Experimental and numerical studies on dynamic crack growth in layered slate rock under wedge impact loads: part II – non-plane strain problem

Dynamic crack propagation in non-plane strain (or 3D) slate blocks under wedge impact loads was investigated numerically in this part of the paper. A parabolic-shaped crack trajectory was taken into consideration to model the crack propagation in slate blocks for analyzing the impact splitting of layered slate rock. Major and minor axes of the parabola were determined from the condition of equal mode I stress intensity factors (SIFs) along the crack front. Mode I SIFs were determined for experimental breaking loads for each increment of crack growth in a manner similar to that mentioned in part I of this paper. These values were compared with the plane strain material fracture toughness value obtained from experimental studies and very good agreement was obtained between them, for the case of actual load applied on the specimen. Numerical analysis of a field problem, i.e., separation of a large-sized slate slab from the rock strata in a slate quarry using wedge impacting, was also carried out in this paper. It can be observed that a large magnitude of load is required to break large-sized slate blocks; but this load is applied through a number of smaller load-capacity actuators-in-parallel, requiring large power capacity for the hydraulic pumps. However, this required power could be reduced considerably if the load applied on the line of hydraulic actuators is cascaded across the (line of) actuators (starting from centrally placed actuators) with a small time delay (equal to the initial crushing time in slate rock).

[1]  Georg Grathwohl,et al.  Ermüdung von Keramik unter Schwingbeanspruchung , 1988 .

[2]  Mariano Perez-Amor,et al.  Cutting of slate tiles by CO2 laser , 2002 .

[3]  Mark S. Shephard,et al.  Automatic crack propagation tracking , 1985 .

[4]  Xian‐Fang Li,et al.  Effects of electric field on crack growth for a penny-shaped dielectric crack in a piezoelectric layer , 2004 .

[5]  K. S. Aleksandrov,et al.  Anisotropy of elastic properties of rocks , 1969 .

[6]  Huajian Gao,et al.  Ab initio dynamics of rapid fracture , 1998 .

[7]  A. J. Bush,et al.  Experimentally determined stress-intensity factors for single-edge-crack round bars loaded in bending , 1978 .

[8]  Y. Nishimatsu,et al.  The mechanics of rock cutting , 1972 .

[9]  Krueger Ronald,et al.  A Shell/3D Modeling Technique for Delaminations in Composite Laminates , 1999 .

[10]  B. Whittaker,et al.  Rock cutting by impact action , 1973 .

[11]  Md. Rabiul Alam Experimental and numerical investigations of impact splitting of naturally bedded layered slate rock , 2005 .

[12]  B. Barr,et al.  Fracture toughness tests for concrete , 1977 .

[13]  Paul A. Wawrzynek,et al.  Automated 3‐D crack growth simulation , 2000 .

[14]  J. F. Knott,et al.  FATIGUE CRACK GROWTH FROM SMALL SEMI‐ELLIPTIC HYDROGEN‐INDUCED CRACKS IN QIN STEEL , 1989 .

[15]  Donald R. Peacor,et al.  Chlorite-illite/muscovite interlayered and interstratified crystals: A TEM/STEM study , 1984 .

[16]  H. P. Rossmanith,et al.  SIMULATION OF CRACKING IN LARGE ARCH DAM: PART I , 1989 .

[17]  A. J. Bush,et al.  Experimentally determined stress-intensity factors for single-edge-crack round bars loaded in bending , 1976 .

[18]  R. Knipe,et al.  Microstructure and cleavage development in selected slates , 1978 .

[19]  David J. Green,et al.  Indentation Crack‐Shape Evolution during Subcritical Crack Growth , 1995 .

[20]  B. Gross,et al.  Side-Cracked Plates Subject to Combined Direct and Bending Forces , 1975 .

[21]  Shankar Mall,et al.  Use of an eight-node element for fast fracture problems , 1980 .

[22]  S. H. White,et al.  A microstructural and microchemical study of cleavage lamellae in a slate , 1981 .