Trace concentrations of vitamin E protect radiation crosslinked UHMWPE from oxidative degradation.

The effect of very low concentrations of Vitamin E on the stability and mechanical behavior of UHMWPE remains unknown. We tested the hypothesis that the oxidation resistance of Vitamin E-blended UHMWPE would be influenced by trace doses of antioxidant, resin, and radiation treatment. Trace concentrations (< or =500 ppm w/w%) of alpha-tocopherol (Vitamin E) were blended separately with GUR 1020 and 1050 resins and molded into disks. From each disk, three groups of 10 mm thick blocks were machined: (1) no irradiation (control); (2) 30 kGy of gamma irradiation in nitrogen; and (3) 75 kGy of gamma irradiation in air. Specimens were subjected to three aging protocols: (a) no aging (control); (b) two weeks and (c) four weeks of accelerated aging in accordance with ASTM F 2003 (i.e., 70 degrees C and 5 atm oxygen). The minimum concentration of Vitamin E needed to stabilize UHMWPE during our accelerated tests depended upon the method of radiation processing. For the 30 and 75 kGy irradiated materials, the addition of 125 ppm or more Vitamin E was sufficient to maintain baseline mechanical and chemical properties through two weeks of accelerated aging. For these groups, the addition of 375 ppm or 500 ppm, respectively, was necessary to maintain baseline mechanical and chemical properties throughout the four-week accelerated aging period. UHMWPE resin molecular weight did not have an effect on oxidation behavior. The results of this experiment therefore supported our hypotheses that trace concentrations of Vitamin E, coupled with radiation treatment-but not resin grade-influence the mechanical and oxidative degradation behavior of UHMWPE.

[1]  E. Ingolič,et al.  Biocompatibility of ultra-high molecular weight polyethylene (UHMW-PE) stabilized with α-tocopherol used for joint endoprostheses assessed in vitro , 2007, Journal of materials science. Materials in medicine.

[2]  K. Lederer,et al.  Accelerated ageing experiments with crosslinked and conventional ultra-high molecular weight polyethylene (UHMW-PE) stabilised with α-tocopherol for total joint arthroplasty , 2006, Journal of materials science. Materials in medicine.

[3]  R. Marr,et al.  Stabilisation of crosslinked ultra-high molecular weight polyethylene (UHMW-PE)-acetabular components with α-tocopherol , 2006, Journal of materials science. Materials in medicine.

[4]  Aiguo Wang,et al.  The Basis for a Second-generation Highly Cross-linked UHMWPE , 2006, Clinical orthopaedics and related research.

[5]  H. Bergmeister,et al.  Animal experiments with ultra-high molecular weight polyethylene (UHMW-PE) stabilised with α-tocopherol used for articulating surfaces in joint endoprostheses , 2006, Journal of materials science. Materials in medicine.

[6]  V. Goldberg,et al.  2006 Otto Aufranc Award Paper: significance of in vivo degradation for polyethylene in total hip arthroplasty. , 2006, Clinical orthopaedics and related research.

[7]  O. Muratoglu,et al.  The effect of α-tocopherol on the oxidation and free radical decay in irradiated UHMWPE☆ , 2006 .

[8]  S. Kurtz,et al.  Oxidation and oxidation potential in contemporary packaging for polyethylene total joint replacement components. , 2006, Journal of biomedical materials research. Part B, Applied biomaterials.

[9]  M. Cannas,et al.  UHMWPE and vitamin E bioactivity: an emerging perspective. , 2006, Biomaterials.

[10]  Ebru Oral,et al.  Wear resistance and mechanical properties of highly cross-linked, ultrahigh-molecular weight polyethylene doped with vitamin E. , 2006, The Journal of arthroplasty.

[11]  O. Muratoglu,et al.  Migration stability of α-tocopherol in irradiated UHMWPE , 2006 .

[12]  W. Harris,et al.  Characterization of irradiated blends of alpha-tocopherol and UHMWPE. , 2005, Biomaterials.

[13]  N. Tomita,et al.  The anti-oxidative properties of α-tocopherol in γ-irradiated UHMWPE with respect to fatigue and oxidation resistance , 2005 .

[14]  Joshua J. Jacobs,et al.  The UHMWPE Handbook. Ultra-High Molecular Weight Polyethylene in Total Joint Replacement , 2005 .

[15]  V. Goldberg,et al.  In vivo degradation of polyethylene liners after gamma sterilization in air. , 2005, The Journal of bone and joint surgery. American volume.

[16]  D. A. Zumbrunnen,et al.  Advancing controlled release packaging through smart blending , 2005 .

[17]  W. Harris,et al.  Alpha-tocopherol-doped irradiated UHMWPE for high fatigue resistance and low wear. , 2004, Biomaterials.

[18]  C. Engh,et al.  Shelf age of the polyethylene tibial component and outcome of unicondylar knee arthroplasty. , 2004, The Journal of bone and joint surgery. American volume.

[19]  L. Costa,et al.  The induction of MMP-9 release from granulocytes by vitamin E in UHMWPE. , 2004, Biomaterials.

[20]  S. Kurtz,et al.  Degradation of mechanical properties of UHMWPE acetabular liners following long-term implantation. , 2003, The Journal of arthroplasty.

[21]  N. Aust,et al.  Studies on the effect of electron beam radiation on the molecular structure of ultra-high molecular weight polyethylene under the influence of α-tocopherol with respect to its application in medical implants , 2002, Journal of materials science. Materials in medicine.

[22]  S M Kurtz,et al.  Accelerated aging studies of UHMWPE. II. Virgin UHMWPE is not immune to oxidative degradation. , 2002, Journal of biomedical materials research.

[23]  S M Kurtz,et al.  Accelerated aging studies of UHMWPE. I. Effect of resin, processing, and radiation environment on resistance to mechanical degradation. , 2002, Journal of biomedical materials research.

[24]  K. Lederer,et al.  Tests of biocompatibility of α-tocopherol with respect to the use as a stabilizer in ultrahigh molecular weight polyethylene for articulating surfaces in joint endoprostheses , 2002, Journal of materials science. Materials in medicine.

[25]  Gerard A Engh,et al.  Rapid Polyethylene Failure of Unicondylar Tibial Components Sterilized with Gamma Irradiation in Air and Implanted After a Long Shelf Life , 2002, The Journal of bone and joint surgery. American volume.

[26]  L. Costa,et al.  Oxidation of orthopaedic UHMWPE. , 2002, Biomaterials.

[27]  K. Lederer,et al.  Examination of the suitability of α-tocopherol as a stabilizer for ultra-high molecular weight polyethylene used for articulating surfaces in joint endoprostheses , 2002, Journal of materials science. Materials in medicine.

[28]  W. Harris,et al.  Identification and quantification of irradiation in UHMWPE through trans-vinylene yield. , 2001, Journal of biomedical materials research.

[29]  W H Harris,et al.  A novel method of cross-linking ultra-high-molecular-weight polyethylene to improve wear, reduce oxidation, and retain mechanical properties. Recipient of the 1999 HAP Paul Award. , 2001, The Journal of arthroplasty.

[30]  J. Bohl,et al.  The Coventry Award. The effects of shelf life on clinical outcome for gamma sterilized polyethylene tibial components. , 1999, Clinical orthopaedics and related research.

[31]  C. Jewett,et al.  Radiation and chemical crosslinking promote strain hardening behavior and molecular alignment in ultra high molecular weight polyethylene during multi-axial loading conditions. , 1999, Biomaterials.

[32]  S. Downes,et al.  Influence of packaging conditions on the properties of gamma-irradiated UHMWPE following accelerated ageing and shelf ageing. , 1999, Biomaterials.

[33]  L. Costa,et al.  Oxidation in orthopaedic UHMWPE sterilized by gamma-radiation and ethylene oxide. , 1998, Biomaterials.

[34]  W H Harris,et al.  Gamma sterilization of UHMWPE articular implants: an analysis of the oxidation problem. Ultra High Molecular Weight Poly Ethylene. , 1996, Biomaterials.

[35]  K. Saum,et al.  Impact of gamma sterilization on clinical performance of polyethylene in the knee. , 1996, The Journal of arthroplasty.

[36]  K. Saum,et al.  The Otto Aufranc Award. Impact of gamma sterilization on clinical performance of polyethylene in the hip. , 1995, Clinical orthopaedics and related research.

[37]  T. Wright,et al.  The natural history of ultra high molecular weight polyethylene. , 1994, Clinical orthopaedics and related research.

[38]  T. Wright,et al.  Post-irradiation aging of ultra-high molecular weight polyethylene. , 1994, The Journal of bone and joint surgery. American volume.

[39]  P. Eyerer,et al.  Property changes of UHMW polyethylene hip cup endoprostheses during implantation. , 1984, Journal of biomedical materials research.

[40]  O. Muratoglu,et al.  Migration stability of alpha-tocopherol in irradiated UHMWPE. , 2006, Biomaterials.

[41]  D. Schroeder,et al.  Anisotropy and oxidative resistance of highly crosslinked UHMWPE after deformation processing by solid-state ram extrusion. , 2006, Biomaterials.

[42]  O. Muratoglu,et al.  The effect of alpha-tocopherol on the oxidation and free radical decay in irradiated UHMWPE. , 2006, Biomaterials.

[43]  S. Kurtz,et al.  Recent Advances of Mechanical Performance and Oxidation Stability in Ultrahigh Molecular Weight Polyethylene for Total Joint Replacement: Highly Crosslinked and α-Tocopherol Doped , 2006 .

[44]  N. Tomita,et al.  The anti-oxidative properties of alpha-tocopherol in gamma-irradiated UHMWPE with respect to fatigue and oxidation resistance. , 2005, Biomaterials.

[45]  S. Al‐Malaika.  Perspectives in stabilisation of polyolefins , 2004 .

[46]  Aiguo Wang,et al.  Comparison of the properties of annealed crosslinked (Crossfire) and conventional polyethylene as hip bearing materials. , 2002, Bulletin (Hospital for Joint Diseases (New York, N.Y.)).

[47]  L. Deschen̂es,et al.  Antioxidant effectiveness of vitamin E in HDPE and tetradecane at 32 C , 2001 .

[48]  Y. Ikada,et al.  Prevention of fatigue cracks in ultrahigh molecular weight polyethylene joint components by the addition of vitamin E. , 1999, Journal of biomedical materials research.