The oxidation behavior of a nanolayered MoSi{sub 2}/SiC composite material was determined at the temperature range of 400{endash}900{degree}C in wet oxidation conditions. The samples were produced in the form of thin films using a sputtering technique from two different sources, and a rotating substrate holder, onto silicon single crystals and low carbon steel. For comparison, the oxidations of both constituents, MoSi{sub 2} and SiC, produced with the same sputtering technique, were measured separately. The microstructure of the MoSi{sub 2}/SiC samples were determined with high resolution transmission electron microscopy (HRTEM), and the composition of the sputtered samples was measured using backscattering (BS) of protons. For quantitative determination of oxidation, the nuclear reaction {sup 16}O(d,p){sup 17}O was utilized. Oxide layers were also analyzed using a secondary ion mass spectrometry (SIMS) and the appearance of the oxidized surface with a scanning electron microscopy (SEM). As expected, the SiC films had both the lowest initial oxidation and steady state oxidation rate. The results show that the oxidation behavior of the MoSi{sub 2}/SiC nanolayered composite material differs from that of both its constituents and involves a degradation mechanism of its own, resulting in the highest oxidation during the initial phase of the oxidation. A steady-statemore » oxidation rate was observed after the initial transient phase to be the highest for the metastable C40 structure of the single MoSi{sub 2} layer. The oxidation rate of the nanolayered structure was retarded by the SiC layers. No signs of pest disintegration were observed on either of the MoSi{sub 2} containing coatings during the steady-state phase of the oxidation at 500{degree}C up to 40 h. Our results show that the oxidation of nanolayered structures can be only in part explained by the oxidation behavior of the constituents and that during the steady-state oxidation of the nanolayered structure the oxidation rate is largely determined by the constituent with the lowest oxidation rate and by the layered structure. {copyright} {ital 1998 Materials Research Society.}« less
[1]
M. Nastasi,et al.
Structure and mechanical properties of MoSi2-Sic nanolayer composites
,
1995
.
[2]
S. Nutt,et al.
Reactive synthesis and characterization of using low-pressure plasma deposition and 100% methane
,
1995
.
[3]
Z. A. Munir,et al.
Field-assisted combustion synthesis of MoSi2-SiC composites
,
1994
.
[4]
T. Nieh,et al.
Pest disintegration of thin MoSi2 films by oxidation at 500° C
,
1994
.
[5]
R. Abbaschian,et al.
Toughening MoSi2 with niobium metal-effects of size and orientation of ductile laminae
,
1994
.
[6]
E. Lavernia,et al.
Creep behavior of plasma-sprayed SiC-reinforced MoSi2
,
1993
.
[7]
T. Nieh,et al.
Kinetics of MoSi_2 pest during low-temperature oxidation
,
1993
.
[8]
N. Stoloff,et al.
Preparation of composites from elemental powders by reactive co-synthesis
,
1993
.
[9]
R. Raj,et al.
Superplastic flow in a non-stoichiometric ceramic: Magnesium aluminate spinel
,
1993
.
[10]
E. Lavernia,et al.
Low-pressure plasma deposition of SiC-reinforced MoSi2
,
1993
.
[11]
Don M. Parkin,et al.
Mechanical Properties and Deformation Behavior of Materials Having Ultra-Fine Microstructures
,
1993
.
[12]
T. Nieh,et al.
Mechanism of MoSi_2 pest during low temperature oxidation
,
1993
.
[13]
E. Lee,et al.
Oxidation of MoSi2-based composites
,
1992
.
[14]
A. Vasudévan,et al.
A comparative overview of molybdenum disilicide composites
,
1992
.
[15]
R. M. Aikin.
On the ductile-to-brittle transition temperature in MoSi2
,
1992
.
[16]
J. L. Brimhall,et al.
Synthesis of a composite in situ using a solid state displacement reaction between Mo2C and Si
,
1992
.
[17]
A. Rollett,et al.
Toughness of dense MoSi2 and composites produced by low pressure plasma deposition
,
1992
.
[18]
T. Hirano,et al.
High temperature deformation of MoSi2 single crystals with the C11b structure
,
1990
.