Oxidation studies of CrAlON nanolayered coatings on steel plates

The requirements of low cost and high-temperature corrosion resistance for bipolar interconnect plates in solid oxide fuel cell stacks have directed attention to the use of metal plates with oxidation resistant coatings. We have investigated the performance of steel plates with nanolayered coatings consisting of [CrON/AlON]n. The coatings were deposited using large-area filtered arc deposition technology, with various O/N pressure ratios, and subsequently annealed in air for up to 25 h at 800 °C. The composition, structure and surface morphology of the coated plates were characterized using RBS, nuclear reaction analysis, and AFM techniques. By altering the architecture and composition of the coatings, the rate of oxidation was reduced relative to the uncoated steel plates, and Fe diffusion from the substrate to the surface through the coating was significantly reduced.

[1]  S. Deevi,et al.  Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review , 2003 .

[2]  Hong-ying Chen,et al.  Phase transformation in chromium nitride films , 2003 .

[3]  K. S. Weil,et al.  Selection and Evaluation of Heat-Resistant Alloys for SOFC Interconnect Applications , 2003 .

[4]  A. Hashimoto,et al.  Oxidation resistance of Cr1-XAlXN and Ti1-XAlXN films , 2003 .

[5]  J. Goodenough,et al.  Reduced area specific resistance for iron-based metallic interconnects by surface oxide coatings , 2001 .

[6]  M. Mayer,et al.  SIMNRA user's guide , 1997 .

[7]  B. Steele,et al.  Materials for fuel-cell technologies , 2001, Nature.

[8]  Michael Nastasi,et al.  Handbook of modern ion beam materials analysis , 1995 .

[9]  D. Gelles,et al.  High-temperature oxidation resistance and surface electrical conductivity of stainless steels with filtered arc Cr–Al–N multilayer and/or superlattice coatings , 2004 .

[10]  W. Hoyer,et al.  The reactive magnetron deposition of CrNxOy films : first results of property investigations , 1999 .

[11]  M. Metikoš-huković,et al.  HIGH TEMPERATURE OXIDATION OF THIN CRN COATINGS DEPOSITED ON STEEL , 1996 .

[12]  R. J. Smith,et al.  Using CrAlN multilayer coatings to improve oxidation resistance of steel interconnects for solid oxide fuel cell stacks , 2004 .

[13]  J. Machet,et al.  Study and elaboration of ternary chromium based compounds (Cr, O, N) deposited by vacuum arc evaporation , 1997 .

[14]  T. Palstra,et al.  Encyclopedia of Materials , 2006 .

[15]  F. Lévy,et al.  High-temperature oxidation resistance of Cr1−xAlxN thin films deposited by reactive magnetron sputtering , 2003 .

[16]  D. Bhat,et al.  Characterization of large area filtered arc deposition technology: part I — plasma processing parameters , 2001 .