Self-ordering of anodic porous alumina formed in organic acid electrolytes

New self-ordering porous alumina films were fabricated in organic acid electrolytes. Highly ordered cell arrangements of porous alumina films were realized in malonic acid at 120 V and tartaric acid at 195 V having 300 nm and 500 nm pore intervals, respectively. Self-organization was achieved at the maximum voltage required to induce high-current-density anodization while preventing burning, i.e., an extremely high-current flow concentrated at local points. The cells of the film grown at a high field must be pressed against each other, so that the self-ordering proceeds with the porous layer growth. When the self-ordering of cell arrangement proceeds, the cells became smaller. To improve the regularity of the cell configuration, a low electrolyte temperature and a relatively high electrolyte concentration were effective for maintaining a high-current-density to prevent burning. Surface flatness was an essential factor for self-ordering, however, the surface oxide film produced by electropolishing an aluminum substrate prevented quick pore growth in the organic acids having a low dissociation constant. It is confirmed that electropolishing followed by alkaline treatment was most appropriate as the pre-treatment in preparing flat surfaces.

[1]  Sachiko Ono,et al.  Self‐Ordering of Cell Arrangement of Anodic Porous Alumina Formed in Sulfuric Acid Solution , 1997 .

[2]  Takayuki Takahagi,et al.  Two-dimensional nanowire array formation on Si substrate using self-organized nanoholes of anodically oxidized aluminum , 1999 .

[3]  Kazuhiro Hane,et al.  100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask , 2001 .

[4]  Kenji Fukuda,et al.  Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic Alumina , 1995, Science.

[5]  H. Masuda,et al.  Growth of anodic porous alumina with square cells , 2003 .

[6]  K. Nishio,et al.  Fabrication of Ideally Ordered Nanohole Arrays in Anodic Porous Alumina Based on Nanoindentation Using Scanning Probe Microscope , 2002 .

[7]  T. Den,et al.  Multiwalled carbon nanotubes growth in anodic alumina nanoholes , 1999 .

[8]  N. Cabrera,et al.  Theory of the oxidation of metals , 1949 .

[9]  S. Shingubara,et al.  Formation of aluminum nanodot array by combination of nanoindentation and anodic oxidation of aluminum , 2003 .

[10]  M. Matsuo,et al.  Transfer of nanoporous pattern of anodic porous alumina into Si substrate , 2003 .

[11]  S. Shingubara,et al.  Self-Organization of a Porous Alumina Nanohole Array Using a Sulfuric/Oxalic Acid Mixture as Electrolyte , 2004 .

[12]  Sachiko Ono,et al.  Controlling Factor of Self-Ordering of Anodic Porous Alumina , 2004 .

[13]  Harry E. Ruda,et al.  Molecular-beam epitaxial growth of GaAs and InGaAs/GaAs nanodot arrays using anodic Al2O3 nanohole array template masks , 2002 .

[14]  Hideki Masuda,et al.  Self-Ordering of Cell Configuration of Anodic Porous Alumina with Large-Size Pores in Phosphoric Acid Solution , 1998 .

[15]  H. Asoh,et al.  Self-Ordering of Anodic Porous Alumina Induced by Local Current Concentration: Burning , 2004 .

[16]  A. Datta,et al.  Ordered anodic alumina nanochannels on focused-ion-beam-prepatterned aluminum surfaces , 2001 .

[17]  Toshiaki Tamamura,et al.  Highly ordered nanochannel-array architecture in anodic alumina , 1997 .

[18]  H. Betz,et al.  Die Bewegung der Ionengitter von Isolatoren bei extremen elektrischen Feldstärken , 1934 .