Plywood Made from Plasma-Treated Veneers: Investigation of Performance Differences between Plasma-Pretreated and Untreated Beech Veneers at Comparable Melamine Resin Load

In this study, the dimensional stability and mechanical properties of plywood made from untreated and plasma-pretreated beech veneers were compared. The wood veneers used (native and thermally modified) were impregnated with melamine resin in a simple dipping process prior to plywood production. The duration of the impregnation process was adjusted to give the same melamine resin loading for the different veneer types, with the plasma-pretreated veneers requiring only a fraction of the impregnation time compared with non-plasma-pretreated veneers. With comparable melamine loading, testing of the mechanical properties of the plywood for the different specimen collectives showed significant differences in some cases with respect to compressive strength, bending strength and tensile strength (with the associated moduli of elasticity). For example, it was shown that plywood made from plasma-pretreated native beech veneers shows an increase in bending strength of about 8%, and from plasma-pretreated and thermally modified beech veneers, there is an increase of about 10% compared to the reference.

[1]  G. Avramidis,et al.  Use of computed tomography to determine penetration paths and the distribution of melamine resin in thermally-modified beech veneers after plasma treatment , 2020 .

[2]  G. Avramidis,et al.  Plywood made from plasma-treated veneers: Shear strength after shrinkage-swelling stress , 2017 .

[3]  G. Avramidis,et al.  Plywood made from plasma-treated veneers: melamine uptake, dimensional stability, and mechanical properties , 2017, Journal of Wood Science.

[4]  Li Yu,et al.  The wood from the trees: The use of timber in construction , 2017 .

[5]  P. Fratzl,et al.  Chemical, colloidal and mechanical contributions to the state of water in wood cell walls , 2016 .

[6]  Ivan Eastin,et al.  Wood-based panels , 2016, Forest Products Annual Market Review 2019-2020.

[7]  Peter Niemz,et al.  Physik des Holzes und der Holzwerkstoffe , 2016 .

[8]  P. Gérardin,et al.  New alternatives for wood preservation based on thermal and chemical modification of wood— a review , 2015, Annals of Forest Science.

[9]  G. Avramidis,et al.  Improved DMDHEU uptake of beech veneers after plasma treatment at atmospheric pressure , 2015, European Journal of Wood and Wood Products.

[10]  G. Avramidis,et al.  Plasma induced effects within the bulk material of wood veneers , 2014 .

[11]  G. Avramidis,et al.  Increasing the water uptake of wood veneers through plasma treatment at atmospheric pressure , 2014, European Journal of Wood and Wood Products.

[12]  G. Avramidis,et al.  Improved absorption characteristics of thermally modified beech veneer produced by plasma treatment , 2011, European Journal of Wood and Wood Products.

[13]  U. Müller,et al.  Transverse Compression Strength and Fracture of Spruce Wood Modified by Melamine-Formaldehyde Impregnation of Cell Walls , 2007 .

[14]  F. Kollmann.  Neues zur Anisotropie der Schwindung und Quellung von Holz , 1981, Holz als Roh- und Werkstoff.

[15]  Yanjun Xie,et al.  Effect of treatments with 1,3-dimethylol-4,5-dihydroxy-ethyleneurea (DMDHEU) on the tensile properties of wood , 2007 .

[16]  C. Hill,et al.  Wood Modification: Chemical, Thermal and Other Processes , 2006 .

[17]  Roger M. Rowell,et al.  Handbook of wood chemistry and wood composites. , 2005 .

[18]  R. Wimmer,et al.  Using UV-Microscopy to Study Diffusion of Melamine-Urea-Formaldehyde Resin in Cell Walls of Spruce Wood , 2002 .

[19]  W. Adam,et al.  Electron Energy Loss Spectroscopy (EELS) for Quantification of Cell-Wall Penetration of a Melamine Resin , 1999 .

[20]  C. Hill,et al.  The Dimensional Stabilisation of Corsican Pine Sapwood by Reaction with Carboxylic Acid Anhydrides. The Effect of Chain Length , 1996 .

[21]  E. W. Washburn.  The Dynamics of Capillary Flow , 1921 .