Predicting the Effect of Underfill Filler Volume Fraction on Solder Fatigue Life and Residual Stress for Surface Mount Components Using Nonlinear Viscoelastic Analyses

Glassy thermoset polymer underfills are commonly used for reliability enhancement in modern electronics. By adding filler to the polymer, underfill mechanical properties, such as bulk and shear moduli and coefficient of thermal expansion, can be altered. Addition of underfills can affect the solder reliability and component failure during dynamic environments. By modifying the nonlinear viscoelastic simplified potential energy clock model, a generic computational tool was created for analyzing filled polymers. Together with a unified creep plasticity model for solder and the Coffin-Manson fatigue criterion, solder fatigue life for underfilled surface mount components was investigated for various underfill filler materials and filler volume fractions (FVFs) using finite element analyses. By creating models of representative components with very different geometries, the effect of adding an underfill and increasing the FVF of hard and glass micro-balloons (GMB) fillers was analyzed. For a large stiff component, the addition of an unfilled underfill reduced the localized tensile stress in the component. Underfill filler volume fractions greater than 10% for hard filler and 15% for GMB filler resulted in a positive effect on the fatigue life. The results were different for a small flexible component. The addition of an unfilled underfill slightly increased the localized tensile stress in the component, but a positive effect on the fatigue life was still demonstrated if the underfill FVFs were greater than 15% for hard filler and 30% for GMB filler.

[1]  Y.-L. Shen,et al.  Numerical study of ductile failure morphology in solder joints under fast loading conditions , 2010, Microelectronics Reliability.

[2]  Cheng-fu Chen,et al.  Effect of underfill filler settling on thermo-mechanical fatigue analysis of flip-chip eutectic solders , 2008, Microelectron. Reliab..

[3]  R. S. Sidhu,et al.  Microstructure-based modeling of deformation in Sn-rich (Pb-free) solder alloys , 2006 .

[4]  D. Frear,et al.  Time-dependent deformation behavior of near-eutectic 60Sn-40Pb solder , 1999 .

[5]  James M. Caruthers,et al.  Extensive validation of a thermodynamically consistent, nonlinear viscoelastic model for glassy polymers , 2004 .

[6]  R. Chambers,et al.  A simplified potential energy clock model for glassy polymers , 2009 .

[7]  Robert S. Chambers,et al.  Potential energy clock model: Justification and challenging predictions , 2007 .

[8]  H. Solomon.  Fatigue of 60/40 Solder , 1986 .

[9]  Nikhilesh Chawla,et al.  Deformation analysis of lap-shear testing of solder joints , 2005 .

[10]  Yu-Lin Shen,et al.  Modeling of Solder Fatigue Failure due to Ductile Damage , 2010 .

[11]  J. J. Stephens,et al.  A viscoplastic theory for braze alloys , 1996 .

[12]  Y.-L. Shen,et al.  On the failure path in shear-tested solder joints , 2007, Microelectron. Reliab..

[14]  Pradeep Lall,et al.  High Speed Digital Image Correlation for Transient-Shock Reliability of Electronics , 2009 .

[15]  D. R. Frear,et al.  Microstructurally Based Finite Element Simulation on Solder Joint Behaviour , 1997 .

[16]  James M. Caruthers,et al.  A thermodynamically consistent, nonlinear viscoelastic approach for modeling glassy polymers , 2004 .

[17]  Leila Ladani,et al.  Numerical analysis of thermo-mechanical reliability of through silicon vias (TSVs) and solder interconnects in 3-dimensional integrated circuits , 2010 .

[18]  Yu‐Lin Shen,et al.  Nonlinear Viscoelastic Finite Element Analysis of Physical Aging in an Encapsulated Transformer , 2009 .