论文信息 - Near Infrared Cut-Off Characteristics of Various Perovskite-Based Composite Films

Near Infrared Cut-Off Characteristics of Various Perovskite-Based Composite Films

Homogenous cesium tungsten tri-oxide (CsxWO3) and molybdenum tri-oxide (Cs0.33MoO3) powder was prepared by solvothermal reaction using (NH4)10H2(W2O7)6, H8MoN2O4 and Cs2CO3 aqueous solution followed by annealing. The cesium doped tungsten tri-oxide (CsxWO3) and the cesium doped molybdenum tri-oxide (CsxMoO3) nanocomposite films was deposited by the sol-gel bar-coating method onto PET-film (polyethylene terephthalate film, thickness 186 ㎛) substrate. The structure and sizes of ceramic particles was observed XRD and PSA spectrometer, the optical properties of their films were investigated by UV-VIS, NIR spectrometer. Synthesized particles typically formed cubic structure for good absorption of NIR, size observed as being 30-100 nm and 3 nanoparticles showed a high transmittance in the visible wavelength region as well as excellent shielding capability of near-infrared (NIR) wavelength, indicating that CsxWO3, Cs0.33MoO3 nanoparticles have a appropriate characteristic as solar filter applications.

[1] R. Tenne,et al. Characterization of Oxides of Cesium , 2004 .

[2] S. Yin,et al. Discovery of an excellent IR absorbent with a broad working waveband: Cs(x)WO3 nanorods. , 2011, Chemical communications.

[3] S. Yin,et al. Microstructure and electrical–optical properties of cesium tungsten oxides synthesized by solvothermal reaction followed by ammonia annealing , 2010 .

[4] Y. Dobrovol’skii,et al. Tungsten oxide bronzes with alkali metals , 2009 .