Encapsulated phase change materials for energy storage – Characterization by calorimetry

Abstract The objective of this research was to develop encapsulated phase change materials (EPCMs) that can store thermal energy at temperatures up to 450 °C, suitable for applications in concentrating solar power systems. From initial explorations of candidate media, the two salts (PCMs) NaNO 3 and eutectic NaCl–MgCl 2 were selected for further development as storage media with phase change. A specialized calorimeter with requisite size and temperature capability was designed and built to obtain enthalpy values of the PCMs at temperatures below and above their melting points. The latent heats of phase change can contribute 57% and 75% to storage capacity of the NaNO 3 and NaCl–MgCl 2 media, respectively, for a 100 °C temperature swing bracketing the salts’ melting points. After calibration, this calorimeter was then used to determine the actual energy storage capacity achieved by capsules of EPCMs of various dimensions. The calorimeter tests proved that the salts and the encapsulation methods chosen here can store thermal energy effectively while taking advantage of the latent heat of phase change. Repeated thermal-cycles showed sustained performance of the EPCMs, with no discernible diminishment in storage capacity.

[1]  L. Hepler,et al.  Heats of transition and melting of sodium nitrate by differential scanning calorimetry: use of indium and sodium nitrate as calibration substances , 1980 .

[2]  A. Sharma,et al.  Review on thermal energy storage with phase change materials and applications , 2009 .

[3]  A. Oztekin,et al.  Heat transfer analysis of encapsulated phase change materials , 2013 .

[4]  Doerte Laing,et al.  Characterization of Sodium Nitrate as Phase Change Material , 2012 .

[5]  R. Pitz-Paal,et al.  Cascaded latent heat storage for parabolic trough solar power plants , 2007 .

[6]  Luisa F. Cabeza,et al.  Review on thermal energy storage with phase change: materials, heat transfer analysis and applications , 2003 .

[7]  Frank P. Incropera,et al.  Fundamentals of Heat and Mass Transfer , 1981 .

[8]  C. Bergman,et al.  Thermodynamic study of the condensed phases of NaNO3, KNO3 and CsNO3 and their transitions , 1995 .

[9]  J. C. Southard.  A Modified Calorimeter for High Temperatures. The Heat Content of Silica, Wollastonite and Thorium Dioxide Above 25°1,2 , 1941 .

[10]  M. Kamimoto,et al.  Heat capacities and latent heats of LiNO3, NaNO3, and KNO3 , 1988 .

[11]  Katsunori Yamaguchi,et al.  Measurement of high temperature heat content of silicon by drop calorimetry , 2002 .

[12]  D. Williams,et al.  Assessment of Candidate Molten Salt Coolants for the NGNP/NHI Heat-Transfer Loop , 2006 .

[13]  J. M. Chavez,et al.  Corrosion of stainless and carbon steels in molten mixtures of industrial nitrates , 1994 .

[14]  E. A. Dancy,et al.  Calorimetric determination of the thermodynamic properties of the alkali metal salts NaNO3, KNO3, Na2Cr2O7, K2Cr2O7 and their binary eutectic solutions , 1980 .

[15]  J. H. Awbery,et al.  The latent heat of fusion of some metals , 1925 .

[16]  S. M. Hasnain.  Review on sustainable thermal energy storage technologies, Part I: heat storage materials and techniques , 1998 .

[17]  G. Janz,et al.  Physical properties data compilations relevant to energy storage. II. Molten salts: data on single and multi-component salt systems , 1979 .

[18]  W. Misiolek,et al.  Containment capsule stresses for encapsulated phase change materials , 2013 .

[19]  F. Grønvold,et al.  Heat capacity of solid zinc from 298.15 to 692.68 K and of liquid zinc from 692.68 to 940 K: thermodynamic function values , 2002 .

[20]  R. Bradshaw,et al.  Corrosion of stainless steels and carbon steel by molten mixtures of commercial nitrate salts , 2004 .