COMPARAISON DES RESULTATS D'ESSAIS DE RUPTURE SOUS CONTRAINTE EN MILIEU SALIN ET DANS L'HYDROGENE GAZEUX DE QUELQUES ACIERS A CARACTERISTIQUES MECANIQUES ELEVEES

LES AUTEURS COMPARENT LES RESULTATS D'ESSAIS DE RUPTURE EFFECTUES AVEC 4 ACIERS A CARACTERISTIQUES MECANIQUES ELEVEES (RE SUPERIEURE OU EGALE A 1200 N/MM2) PLACES SOUS CONTRAINTE, SOIT DANS L'HYDROGENE GAZEUX SOUS 1 ATMOSPHERE, SOIT DANS UNE SOLUTION SALINE 0,6 M NACL. IL S'AGIT D'ACIERS AU NI-CR-MO (35 NCD 16), AU SI (61 S 7), AU CR-MO (45 CD 4) ET AU SI-CR-MO ( 45 SCD 6). LES ESSAIS SONT REALISES AVEC DES EPROUVETTES ENTAILLEES DE MECANIQUE DE LA RUPTURE DE TYPE CT. ILS MONTRENT QUE : -LES SEUILS DE NON-PROPAGATION DES FISSURES SONT SENSIBLEMENT PLUS ELEVES DANS L'HYDROGENE GAZEUX (1 ATM) QUE DANS LA SOLUTION SALINE ; -SI L'ON CONSIDERE LA VALEUR DU SEUIL DE NON-PROPAGATION DES FISSURES COMME CRITERE DE RESISTANCE A LA RUPTURE DUE A L'HYDROGENE, L'ORDRE DE MERITE OBTENU POUR LES 4 ACIERS ETUDIES EST LE MEME, QUE L'ON EFFECTUE LES ESSAIS DANS LE MILIEU AQUEUX OU GAZEUX ; -LA DUREE DE VIE DES EPROUVETTES, TOUTES AUTRES CONDITIONS EGALES PAR AILLEURS, EST ENVIRON 10 FOIS PLUS COURTE DANS H2 QUE DANS LA SOLUTION 0,6 M NACL ; -LES FACIES DE RUPTURE NE SONT PAS TOUT-A-FAIT LES MEMES DANS LES DEUX MILIEUX : EN PLUS DES ZONES DE DECOHESION INTER-GRANULAIRE, ON TROUVE POUR LES ECHANTILLONS ROMPUS DANS L'HYDROGENE DE NOMBREUSES ZONES DE QUASI-CLIVAGE ET DE NOMBREUSES ASPERITES AUX JOINTS DE GRAINS (A).