Effect of tempering temperature on the microstructure and mechanical properties of a reactor pressure vessel steel

Abstract The microstructure and mechanical properties of reactor pressure vessel (RPV) steel were investigated after tempering at different temperatures ranging from 580 to 700 °C for 5 h. With increasing tempering temperature, the impact toughness, which is qualified by Charpy V-notch total absorbed energy, initially increases from 142 to 252 J, and then decreases to 47 J, with a maximum value at 650 °C, while the ultimate tensile strength varies in exactly the opposite direction. Comparing the microstructure and fracture surfaces of different specimens, the variations in toughness and strength with the tempering temperature were generally attributed to the softening of the bainitic ferrite, the agminated Fe 3 C carbides that resulted from decomposition of martensite/austenite (M/A) constituents, the precipitation of Mo 2 C carbides, and the newly formed M/A constituents at the grain boundaries. Finally, the correlation between the impact toughness and the volume fraction of the M/A constituents was established, and the fracture mechanisms for the different tempering conditions are explained.

[1]  K. Obrtlík,et al.  Dislocation structures in 16MND5 pressure vessel steel strained in uniaxial tension at different temperatures from −196 °C up to 25 °C , 2007 .

[2]  A. Rossoll,et al.  Determination of the Fracture Toughness of a Low Alloy Steel by the Instrumented Charpy Impact Test , 2002 .

[3]  F. Carré,et al.  Structural materials challenges for advanced reactor systems , 2009 .

[4]  Young-Roc Im,et al.  Effects of carbide precipitation on the strength and Charpy impact properties of low carbon Mn–Ni–Mo bainitic steels , 2001 .

[5]  W. C. Leslie,et al.  Tempering of steel , 1972, Steels.

[6]  S. Zinkle,et al.  Structural materials for fission & fusion energy , 2009 .

[7]  Navneet Arora,et al.  Micromechanical modelling of reactor pressure vessel steel , 2012 .

[8]  K. D. Haverkamp,et al.  Effect of heat treatment and precipitation state on toughness of heavy section Mn-Mo-Ni-steel for nuclear power plants components , 1984 .

[9]  P. Thomason,et al.  Ductile Fracture of Metals , 1990 .

[10]  A. Pineau,et al.  INTERGRANULAR FRACTURE STRESS AND PHOSPHORUS GRAIN BOUNDARY SEGREGATION OF A Mn-Ni-Mo STEEL , 1999 .

[11]  Wei Yan,et al.  Change of tensile behavior of a high-strength low-alloy steel with tempering temperature , 2009 .

[12]  B. Bai,et al.  The tempering behavior of granular structure in a Mn-series low carbon steel , 2011 .

[13]  T. Byun,et al.  Application of intercritical heat treatment to improve toughness of SA508 Cl.3 reactor pressure vessel steel , 1999 .

[14]  Kazuhiro Suzuki,et al.  Effects of Copper and Phosphorus on Temper Embrittlement of Mn–Mo–Ni Low Alloy Steel (ASTM A533–B) , 1975 .

[15]  Steven J. Zinkle,et al.  Materials Challenges in Nuclear Energy , 2013 .

[16]  D. Shetty,et al.  Fractographic observations of cleavage initiation in the ductile-brittle transition region of a reactor-pressure-vessel steel , 1983 .

[17]  H. D. Klerk,et al.  Upper-nose temper embrittlement phenomena in a Mn-Mo-Ni pressure vessel steel , 1992 .

[18]  S. Kheirandish,et al.  Affect of the tempering temperature on the microstructure and mechanical properties of dual phase steels , 2012 .

[19]  Byoungchul Hwang,et al.  Effect of carbide distribution on the fracture toughness in the transition temperature region of an SA 508 steel , 2002 .

[20]  G. E. Lucas,et al.  Embrittlement of nuclear reactor pressure vessels , 2001 .

[21]  Yanbin Sun,et al.  Critical cleavage fracture stress characterization of A508 nuclear pressure vessel steels , 2014 .

[22]  K. Obrtlík,et al.  Dislocation structures in 16MND5 pressure vessel steel strained in uniaxial tension , 2005 .

[23]  Tae Soon Kim,et al.  Low-cycle fatigue behaviors of two heats of SA508 Gr.1a low alloy steel in 310 °C air and deoxygenated water—Effects of dynamic strain aging and microstructures , 2013 .

[24]  Wei Liu,et al.  Effect of tempering temperature on the toughness of 9Cr–3W–3Co martensitic heat resistant steel , 2014 .

[25]  Sangho Kim,et al.  Correlation of the microstructure and fracture toughness of the heat-affected zones of an SA 508 steel , 2000 .

[26]  Toshiro Kobayashi,et al.  Analysis of impact properties of A533 steel for nuclear reactor pressure vessel by instrumented Charpy test , 1984 .

[27]  Rolf Sandström,et al.  Low temperature creep crack growth in low alloy reactor pressure vessel steel , 2005 .

[28]  Sangho Kim,et al.  Effects of alloying elements on fracture toughness in the transition temperature region of base metals and simulated heat-affected zones of Mn-Mo-Ni low-alloy steels , 2004 .

[29]  W. Clark,et al.  The mechanism of brittle fracture in a microalloyed steel: Part I. Inclusion-induced cleavage , 2000 .

[30]  Jialin Gu,et al.  Effect of tempering temperature and carbide free bainite on the mechanical characteristics of a high strength low alloy steel , 2004 .

[31]  Byeong-Joo Lee,et al.  Calculation of α/γ equilibria in SA508 grade 3 steels for intercritical heat treatment , 1998 .

[32]  Jacques Besson,et al.  Ductile to brittle transition of an A508 steel characterized by Charpy impact test: Part I: experimental results , 2005 .

[33]  M. Guttmann,et al.  Mechanism of upper-nose temper embrittlement in Mn–Ni–Mo A533 gr. B steel , 1981 .

[34]  Sangho Kim,et al.  Analysis of fracture toughness in the transition-temperature region of an Mn-Mo-Ni low-alloy steel , 2003 .

[35]  R. Thomson,et al.  Carbide precipitation in martensite during the early stages of tempering Cr- andMo-containing low alloy steels , 1998 .