ti/Cu seed layer not only have higher shear force than the Cu-bump with Ti/Cu seed layer but also has higher resistance to fatigue failure than the Au, SnCu, SnAg bumps.
[1] K. Tu,et al. Tin–lead (SnPb) solder reaction in flip chip technology , 2001 .
[2] Soon-Min Hong,et al. Pb‐free solder bumping for flip chip package by electroplating , 2003 .
[3] H. Honma,et al. Advanced copper electroplating for application of electronics , 2003 .