Synthesis and properties of poly(butylene succinate): Efficiency of different transesterification catalysts

The efficiency of organometal- (Ti, Zr, Sn, Hf, and Bi) and metal oxide- (Ge and Sb) based catalysts was investigated during the transesterification step of the synthesis of poly(butylene succinate) (PBS). PBS was prepared from succinic acid and 1,4-butanediol via a two-stage melt polycondensation process. The catalytic efficiency of the organometal catalysts was as follows: Ti≫Zr∼ Sn>Hf>Sb>Bi. The germanium and antimony metal oxides displayed desirable catalytic efficiency when were associated with hydroxy acids (lactic acid or glycolic acid), which acted as chelating agents. However, this catalytic system exhibited lower efficiency compared to the titanium system. Furthermore, at high concentrations of hydroxy acids the overall transesterification rate decreased. This effect can be explained by the substitution of PBS hydroxyl end groups by a lactic or glycolic unit, both of which are less reactive during the transesterification reaction. The role of catalytic residues during the storage and processing of PBS was also studied. The reduced viscosity of the PBS samples did not vary when processing at 190 °C from 1 to 10 minutes. However, when stored under ambient conditions, all PBS samples were prone to significant hydrolytic degradation, especially those containing a titanium catalyst. This behavior indicates that zirconium- and germanium-based catalysts could be interesting substitutes for titanium-based catalysts. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011.

[1]  K. Mukai,et al.  Structural Effects upon Enzymatic Hydrolysis of Poly(butylene succinate-co-ethylene succinate)s , 1997 .

[2]  V. Bakhmutov,et al.  Investigation of the formation of poly(ethylene terephthalate) with model molecules: kinetics and mechanisms of the catalytic esterification and alcoholysis reactions. II: Catalysis by metallic derivatives (monofunctional reactants) , 1988 .

[3]  K. Reichert,et al.  Screening of Different Titanium (IV) Catalysts in the Synthesis of Poly(ethylene terephthalate) , 2008 .

[4]  Dong Kook Kim,et al.  Effect of isocyanate‐modified fumed silica on the properties of poly(butylene succinate) nanocomposites , 2008 .

[5]  K. Reichert,et al.  Kinetic Studies of Polyethylene Terephthalate Synthesis with Titanium-Based Catalyst , 2007 .

[6]  W. Macdonald.  New advances in poly(ethylene terephthalate) polymerization and degradation , 2002 .

[7]  T. Hirabayashi,et al.  Environmentally Benign Polyester Synthesis by Room Temperature Direct Polycondensation of Dicarboxylic Acid and Diol , 2005 .

[8]  M. Ueda,et al.  Convenient synthesis of aliphatic polyesters by distannoxane-catalyzed polycondensation. , 2001, Biomacromolecules.

[9]  M. Lahcini,et al.  Aliphatic Polyesters by Bismuth Triflate-Catalyzed Polycondensations of Dicarboxylic Acids and Aliphatic Diols , 2008 .

[10]  Chandrashekhar V. Rode,et al.  Tailoring of activity and selectivity using bimetallic catalyst in hydrogenation of succinic acid , 2002 .

[11]  Catherine Pinel,et al.  Aqueous-Phase Hydrogenation of Biomass-Based Succinic Acid to 1,4-Butanediol Over Supported Bimetallic Catalysts , 2010 .

[12]  Wantai Yang,et al.  Synthesis of aliphatic polyesters by a chain‐extending reaction with octamethylcyclotetrasilazane and hexaphenylcyclotrisilazane as chain extenders , 2004 .

[13]  H. Kim,et al.  Enhanced hydrolysis resistance of biodegradable polymers and bio-composites , 2008 .

[14]  D. Bikiaris,et al.  Synthesis and comparative biodegradability studies of three poly(alkylene succinate)s , 2006 .

[15]  T. Hirabayashi,et al.  Room-Temperature Polycondensation of Dicarboxylic Acids and Diols Catalyzed by Water-Stable Lewis Acids , 2005 .

[16]  Yang-Kyoo Han,et al.  Preparation and characterization of high molecular weight poly(butylene succinate) , 2002 .

[17]  J. Chung.  Acid-base and catalytic properties of metal compounds in the preparation of poly(ethylene terephthalate) , 1990 .

[18]  K. Masenelli-Varlot,et al.  End-group modification of poly(2,6-dimethyl-1,4-phenylene ether) and in situ synthesis of poly(2,6-dimethyl-1,4-phenylene ether)-b-Poly(ethylene terephthalate) block copolymer , 2008 .

[19]  Changyin Zhu,et al.  Synthesis and biodegradation of aliphatic polyesters from dicarboxylic acids and diols , 2003 .

[20]  A. Fradet,et al.  Models for Polyesterification Kinetics. III. Preliminary Studies on the Catalysis by Titanium(IV) Tetraalkoxides , 1982 .

[21]  Wangliang Yang,et al.  Chain extension of polybutylene adipate and polybutylene succinate with adipoyl- and terephthaloyl-biscaprolactamate , 2007 .

[22]  Y. Inai,et al.  Synthesis of Aliphatic Polyesters by Direct Polyesterification of Dicarboxylic Acids with Diols under Mild Conditions Catalyzed by Reusable Rare-Earth Triflate , 2003 .

[23]  Xiaoyun Liu,et al.  A study on biodegradable aliphatic poly(tetramethylene succinate): the catalyst dependences of polyester syntheses and their thermal stabilities , 2003 .

[24]  H. Kricheldorf,et al.  Syntheses of Polyesters from Succinic Anhydride and Various Diols Catalyzed by Metal Triflates , 2009 .

[25]  H. Kricheldorf,et al.  Telechelic polyesters of ethane diol and adipic or sebacic acid by means of bismuth carboxylates as non-toxic catalysts , 2005 .

[26]  H. Tanaka,et al.  Microbial degradation of an aliphatic polyester with a high melting point, poly(tetramethylene succinate) , 1995, Applied and environmental microbiology.

[27]  D. Bikiaris,et al.  Synthesis of poly(alkylene succinate) biodegradable polyesters. Part II: Mathematical modelling of the polycondensation reaction , 2008 .

[28]  D. Achilias,et al.  Synthesis of poly(alkylene succinate) biodegradable polyesters I. Mathematical modelling of the esterification reaction , 2006 .