Diffusion bonding of Ti and Ti-Al (Ti-10, 20 and 40 mol%Al) alloys to high carbon steel was carried out at 1073 and 1273 K for 3.6 ks in a vacuum. It has been found that the joint with Ti-20 mol%Al alloy is separated in the vicinity of the interface promptly after the bonding treatment at 1273 K. Such a phenomenon could not be observed in other Ti-Al alloy/steel joints, and the Ti-20 mol%Al alloy/steel joint bonded at 1073 K showed a high strength of about 170 MPa. Therefore, this phenomenon depends on the bonding temperature and the composition of the Ti-Al alloys. From the observation results of the interface, it is thought that the diffusion of constituent elements across the interface is part of the reason for the separation phenomenon. The separated surface of the Ti-20 mol%Al alloy side showed diffraction peaks of TiC phase by XRD. Its Vickers hardness was about 1200 and approximately 4 times higher than that before the bonding treatment. It is expected that the separation phenomenon at the Ti-20 mol%Al alloy/steel interface serves surface modification of titanium materials, which show poor wear resistance.
[1]
Kyuhong Lee,et al.
Improvement of high-temperature hardness of (TiC, TiB)/Ti–6Al–4V surface composites fabricated by high-energy electron-beam irradiation
,
2004
.
[2]
A. Chiba,et al.
Diffusion bonding of TiAl alloy to eutectoid steel and its interfacial self-destruction behavior
,
2004
.
[3]
A. Chiba,et al.
Effect of Zr and Ta Inserts on Bonding Strength and Interfacial Microstructures of Ti/Steel Clads
,
2002
.
[4]
N. Richards,et al.
Electron beam welding of a Ti–45Al–2Nb–2Mn+0.8 vol.% TiB2 XD alloy
,
1997
.
[5]
Tetsuya Shimizu,et al.
Joining of TiAl and steels by induction brazing
,
1997
.
[6]
M. Koçak,et al.
The fracture behavior of diffusion-bonded duplex gamma TiAl
,
1996
.
[7]
篠崎 賢二,et al.
金属間化合物γ-TiAlの拡散接合性と継手強度 : TiAlの拡散接合に関する研究(第1報)
,
1993
.
[8]
K. Ikeuchi,et al.
Effect of Carbon Content on the Diffusion Bonding of Iron and Steel to Titanium
,
1987
.