Fabrication of aspheric surface using ultraprecision cutting and BMG molding

Abstract A new process to replicate an aspheric lens is presented in this study. A mold of oxygen free copper (OFC) is fabricated using ultraprecision machining, which is a popular material for machining due to its good machinability. But OFC has a very low hardness of 1.606 GPa, it is not suitable for the subsequent molding process. Then, this OFC mold (known as the first mold) is used to hot emboss on Mg 58 Cu 31 Y 11 amorphous alloy to form a secondary mold which is one kind of metallic glass. The hardness of the secondary mold is as high as 3.445 GPa, whereas the glass transition temperature ( T g ) of the Mg 58 Cu 31 Y 11 metallic glass is as low as 413 K (140 °C), at which the Mg 58 Cu 31 Y 11 metallic glass shows a good glass-forming ability (GFA). In order to perform superplastic microforming, the working temperature must be close to the glass temperature around 413 K. Therefore, in this study, the temperatures of the hot embossing experiments to fabricate the secondary mold are set at 423 K (150 °C). It shows experimentally that the working temperature is dependent on the applied stress level. Since the Mg 58 Cu 31 Y 11 metallic glass has superplastic property at the supercooled liquid region, it can be easily formed by the master die. This embossing process on the Mg 58 Cu 31 Y 11 metallic glass makes molding process faster and more diverse applications. Next, the secondary mold is used to emboss on polymethylmethacrylate (PMMA) sheets for replication process. The Mg 58 Cu 31 Y 11 metallic glass is not only a good material for hot embossing process to fabricate micro-structure directly, but also an excellent fast-molding material for hot embossing process. It is expected that the machining processes described in this paper could be applied to the related fields to fabricate precision components required of micro, sub-micro, or nano order of dimensional accuracy.

[1]  J. C. Huang,et al.  Viscous flow behavior and thermal properties of bulk amorphous Mg58Cu31Y11 alloy , 2007 .

[2]  V. C. Venkatesh,et al.  Semi-Ductile Grinding and Polishing of Ophthalmic Aspherics and Spherics* , 1995 .

[3]  Weimin Lin,et al.  Development of Desktop 4-axes Machine Tools , 2005 .

[4]  Jian Xu,et al.  Critical size and strength of the best bulk metallic glass former in the Mg-Cu-Gd ternary system , 2007 .

[5]  Y. Saotome,et al.  Superplastic nanoforming of Pd-based amorphous alloy , 2001 .

[6]  F. Sommer,et al.  Mechanical properties of amorphous and crystallised Mg-35 wt.% Ni , 2005 .

[7]  Parag Vichare,et al.  The novel bondless wheel, spherical glass chips and a new method of aspheric generation , 2005 .

[8]  Chung-Yu Wu,et al.  Nanoimprint of gratings on a bulk metallic glass , 2007 .

[9]  W. Johnson,et al.  Viscosity of the supercooled liquid and relaxation at the glass transition of the Zr46.75Ti8.25Cu7.5Ni10Be27.5 bulk metallic glass forming alloy , 1998 .

[10]  C. Liu,et al.  A new glass-forming ability criterion for bulk metallic glasses , 2002 .

[11]  M. Takayanagi,et al.  Glass-transition Temperature and Thermal Expansion Coefficient of a Two-Phase System of Polymers , 1971 .

[12]  Sangkee Min,et al.  Recent Advances in Mechanical Micromachining , 2006 .

[13]  C. Liu,et al.  A new glass-forming ability criterion for bulk metallic glasses , 2002 .

[14]  V. C. Venkatesh.  Precision manufacture of spherical and aspheric surfaces on plastics, glass, silicon and germanium , 2003 .

[15]  Ekkard Brinksmeier,et al.  Merging Technologies for Optics , 2007 .

[16]  A. L. Greer,et al.  Viscous-flow behavior of amorphous Co69Fe4.5Nb1.5Si10B15 alloys , 2001 .

[18]  V. C. Venkatesh,et al.  Diamond Grinding of Aspheric Surfaces on a CNC 4-Axis Machining Centre , 1985 .

[19]  F. Sommer,et al.  Mechanical Properties of Crystallised Amorphous Mg-23.5Ni(wt.%) Alloy. , 2004 .

[20]  D. Miracle,et al.  Composition range and glass forming ability of ternary Ca–Mg–Cu bulk metallic glasses , 2006 .

[21]  A. Inoue,et al.  The effect of Ni substitution on the glass-forming ability and mechanical properties of Mg–Cu–Gd metallic glass alloys , 2005 .

[22]  Zhaoping Lu,et al.  Glass transition and crystallization of Mg–Ni–Nd metallic glasses studied by temperature-modulated DSC , 2004 .

[23]  Hao Wang,et al.  Formation and mechanical properties of Mg65Cu25Er10 and Mg65Cu15Ag10Er10 bulk amorphous alloys , 2005 .

[24]  G. Papanicolaou,et al.  Effect of interfacial phenomena on the thermal expansion behavior of rubber-toughened PMMA composites , 1998 .

[25]  Ho-Sang Kim,et al.  Diamond turning of large off-axis aspheric mirrors using a fast tool servo with on-machine measurement , 2004 .

[26]  A. Inoue,et al.  Structure and mechanical properties of Mg85Cu5Zn5Y5 amorphous alloy containing nanoscale particles , 2004 .

[27]  Z. Lu,et al.  Glass formation criterion for various glass-forming systems. , 2003, Physical review letters.

[28]  Tsunemoto Kuriyagawa,et al.  A new grinding method for aspheric ceramic mirrors , 1996 .