Investigation of the distribution of laser damage precursors at 1064 nm, 12 ns on niobia-silica and zirconia-silica mixtures.

Simple Nb(2)O(5), ZrO(2), SiO(2) oxide coatings and their mixtures with SiO(2) have been prepared by the Ion Beam Sputtering (IBS) technique. The Laser-Induced Damage of these samples has been studied at 1064 nm, 12 ns. The laser induced damage threshold (LIDT) decreases in both sets of the mixtures with the volumetric fraction of high index material. We find that the nanosecond LIDT of the mixtures is related to the band gap of the material as it has been widely observed in the subpicosecond regime. The laser damage probability curves have been fitted firstly by a statistical approach, i.e. direct calculation of damage precursor density from damage probability and secondly by a thermal model based on absorption of initiator. The distributions of damage precursors versus fluence extracted from these fittings show a good agreement. The thermal model makes it possible to connect damage probability to precursor physical properties. A metallic defect with a maximum radius of 18 nm was proposed to the interpretation. The critical temperature in the laser damage process exhibited a dependence on the band-gap of the material.

[1]  Maria Rita Perrone,et al.  HfO2 films with high laser damage threshold , 2000 .

[2]  C. C. Lee,et al.  Low-Loss Dielectric Mirror with Ion-Beam-Sputtered TiO 2-SiO 2 Mixed Films. , 2001, Applied optics.

[3]  Laurent Gallais,et al.  Investigation of nanodefect properties in optical coatings by coupling measured and simulated laser damage statistics , 2008 .

[4]  Michael D. Feit,et al.  Implications of nanoabsorber initiators for damage probability curves, pulselength scaling, and laser conditioning , 2003, SPIE Laser Damage.

[5]  S G Demos,et al.  Localized dynamics during laser-induced damage in optical materials. , 2004, Physical review letters.

[6]  Michael D. Feit,et al.  Analysis of bulk DKDP damage distribution, obscuration, and pulse-length dependence , 2001, SPIE Laser Damage.

[7]  C K Carniglia,et al.  Stress reduction in ion beam sputtered mixed oxide films. , 1989, Applied optics.

[8]  D. Lynch,et al.  Optical Properties of Niobium from 0.1 to 36.4 eV , 1973 .

[9]  S. Papernov,et al.  Correlations between embedded single gold nanoparticles in SiO2 thin film and nanoscale crater formation induced by pulsed-laser radiation , 2002 .

[10]  Valdas Sirutkaitis,et al.  Calculations and experimental demonstration of multi-photon absorption governing fs laser-induced damage in titania. , 2009, Optics express.

[11]  L. Lamaignère,et al.  An accurate, repeatable, and well characterized measurement of laser damage density of optical materials. , 2007, The Review of scientific instruments.

[12]  Lars Jensen,et al.  Spot-size dependence of the LIDT from the NIR to the UV , 2009, Laser Damage.

[13]  Holger Blaschke,et al.  Laser-induced damage of pure and mixture material high reflectors for 355nm and 1064nm wavelength , 2011, Optical Systems Design.

[14]  Sonny Ly,et al.  Extracting the distribution of laser damage precursors on fused silica surfaces for 351 nm, 3 ns laser pulses at high fluences (20-150 J/cm2). , 2012, Optics express.

[15]  J. Porteus,et al.  Absolute onset of optical surface damage using distributed defect ensembles. , 1984, Applied optics.

[16]  Laurent Gallais,et al.  Multiscale analysis of the laser-induced damage threshold in optical coatings. , 2008, Applied optics.

[17]  D Milam,et al.  Statistical analysis of defect-caused laser damage in thin films. , 1977, Applied optics.

[18]  Kai Starke,et al.  TixSi1−xO2 optical coatings with tunable index and their response to intense subpicosecond laser pulse irradiation , 2008 .

[19]  Myriam Zerrad,et al.  Characterization of zirconia- and niobia-silica mixture coatings produced by ion-beam sputtering. , 2011, Applied optics.