Effect of cement type on the resistance of concrete against chloride penetration

Abstract In chloride containing environment, chloride permeability of concrete is an important parameter affecting the service life of concrete structures. The primary objective of this experimental study was to study the effect of cement types on the resistance of concrete against chloride penetration for given compressive strength classes. These cements included two different types of granulated blast-furnace slag cement (CEM III/A 32.5N and CEM III/A 42.5N), a sulfate resisting cement (SRC 32.5), and a Portland cement blended with fly ash; all of which compared to an ordinary Portland cement (CEM I 42.5R). For each binder type, four concretes at different strength classes were produced and as a result 20 mixtures were obtained. Rapid chloride ion penetration tests according to ASTM C 1202 were conducted. In addition, electrical resistivity and capillary water absorption tests were carried out. In order to characterize the concrete quality, compressive strength of the specimens were also obtained. The test results clearly demonstrated that the blast-furnace slag cements have the highest resistance against chloride penetration, while the pure Portland cement and sulfate resisting cement have the lowest resistance. Concretes produced with the sulfate resisting cement had substantially higher capillary sorption compared to other mixtures. Test results confirmed the strong relationship between the chloride permeability and electrical resistivity.

[1]  P. K. Mehta.  Concrete in the Marine Environment , 1990 .

[2]  G. Osborne,et al.  DURABILITY OF PORTLAND BLAST-FURNACE SLAG CEMENT CONCRETE , 1999 .

[3]  V. M. Malhotra,et al.  Concrete Incorporating Supplementary Cementing Materials: Effect of Curing on Compressive Strength and Resistance to Chloride-Ion Penetration , 1999 .

[4]  Jan Skalny,et al.  Sulfate attack on concrete , 2001 .

[5]  Ravindra K. Dhir,et al.  Development of chloride-resisting concrete using fly ash , 1999 .

[6]  J. Chen,et al.  High-pressure epoxy-impregnated cementitious materials for microstructure characterization , 2002 .

[7]  Mark G. Stewart,et al.  Structural Safety and Serviceability of Concrete Bridges Subject to Corrosion , 1998 .

[8]  Odd E. Gjørv,et al.  Electrical Resistivity Measurements for Quality Control During Concrete Construction , 2008 .

[9]  J. Bijen,et al.  Blast furnace slag cement for durable marine structures , 1996 .

[10]  P. K. Mehta,et al.  Sustainable High-Performance Concrete Structures , 2006 .

[11]  Kimberly E. Kurtis,et al.  Time to failure for concrete exposed to severe sulfate attack , 2003 .

[12]  J. Sharp,et al.  The mineralogy and microstructure of three composite cements with high replacement levels , 2002 .

[13]  A. Neville.  THE CONFUSED WORLD OF SULFATE ATTACK ON CONCRETE , 2004 .

[14]  Koji Sakai,et al.  Concrete technology for a sustainable development in the 21st century , 1999 .

[15]  V. Malhotra.  Role of supplementary cementing materials in reducing greenhouse gas emissions , 1999 .

[16]  Mehmet Ali Tasdemir,et al.  Mechanical Properties and Rapid Chloride Permeability of Concrete With Ground Fly Ash , 2005 .

[17]  Della M. Roy,et al.  Investigation of relations between porosity, pore structure, and C1− diffusion of fly ash and blended cement pastes , 1986 .

[18]  A. Neville.  Properties of Concrete , 1968 .

[19]  K. Mehta.  Reducing the Environmental Impact of Concrete , 2001 .

[20]  X. Guan,et al.  Research on optimizing components of microfine high-performance composite cementitious materials , 2002 .

[21]  Rob B. Polder,et al.  Test methods for on site measurement of resistivity of concrete — a RILEM TC-154 technical recommendation , 2001 .