Thermal Stability Characterization of the Au–Sn Bonding for High-Temperature Applications

There is a need for electromechanical devices capable of operating in high-temperature environments (>200°C) for a wide variety of applications. Today's wide-bandgap semiconductor-based power electronics have demonstrated a potential of operating above 400°C, however, they are still limited by packaging. Among the most promising alternatives is the Au-Sn eutectic solder, which has been widely used due to its excellent mechanical and thermal properties. However, the operating temperature of this metallurgical system is still limited to ~250°C owing to its melting temperature of 280°C. Therefore, a high-temperature-resistant system is much needed, but without affecting the current processing temperature of ~325°C, typically exhibited in most high-temperature Pb-free solders. In this paper, we present the development and characterization of a fluxless die-attach soldering process based on gold-enriched solid-liquid interdiffusion (SLID). A low-melting-point material (eutectic Au-Sn) is deposited in the face of a substrate, whereas a high-melting-point material, gold in this instance, is deposited in its mating substrate. Deposition of all materials was performed using a jet vapor deposition (JVD) equipment where thicknesses are controlled to achieve specific compositions in the mixture. Sandwiched coupons are isothermally processed in a vacuum reflow furnace for different reflow times. Post-processed samples confirm the interdiffusion mechanism as evidenced by the formation of sound joints that prove to be thermally stable up to ~490°C after the completion of the SLID process. Differential scanning calorimetry demonstrate the progression of the SLID process by quantifying the remaining low-melting-point constituent as a function of time and temperature, this serving as an indicator of the completion of the soldering process. Mechanical testing reveals a joint with shear strength varying from 39 to 45.5 MPa, demonstrating to be stable even after 500 h of isothermal aging. Moreover, these investigations successfully demonstrate the use of the Au-Sn SLID system and the JVD technology as potential manufacturing processes and as a lead-free die-attach technology.

[1]  R.W. Johnson,et al.  The changing automotive environment: high-temperature electronics , 2004, IEEE Transactions on Electronics Packaging Manufacturing.

[2]  W. Gasior,et al.  Enthalpy of formation of Au–Sn intermetallic phases. Part II , 2011 .

[3]  R. Wayne Johnson,et al.  Die Attach for High Temperature Electronics Packaging , 2008 .

[4]  W. Gasior,et al.  Enthalpy of formation of intermetallic phases from the Au-Sn system , 2010 .

[5]  Chin C. Lee,et al.  High temperature silver-indium joints manufactured at low temperature , 2000 .

[6]  D. Ibitayo,et al.  Microstructural Evolution and Thermal Stability Characterization of a High Temperature Die Attach Lead-Free System , 2012 .

[7]  Welch,et al.  Vacuum and Hermetic Packaging of MEMS using Solder , 2008 .

[8]  Yi Liu,et al.  Power Device Packaging Technologies for Extreme Environments , 2007, IEEE Transactions on Electronics Packaging Manufacturing.

[9]  H. Fujita,et al.  Uniaxial tensile and shear deformation tests of gold–tin eutectic solder film , 2007 .

[10]  Chin C. Lee,et al.  Au-In bonding below the eutectic temperature , 1993 .

[11]  Chin C. Lee,et al.  AuSn alloy phase diagram and properties related to its use as a bonding medium , 1993 .

[12]  Seung-Boo Jung,et al.  Microstructural evolution of Sn-rich Au–Sn/Ni flip-chip solder joints under high temperature storage testing conditions , 2007 .

[13]  Pedro O. Quintero,et al.  Silver-Indium Transient Liquid Phase Sintering for High Temperature Die Attachment , 2009 .

[14]  S. Jung,et al.  Reliability evaluation of Au–20Sn flip chip solder bump fabricated by sequential electroplating method with Sn and Au , 2008 .

[15]  S. Corbin,et al.  Quantifying metallurgical interactions in solid/liquid diffusion couples using differential scanning calorimetry , 2005 .

[16]  S. Cain,et al.  Experimental study of the kinetics of transient liquid phase solidification reaction in electroplated gold-tin layers on copper , 1997 .

[17]  Y.C. Lee,et al.  Soldering technology for optoelectronic packaging , 1996, 1996 Proceedings 46th Electronic Components and Technology Conference.

[18]  K. Aasmundtveit,et al.  Au-Sn fluxless SLID bonding: Effect of bonding temperature for stability at high temperature, above 400 °C , 2010, 3rd Electronics System Integration Technology Conference ESTC.

[19]  F. P. McCluskey,et al.  Temperature Cycling Reliability of High-Temperature Lead-Free Die-Attach Technologies , 2011, IEEE Transactions on Device and Materials Reliability.

[20]  T. B. Massalski,et al.  A study of the transient liquid phase bonding process applied to a Ag/Cu/Ag sandwich joint , 1988 .

[21]  O. Løvvik,et al.  Au-Sn SLID Bonding—Properties and Possibilities , 2012, Metallurgical and Materials Transactions B.

[22]  T. Eagar,et al.  Transient Liquid Phase Bonding , 1992 .

[23]  L. Frey,et al.  Evolution of shear strength and microstructure of die bonding technologies for high temperature applications during thermal aging , 2010, 2010 12th Electronics Packaging Technology Conference.

[24]  C.C. Lee,et al.  High temperature Cu-Sn joints manufactured by a 250/spl deg/C fluxless bonding process , 1995, Proceedings of 1995 IEEE Multi-Chip Module Conference (MCMC-95).

[25]  D. Ivey,et al.  Microstructural study of co-electroplated Au/Sn alloys , 2001 .