The Development of Second Generation HTS Wire at American Superconductor

Development of the second generation (2G) YBCO high temperature superconducting wire has progressed rapidly and its performance is approaching, and in some areas exceeding, that of first generation (1G) HTS wire. American Superconductor's approach to the low-cost manufacturing of 2G wire is based on a wide-strip (4 cm) process using a metal organic deposition (MOD) process for the YBCO layer and the RABiTS (rolling assisted biaxially textured substrate) process for the template. In addition, the wide-strip RABiTS/MOD-YBCO process provides the flexibility to engineer practical 2G HTS wires with architectures and properties tailored for specific applications and operating conditions through slitting to custom widths and laminating with custom metallic stabilizers. This paper will review the status of the 2G manufacturing scale up at AMSC and describe the properties and architecture of the 2G wire being developed and tested for various applications including in cables, coils and fault current limiters. Performance of 100 meter class, 4 mm wide wires at 77 K, self-field has reached 100 A (250 A/cm-width) with single-coat YBCO and 140 A (350 A/cm-width) with double-coat YBCO. A 5 cm inner diameter coil fabricated from the latter wire achieved 1.5 T at 64 K, confirming the capability of the wire for coil applications.

[1]  S. Fleshler,et al.  The Development of Second Generation HTS Wire at American Superconductor , 2009, IEEE transactions on applied superconductivity.

[2]  Q. Jia,et al.  Understanding High Critical Currents in YBa2Cu3O7 Thin Films and Coated Conductors , 2004 .

[3]  Q. Jia,et al.  Angular-dependent vortex pinning mechanisms in YBa2Cu3O7 coated conductors and thin films , 2003, cond-mat/0310568.

[4]  Xiaoping Li,et al.  Metalorganic Deposition of YBCO Films for Second-Generation High-Temperature Superconductor Wires , 2004 .

[5]  D. Larbalestier,et al.  Top-down and bottom-up through-thickness current anisotropy in a bilayer YBa2Cu3O7−x film , 2007 .

[6]  Xiaoping Li,et al.  Stacking faults in YBa2Cu3O7−x: Measurement using x-ray diffraction and effects on critical current , 2006 .

[7]  Wei Zhang,et al.  YBCO coated conductors by an MOD/RABiTS™ process , 2003 .

[8]  Xiaoping Li,et al.  Influence of oxygen deficiency on the out-of-plane tilt of epitaxial Y_2O_3 films on Ni–5%W tapes , 2009 .

[9]  M. Paranthaman,et al.  The RABiTS Approach: Using Rolling-Assisted Biaxially Textured Substrates for High-Performance YBCO Superconductors , 2004 .

[10]  M. Kramer.  Processing controlled stacking faults in YBa2Cu3O7−δ and their effect on flux pinning , 1991 .

[11]  Wei Zhang,et al.  RAPID COMMUNICATION: Uniform performance of continuously processed MOD-YBCO-coated conductors using a textured Ni-W substrate , 2003 .

[12]  Wei Zhang,et al.  Second generation HTS wire based on RABiTS substrates and MOD YBCO , 2005, IEEE Transactions on Applied Superconductivity.

[13]  M. Rupich,et al.  Enhanced in-field critical currents of YBCO second-generation (2G) wire by Dy additions , 2005 .

[14]  Alexander Otto,et al.  Progress in high temperature superconductor coated conductors and their applications , 2008 .

[15]  David C. Larbalestier,et al.  Superconducting materials for large scale applications , 2004, Proceedings of the IEEE.

[16]  Wei Zhang,et al.  Progress in Nanoengineered Microstructures for Tunable High‐Current, High‐Temperature Superconducting Wires , 2008 .