Facile hydrophobicity/hydrophilicity modification of SMP surface based on metal constrained cracking

This study demonstrates an easy way to change surface characteristics, the water contact angle on styrene based shape memory polymer (SMP) surface alters before and after cracking formation and recovery. The contact angle of water on the original SMP surface is about 85 degree, after coating with Al and then kneading from side face at glass transition temperature Tg, cracking appeared both on Al film and SMP; cooling down and removing the Al film, cracks remain on SMP surface while the contact angle reduced to about 25 degree. When reheated above Tg, the cracks disappeared, and the contact angle go back to about 85 degree. The thin Al film bonded on SMP surface was coated by spurting, that constrains the deformation of SMP. Heating above Tg, there are complex interactions between soft SMP and hard metal film under kneading. The thin metal film cracked first with the considerable deformation of soft polymer, whereafter, the polymer was ripped by the metal cracks thus polymer cracked as well. Cracks on SMP can be fixed cooling down Tg, while reheated, cracks shrinking and the SMP recovers to its original smooth surface. Surface topography changed dramatically while chemical composition showed no change during the deformation and recovery cycle, as presented by SEM and EDS. Furthermore, the wetting cycle is repeatable. This facile method can be easily extended to the hydropobicity/hydrophilicity modification of other stimuli-responsive polymers and put forward many potential applications, such as microfluidic switching and molecule capture and release.

[1]  Angeliki Tserepi,et al.  "Smart" polymeric microfluidics fabricated by plasma processing: controlled wetting, capillary filling and hydrophobic valving. , 2010, Lab on a chip.

[2]  R. Adams,et al.  A Rapid Method of Measuring the Glass Transition Temperature Using a Novel Dynamic Mechanical Analysis Method , 2013 .

[3]  Yanju Liu,et al.  Shape-memory polymers and their composites: Stimulus methods and applications , 2011 .

[4]  Ryan R. Kohlmeyer,et al.  Remote, local, and chemical programming of healable multishape memory polymer nanocomposites. , 2012, Nano letters.

[5]  Holger Becker,et al.  Polymer microfabrication technologies for microfluidic systems , 2008, Analytical and bioanalytical chemistry.

[6]  Denis P. Dowling,et al.  Effect of Surface Wettability and Topography on the Adhesion of Osteosarcoma Cells on Plasma-modified Polystyrene , 2011, Journal of biomaterials applications.

[7]  V. Ashby,et al.  It is the outside that counts: chemical and physical control of dynamic surfaces. , 2013, Journal of the American Chemical Society.

[8]  R. Full,et al.  Adhesive force of a single gecko foot-hair , 2000, Nature.

[9]  Xin Lan,et al.  Study on the activation of styrene-based shape memory polymer by medium-infrared laser light , 2010 .

[10]  T. Xie.  Recent advances in polymer shape memory , 2011 .

[11]  G. López,et al.  The Influence of Surface Wettability on the Adhesion Strength of Settled Spores of the Green Alga Enteromorpha and the Diatom Amphora1 , 2002, Integrative and comparative biology.

[12]  Il-Joo Cho,et al.  Effect of topography on the wetting of nanoscale patterns: experimental and modeling studies. , 2014, Nanoscale.

[13]  F. Rossi,et al.  Plasma-based processes for surface wettability modification. , 2006, Langmuir : the ACS journal of surfaces and colloids.

[14]  Yanju Liu,et al.  Shape memory polymers and their composites in aerospace applications: a review , 2014 .

[15]  A. Chakraborty,et al.  Generation of sidewall patterns in microchannels via strain-recovery deformations of polystyrene , 2012 .

[16]  A. Lendlein,et al.  Multifunctional Shape‐Memory Polymers , 2010, Advanced materials.

[17]  C. Fotakis,et al.  Tuning cell adhesion by controlling the roughness and wettability of 3D micro/nano silicon structures. , 2010, Acta biomaterialia.

[18]  S. Garimella,et al.  Electrical Actuation-Induced Droplet Transport on Smooth and Superhydrophobic Surfaces , 2010 .

[19]  Kyriakos Porfyrakis,et al.  How Surface Topography Relates to Materials' Properties , 2002, Science.

[20]  I. Karapanagiotis,et al.  Modification of the wettability of polymer surfaces using nanoparticles , 2014 .

[21]  A. Chakraborty,et al.  Fabrication of Super-Hydrophobic Microchannels via Strain-Recovery Deformations of Polystyrene and Oxygen Reactive Ion Etch , 2013, Materials.

[22]  Jaroslaw Drelich,et al.  Hydrophilic and superhydrophilic surfaces and materials , 2011 .