In-situ repair of composite sandwich structures using cyanoacrylates

Abstract A novel method for the in-situ repair of composite sandwich structures using microvascular networks and cyanoacrylate (CA) adhesive systems has been presented. Upon a damage event, the vascules become ruptured, providing a route for the introduction of adhesive directly into the damage site. The efficacy of the two repair agents was first assessed under static and fatigue conditions using a modified double cantilever beam (DCB) method. Once baseline fracture behaviour of the cyanoacrylates has been established, they were further assessed by injection into a series of pre-damaged T-joint specimens. The presence of the vasculature was shown to have no detrimental impact on mechanical performance, whilst both of the cyanoacrylates were shown to be highly effective in the recovery of stiffness and ultimate strength of the T-joint specimens.

[1]  N. Sottos,et al.  Autonomic healing of polymer composites , 2001, Nature.

[2]  P. Curtis,et al.  A smart repair system for polymer matrix composites , 2001 .

[3]  R. A. Shenoi,et al.  Influence of material and geometry variations on the behaviour of bonded tee connections in FRP ships , 1992 .

[4]  Dan Zenkert,et al.  Testing and analysis of ultra thick composites , 2010 .

[5]  Gökdeniz Neşer,et al.  Effect of T-Joint Geometry on the Performance of a GRP/PVC Sandwich System Subjected to Tension , 2009 .

[6]  Ian P Bond,et al.  Interactions between propagating cracks and bioinspired self-healing vascules embedded in glass fibre reinforced composites , 2011 .

[7]  Ian P Bond,et al.  Self‐Healing Fibre Reinforced Composites via a Bioinspired Vasculature , 2011 .

[8]  R. Morishima,et al.  Numerical analysis and experiment of composite sandwich T-joints subjected to pulling load , 2011 .

[9]  R. A. Shenoi,et al.  Fatigue failure mechanisms in fibre-reinforced plastic laminated tee joints , 1995 .

[10]  S. Donaldson,et al.  Biomimetic composite structural T-joints , 2012 .

[11]  I. Bond,et al.  Biomimetic self-healing of advanced composite structures using hollow glass fibres , 2006 .

[12]  T. O'brien.  Assessment of Composite Delamination Self-Healing Under Cyclic Loading , 2009 .

[13]  R S Trask,et al.  Characterization and analysis of carbon fibre-reinforced polymer composite laminates with embedded circular vasculature , 2010, Journal of The Royal Society Interface.

[14]  Aage Lystrup,et al.  Design and test of lightweight sandwich T-joint for naval ships , 2005 .

[15]  Adam Przekop,et al.  Design and Analysis of a Stiffened Composite Structure Repair Concept , 2011 .

[16]  R. A. Shenoi,et al.  A Study of Structural Composite Tee Joints in Small Boats , 1990 .

[17]  Damage tolerance of laminated tee joints in FRP structures , 1998 .

[18]  Stefanie Feih,et al.  Bio-inspired design of aerospace composite joints for improved damage tolerance , 2012 .

[19]  Torgeir Moan,et al.  Experimental and Numerical Study of Composite T-Joints , 1996 .

[20]  Ian P Bond,et al.  The Role Of Embedded Bioinspired Vasculature On Damage Formation In Self-Healing Carbon Fibre Reinforced Composites , 2011 .

[21]  S. Furman,et al.  Poly[ethylene-co-(methacrylic acid)] Healing Agents for Mendable Carbon Fiber Laminates , 2010 .

[22]  I. Partridge,et al.  3D reinforcement of stiffener-to-skin T-joints by Z-pinning and tufting , 2006 .

[23]  M. Wisnom,et al.  Investigation into failure of laminated composite T-piece specimens under bending loading , 2013 .

[24]  Valery N. Pilipchuk,et al.  Analysis of crack formation in T-joint structures under dynamic loading , 2011 .

[25]  A. Mouritz,et al.  Experimental determination of the structural properties and strengthening mechanisms of z-pinned composite T-joints , 2011 .

[26]  Naoki Takano,et al.  Intelligent Material Systems Using Epoxy Particles to Repair Microcracks and Delamination Damage in GFRP , 1999 .