Experimental study on the panel size effects of the low velocity impact (LVI) and compression after impact (CAI) of laminated composites, part II: CAI

[1]  A. Waas,et al.  Low velocity impact and compressive response after impact of thin carbon fiber composite panels , 2022, International Journal of Solids and Structures.

[2]  A. Waas,et al.  Experimental Analysis of Low Velocity Impact on Carbon Fiber Reinforced Polymer (CFRP) Composite Panels , 2022, AIAA SCITECH 2022 Forum.

[3]  Lokman Gemi,et al.  Experimental Investigation of the Effect of Diameter upon Low Velocity Impact Response of Glass Fiber Reinforced Composite Pipes , 2021 .

[4]  A. Waas,et al.  The effect of stacking sequence on the LVI damage of laminated composites; experiments and analysis , 2021 .

[5]  A. Waas,et al.  An Experimental and Computational Study on the Low Velocity Impact-Induced Damage of a Highly Anisotropic Laminated Composite Panel , 2021 .

[6]  Anthony M. Waas,et al.  Accelerating computational analyses of low velocity impact and compression after impact of laminated composite materials , 2021 .

[7]  Mark Pankow,et al.  Validation of an efficient finite element analysis approach for simulation of low velocity impact and compression strength after impact response , 2021 .

[8]  A. Waas,et al.  Predicting the low velocity impact damage of a quasi-isotropic laminate using EST , 2020 .

[9]  C. Rose,et al.  Progressive Damage Analysis of Post-buckled Stiffened Panels under Static Compressive Loading , 2020 .

[10]  Nam Phan,et al.  Assessment of damage tolerance approaches for composite aircraft with focus on barely visible impact damage , 2019, Composite Structures.

[11]  A. Wagih,et al.  Scaling effects of composite laminates under out-of-plane loading , 2019, Composites Part A: Applied Science and Manufacturing.

[12]  A. Waas,et al.  Low-velocity impact predictions of composite laminates using a continuum shell based modeling approach Part b: BVID impact and compression after impact , 2018, International Journal of Solids and Structures.

[13]  Wei Sun,et al.  Experiment investigation on impact damage and influences on compression behaviors of single T-stiffened composite panels , 2018, Composite Structures.

[14]  I. García-Moreno,et al.  Experimental study of the influence of thickness and ply-stacking sequence on the compression after impact strength of carbon fibre reinforced epoxy laminates , 2018 .

[15]  Jason E. Action,et al.  ICME Approach to Compression Strength after Impact Modeling , 2018 .

[16]  S. Hallett,et al.  Failure mechanisms and damage evolution of laminated composites under compression after impact (CAI): Experimental and numerical study , 2018 .

[17]  X. Tan,et al.  Effect of fatigue loading on impact damage and buckling/post-buckling behaviors of stiffened composite panels under axial compression , 2017 .

[18]  Z. Guan,et al.  An experimental and numerical study on scaling effects in the low velocity impact response of CFRP laminates , 2016 .

[19]  M. Remacha,et al.  A new device for determining the compression after impact strength in thin laminates , 2015 .

[20]  I. Sinclair,et al.  Observations of damage development from compression-after-impact experiments using ex situ micro-focus computed tomography , 2014 .

[21]  J. Barrau,et al.  Experimental analysis of CFRP laminates subjected to compression after impact: The role of impact-induced cracks in failure , 2014 .

[22]  Zhongyi Zhang,et al.  Low-velocity impact response of non-woven hemp fibre reinforced unsaturated polyester composites: Influence of impactor geometry and impact velocity , 2012 .

[23]  Giangiacomo Minak,et al.  Low velocity impact and compression after impact tests on thin carbon/epoxy laminates , 2011 .

[24]  Hao Yan,et al.  Compression-after-impact response of woven fiber-reinforced composites , 2010 .

[25]  G. Minak,et al.  Influence of diameter and boundary conditions on low velocity impact response of CFRP circular laminated plates , 2008 .

[26]  Wesley J. Cantwell,et al.  Scaling Effects in the Low Velocity Impact Response of Fiber-Metal Laminates , 2008 .

[27]  Wesley J. Cantwell,et al.  Geometrical effects in the low velocity impact response of GFRP , 2007 .

[28]  S. Sánchez-Sáez,et al.  Compression after impact of thin composite laminates , 2005 .

[29]  Luis Reis,et al.  Failure mechanisms on composite specimens subjected to compression after impact , 1998 .

[30]  G.A.O. Davies,et al.  Impactor mass and specimen geometry effects in low velocity impact of laminated composites , 1992 .