Microwave plasma treatment of polymer surface for irreversible sealing of microfluidic devices.

Microwave plasma was generated in a glass bottle containing 2-3 Torr of oxygen for plasma treatment of a polymer surface. A "kitchen microwave oven" and a dedicated microwave digestion oven were used as the power source. Poly(dimethylsiloxane)(PDMS) slabs treated by a 30 W plasma for 30-60 s sealed irreversibly to form microfluidic devices that can sustain solution flow of an applied pressure of 42 psi without leaking. Experimental set up and conditions for the production of a homogeneous plasma to activate the PDMS surface for irreversible sealing are described in detail. The surface of a microwave plasma-treated PDMS slab was characterized using atomic force microscopy (AFM) and attenuated total reflection-Fourier Transform infrared spectroscopy (ATR-FTIR). The plasma-treated surface bears silica characteristics.

[1]  Michael Vollmer,et al.  Physics of the microwave oven , 2004 .

[2]  Jin Ho Kim,et al.  Surface modification of poly(dimethylsiloxane) microchannels , 2003, Electrophoresis.

[3]  Brent T. Ginn,et al.  Polymer Surface Modification Using Microwave-Oven-Generated Plasma , 2003 .

[4]  Bin Wang,et al.  Surface characterization using chemical force microscopy and the flow performance of modified polydimethylsiloxane for microfluidic device applications , 2003, Electrophoresis.

[5]  G. Whitesides,et al.  Components for integrated poly(dimethylsiloxane) microfluidic systems , 2002, Electrophoresis.

[6]  G. Whitesides,et al.  Poly(dimethylsiloxane) as a material for fabricating microfluidic devices. , 2002, Accounts of chemical research.

[7]  J. Hahn,et al.  Poly(dimethylsiloxane) microchip for precolumn reaction and micellar electrokinetic chromatography of biogenic amines , 2002, Electrophoresis.

[8]  N. Nguyen,et al.  Fundamentals and Applications of Microfluidics , 2002 .

[9]  Investigation of the stiffness change in, the indentation force and the hydrophobic recovery of plasma-oxidized polydimethylsiloxane surfaces by tapping mode atomic force microscopy , 2001 .

[10]  Charles R. Kurkjian,et al.  Nanoscale roughness of oxide glass surfaces , 2000 .

[11]  G. Whitesides,et al.  Fabrication of microfluidic systems in poly(dimethylsiloxane) , 2000, Electrophoresis.

[12]  G. Whitesides,et al.  Rapid Prototyping of Microfluidic Systems in Poly(dimethylsiloxane). , 1998, Analytical chemistry.

[13]  Ulf W. Gedde,et al.  Hydrophobicity Recovery of Polydimethylsiloxane after Exposure to Corona Discharges , 1998 .

[14]  George M. Whitesides,et al.  Rapid prototyping of complex structures with feature sizes larger than 20 μm , 1996 .

[15]  A. Steyn‐Ross,et al.  Standing waves in a microwave oven , 1990 .